Abstract
Hot corrosion arises when metals are excited in the temperature range 700–900 °C in the existence of sulphate deposits, formed as a result of the reaction among sodium chloride and sulphur mixtures in the gas phase adjoining the metals. No alloy is resistant to hot corrosion occurrence indefinitely even though there are certain alloys that require a prolonged origination time at which the hot corrosion progression from the beginning stage to the circulation stage. Superalloys have been established for high-temperature applications. However, these alloys are not constantly able to meet both the high-temperature strength and high-temperature corrosion resistance simultaneously, so the need is to protect from hot corrosion. The high-temperature guarding system must meet numerous benchmarks, provide satisfactory environment resistance, be chemically and mechanically compatible with the substrate, be practically applicable, reliable and economically viable. This chapter briefly reviews the hot corrosion of some Ni- and Fe-base superalloys to recognise the occurrence. Extensive reviews on the hot corrosion of coatings have looked regularly since early 1970; the purpose of this chapter is not to repeat the published resources but relatively to emphasis on research developments and to point out some research forecasts.
Keywords
This is a preview of subscription content, log in via an institution.
Buying options
Tax calculation will be finalised at checkout
Purchases are for personal use only
Learn about institutional subscriptionsReferences
Backman, R., Hupa, M., & Uppstu, E. (1987). Fouling and corrosion mechanisms in the recovery boiler superheater area. Tappi Journal, 70, 123–127.
Bansal, P., Padture, N. P., & Vasiliev, A. (2003). Improved interfacial properties of Al2O3–13 wt% TiO2 plasma sprayed coatings derived from nanocrytalline powders. Acta Materialia, 51, 2959–2970.
Beltran, A. M., & Shores, D. A. (1972). Hot corrosion. In C. T. Sims & W. C. Hagel (Eds.), Shores. NY: Wiley Publ., John Wiley and Sons. (Chapter 11).
Bhushan, B., & Gupta, B. K. (1991). Handbook of tribology: Materials, coatings and surface treatments. New York: McGraw-Hill.
Bornstein, N. S., & DeCrescente, M. A. (1969). Relationship between compounds of sodium and sulfur and sulfidation. Transactions of the Metallurgical Society of AIME, 245(9), 1947.
Bornstein, N. S., DeCrescente, M. A., & Roth, H. A. (1973). The relationship between relative oxide ion content of Na2SO4, the presence of liquid metal oxides and sulfidation attack. Metallurgical Transactions, 4, 1799–1810.
Bornstein, N. S., Decrescente, M. A., & Roth, H. A. (1975). Effect of vanadium and sodium compounds on the accelerated oxidation of nickel base alloys. In: Proceedings of the Conference on Gas Turbine Materials in the Marine Environment, MMIC-75–27 (pp. 115–160). Columbus, Ohio, USA.
Deb, D., Iyer, S. R., & Radhakrishnan, V. M. (1996). A comparative study of oxidation and hot corrosion of a cast nickel base superalloy in different corrosive environments. Materials Letters, 29, 19–23.
Ding, C., Chen, H., Liu, X., & Zeng, Y. (2003). Plasma sprayed nanostructure zirconia coatings for wear resistance. In C. Moreau & B. Marple (Eds.), Thermal spray 2003: Advancing the science & applying the technology (pp. 455–458). Materials Park, Ohio, USA: ASM International.
Eliaz, N., Shemesh, G., & Latanision, R. M. (2002). Hot corrosion in gas turbine components. Engineering Failure Analysis, 9, 31–43.
Fairman, L. (1962). Technical note: Mechanism of accelerated oxidation by vanadium-containing fuel ash. Corrosion Science, 2, 293–296.
Gitanjaly, Prakash, S., & Singh, S. (2002). Effects of MgO and CaO on hot corrosion of Fe base superalloy superfer 800H in Na2SO4–60 %V2O5 environment. British Corrosion Journal, 37(1), 56–62.
Gledhill, H. C., Turner, I. G., & Doyle, C. (1999). Direct morphological comparison of vacuum plasma sprayed and detonation gun sprayed hydroxyapatite coatings for orthopedic applications. Biomaterials, 20, 315–322.
Goebel, J. A., & Pettit, F. S. (1970a). Na2SO4-induced accelerated oxidation (hot corrosion) of nickel. Metallurgical Transactions, 1, 1943–1954.
Goebel, J. A., & Pettit, F. S. (1970b). The influence of sulphides on the oxidation behaviour of nickel-base alloys. Metallurgical Transactions, 1, 3421–3429.
Goebel, J. A., Pettit, F. S., & Goward, G. W. (1973). Mechanisms for the hot corrosion of nickel-base alloys. Metallurgical Transactions, 4, 261–275.
Guo, M. H., Wang, Q. M., Gong, J., Sun, C., Huang, R. F., & Wen, L. S. (2006). Oxidation and hot corrosion behavior of gradient NiCoCrAlYSiB coatings deposited by a combination of arc ion plating and magnetron sputtering techniques. Corrosion Science, 48, 2750–2764.
