Effect of Particle Size Distribution on the Sintering Behaviour of Fly Ash, Red Mud and Fly Ash-Red Mud Mixture

  • Sedef Dikmen
  • Zafer Dikmen
  • Gülgün Yılmaz
  • Seyhan Fırat
Conference paper
Part of the Lecture Notes in Civil Engineering book series (LNCE, volume 7)

Abstract

In this study, the characterization and microstructure observation of the sintering behaviour of F (from Seyitömer Thermal Power Plant) and C (from Soma Thermal Power Plant) types fly ashes, red mud and red mud–fly ash mixtures at 4 and 8 h milling times with a mortar type ball are investigated. The particle size distribution (PSD) was carried out by laser technique. The PSD analysis revealed that the particle size decreased with increasing milling time. After milling, the samples were pressed into a cylindrical form without using any additive or binder. The formed samples were sintered at 1050 °C. Phase evolutions and microstructures of the formed samples were carried out by using X-ray diffraction method (XRD) and scanning electron microscope (SEM) method, respectively. The water absorption and compressive strength were tested to determine some physico-mechanical properties. The results of mineralogical analysis as well as the microstructural observations reveal that phase transformations occurred during the sintering treatments. The results showed that at the chosen optimum conditions (F type fly ash-red mud mixture with 1:1 ratio, sintering temperature of 1050 °C and milling time of 4 h), the best characteristics of sintered glass ceramic could be obtained. Values obtained from mechanical testing showed that the fly ash–red mud sintered ceramic materials had increased strength compared to other sintered ceramic materials. The sintered materials from red mud have the highest water absorption value.

Keywords

Fly ash Red mud Sintering behaviour Microstructure Mechanical properties 

References

  1. 1.
    Borges AJP, Hauser-Davis RA, Oliveira TF (2011) Cleaner red mud residue production at an alumina plant by applying experimental design techniques in the filtration stage. J Clean Prod 19(15):1763–1769CrossRefGoogle Scholar
  2. 2.
    Li LY (1998) Properties of red mud of tailings produced under varying process conditions. J Environ Eng 124(3):254–264CrossRefGoogle Scholar
  3. 3.
    Liu Y, Naidu R (2014) Hidden values in bauxite residue (red mud): recovery of metals. Waste Manag 34:2662–2673CrossRefGoogle Scholar
  4. 4.
    Arslan S, Ucbeyiay H, Çelikel B, Baygül M, Avcu S Demir GK (2015) Eti aluminum red mud characteristics and evaluation of dewatering performance. In: Bauxite residue valorization and best practices conference-2015. KU Leuven, Belgium (5–7/10/2015)Google Scholar
  5. 5.
    Kurtoglu SF, Soyer-Uzun S, Uzun A (2016) Tuning structural characteristics of red mud by simple treatments. Ceram Int 42(15):17581–17593CrossRefGoogle Scholar
  6. 6.
    Liu S, Guan X, Zhang S, Xu C, Li H, Zhang J (2006) Sintering red mud based imitative ceramic bricks with CO2 emissions below zero. Mater Lett 191:1–224Google Scholar
  7. 7.
    Yang J, Zhang D, Hou J, He B, Xiao B (2008) Preparation of glass-ceramics from red mud in the aluminum industries. Ceram Int 34(1):125–130CrossRefGoogle Scholar
  8. 8.
    Liu RX, Poon CS (2016) Utilization of red mud derived from bauxite in self-compacting concrete. J Clean Prod 11(2):384–391CrossRefGoogle Scholar
  9. 9.
    Kang SP, Kwon SJ (2017) Effects of red mud and alkali-activated slag cement on efflorescence in cement mortar. Constr Build Mater 133:459–467CrossRefGoogle Scholar
  10. 10.
    Abbasi SM, Rashidi A, Ghorbani A, Khalaj G (2016) Synthesis, processing, characterization, and applications of red mud/carbon nanotube composites. Ceram Int 42(15):16738–16743CrossRefGoogle Scholar
  11. 11.
    Zhao Y, Zhang L, Ni F, Xi B, Xia X, Peng X, Luan Z (2011) Evaluation of a novel composite inorganic coagulant prepared by red mud for phosphate removal. Desalination 273(2–3):414–420CrossRefGoogle Scholar
  12. 12.
    Feng Y, Wu D, Liao C, Deng Y, Zhang T, Shih K (2016) Red mud powders as low-cost and efficient catalysts for persulfate activation: pathways and reusability of mineralizing Sulfadiazine. Sep Purif Technol 167:136–145CrossRefGoogle Scholar
  13. 13.
    Kumar S, Kumar R, Bandopadhyay A (2006) Innovative methodologies for the utilization of wastes from metallurgical and allied industries. Resour Conserv Recycl 48(4):301–314CrossRefGoogle Scholar
  14. 14.
    Zhang M, Zhao M, Zhang G, Mann D, Lumsden K, Tao M (2016) Durability of red mud-fly ash based geopolymer and leacing behavior of heavy metals in sulphiric acid solutions and deionized water. Constr Build Mater 124:373–382CrossRefGoogle Scholar
  15. 15.
    Ersoy B, Kavas T, Evcin A, Başpınar S, Sarıışık A, Önce G (2008) The Effect of BaCO3 addition on the sintering behaviour of lignite coal fly ash. Fuel 87:2563–2571CrossRefGoogle Scholar
  16. 16.
    Blissett RS, Rowson NA (2012) A review of the multi-component utilisation of coal fly ash. Fuel 97:1–23CrossRefGoogle Scholar
  17. 17.
    Fırat S, Yilmaz G, Cömert AT, Sümer M (2012) Utilization of marble dust, fly ash and waste sand (Silt-Quartz) in road subbase filling materials. KSCE J Civ Eng 16(7):1143–1151CrossRefGoogle Scholar
  18. 18.
    Fırat S, Comert AT (2011) Curing time effects on CBR of stabilized kaoline with fly ash, lime and cement. J Fac Eng Archit Gaz 26(4):719–730Google Scholar
  19. 19.
    Öntürk K, Fırat S, Vural İ, Khatib JM (2014) Uçucu kül ve mermer tozu kullanarak yol altyapısının iyileştirilmesi”, J Polytech 17(1) (Special Issue):35–42Google Scholar
  20. 20.
    Pandey VC, Singh N (2010) Impact of fly ash incorporation in soil systems. Agric Ecosyst Environ 136:16–27CrossRefGoogle Scholar
  21. 21.
    Li F, Wu W, Li R, Fu X (2016) Adsorption of phosphate by acid-modified fly ash and palygorskite in aqueous solution: experimental and modeling. Appl Clay Sci 132:343–352CrossRefGoogle Scholar
  22. 22.
    Barbieri L, Lancellotti I, Manfredini T, Queralt I, Rincon J (1999) Design, obtainment and properties of glasses and glass-ceramics from coal fly ash. Fuel 78:271–276CrossRefGoogle Scholar
  23. 23.
    Zeybek O (2009) Fly ash based geopolymer brick production. Master of Science Thesis, Anadolu University, Graduate School of Sciences, Civil Engineering Program, Eskisehir, Turkey (Advisor: O. Arioz)Google Scholar
  24. 24.
    McMillan PW (1979) Glass-ceramics, 2nd edn. Academic Press, LondonGoogle Scholar
  25. 25.
    Liu W, Yang J, Xiao B (2009) Review on treatment and utilization of bauxite residues in China. Int J Miner Process 93:220–231CrossRefGoogle Scholar
  26. 26.
    Samal S, Ray AK, Bandopadhyay A (2015) Characterization and microstructure observation of sintered red mud-fly ash mixture at various elevated temperature. J Clean Prod 101:368–376CrossRefGoogle Scholar
  27. 27.
    Kumar A, Kumar S (2013) Developtment of paving blocks from synergistic use of red mud and fly ash using geopolymerization. Constr Build Mater 38:865–871CrossRefGoogle Scholar
  28. 28.
    Liu T, Tang Y, Li Z, Wu T, Lu A (2016) Red Mud and fly ash in corporation for lightweight foamed ceramics using lead-zinc mine tailings as foaming agent. Mater Lett 183:362–364CrossRefGoogle Scholar
  29. 29.
    Yılmaz H (2015) Characterization and comparison of leaching behaviors of fly ash samples from three different power plants in Turkey. Fuel Process Technol 137:240–249CrossRefGoogle Scholar
  30. 30.
    Erol M, Genc A, Ovecoglu ML, Kucukbayrak S, Tapyik Y, Yucelen E (2000) Characterization of a glass-ceramic produced from thermal power plant fly ashes. J Eur Ceram Soc 20:2209–2214CrossRefGoogle Scholar
  31. 31.
    Yılmaz G (2012) Structural characterization of glass–ceramics made from fly ash containing SiO2–Al2O3–Fe2O3–CaO and analysis by FTIR–XRD–SEM methods. J Mol Struct 1019:37–42CrossRefGoogle Scholar

Copyright information

© Springer International Publishing AG, part of Springer Nature 2018

Authors and Affiliations

  • Sedef Dikmen
    • 1
  • Zafer Dikmen
    • 1
  • Gülgün Yılmaz
    • 2
  • Seyhan Fırat
    • 3
  1. 1.Physics Department, Science FacultyAnadolu UniversityEskişehirTurkey
  2. 2.Porsuk Vocational SchoolAnadolu UniversityEskişehirTurkey
  3. 3.Department of Civil Engineering, Faculty of TechnologyGazi UniversityAnkaraTurkey

Personalised recommendations