Gurrappa, I. (1999). Hot corrosion behavior of CM 247 LC alloy in Na2SO4 and NaCl environments. Oxidation of Metals, 51(5), 353–382.
Gurrappa, I. (2000). Hot corrosion of protective coatings. Materials and Manufacturing Processes, 15(5), 761–773.
Gurrappa, I. (2003). Influence of alloying elements on hot corrosion of superalloys and coatings: Necessity of smart coatings for gas turbine engines. Journal of Materials Science and Technology, 19(2), 178–183.
Hancock, P. (1987). Vanadic and chloride attack of superalloys. Materials Science and Technology, 3, 536–544.
Handbook, M. (1975). Failure analysis and prevention (Vol. 10). Metals Park OH, USA: ASM Publication.
Hao, D., Hua, W., Liu, J., Gong, J., Sun, C., & Wen, L. (2005). Influence of process variables on the qualities of detonation gun sprayed WC–Co coatings. Materials Science and Engineering: A, 408, 202–210.
Heath, G. R., Heimgartner, P., Irons, G., Miller, R., & Gustafsson, S. (1997). An assessment of thermal spray coating technologies for high temperature corrosion protection. Materials Science Forum, 251–54, 809–816.
Herman, H. (1988). Plasma sprayed coatings. Scientific American, 259(3), 78–83.
Hocking, M. G. (1993). Coatings resistant to erosive/corrosive and severe environments. Surface and Coatings Technology, 62, 460–466.
Hwang, Y. S., & Rapp, R. A. (1989). Thermochemistry and solubilities of oxides in sodium sulfate-vanadate solutions. Corrosion, 45(11), 933–937.
Iyer, S. R., Iyer, K. J. L., & Radhakrishan, V. M. (1987). High temperature corrosion of a Ni-base superalloy by Vanadium. In Proceedings of the 10th ICMC (Vol. IV, pp. 3665–3670) Madras, India.
Jordan, E. H., Gell, M., Sohn, Y. H., Goberman, D., Shaw, L., Jiang, S., et al. (2001). Fabrication and evaluation of plasma sprayed nanostructured alumina-titania coatings with superior properties. Materials Science and Engineering: A, 301, 80–89.
Kamachi Mudali, U., Bhuvaneswaran, N., Shankar, P., & Raj, Baldev. (2004). Corrosion behaviour of intermetallic aluminide coatings on nitrogen-containing austenitic stainless steels. Corrosion Science, 46, 2867–2892.
Kamal, S., Jayaganthan, R., & Prakash, S. (2009). Evaluation of cyclic hot corrosion behaviour of detonation gun sprayed Cr3C2–NiCr coating on nickel and iron based superalloys. Surface and Coatings Technology, 203(8), 1004–1013.
Kamal, S., Jayaganthan, R., & Prakash, S. (2010). Hot corrosion studies of detonation-gun-sprayed NiCrAlY + 0.4 wt%CeO2 coatings on superalloys in molten salt environment. Journal of Materials Engineering and Performance, 20(6), 1068–1077.
Kamal, S., Jayaganthan, R., Prakash, S., & Kumar, Sanjay. (2008). Hot corrosion behavior of detonation gun sprayed Cr3C2–NiCr coatings on Ni and Fe-based superalloys in Na2SO4–60 % V2O5 environment at 900 °C. Journal of Alloys and Compounds, 463(1-2), 358–372.
Kawase, R., & Nakano, A. (1996). Production of heat and corrosion-resistant plastic coating. In Proceedings of the 9th National Thermal Spray Conference (pp. 257–262). Cincinnati, Ohio.
Kerby, R. C., & Wilson, J. R. (1972). Electrical conduction properties of liquid vanadates. II. The sodium. Canadian Journal of Chemistry, 58, 2871–2876.
Khajavi, M. R., & Shariat, M. H. (2004). Failure of first stage gas turbine blades. Engineering Failure Analysis, 11, 589–597.
Khana, A. S., & Jha, S. K. (1998). Degradation of materials under hot corrosion conditions. Transactions of the Indian Institute of Metals, 51(5), 279–290.
Kim, J.-H., Yang, H.-S., Baik, K.-H., Seong, B. G., Lee, C.-H., & Hwang, S. Y. (2006). Development and properties of nanostructured thermal spray coatings. Current Applied Physics, 6(6), 1002–1006.
Knotek, O. (2001). Thermal spraying and detonation spray gun processes. In R. F. Bunshah (Ed.) Handbook of hard coatings: Deposition technologies, properties and applications. Noyes Pub. Park Ridge, New Jersey, USA/William Andrew Publishing, LLC, Norwich, New York, USA (pp. 77–107) (Chapter 3).
Koch, G. H., Brongers, M. P. H., Thompson, N. G., Virmani, Y. P., & Payer, J. H. (2002). Historic congressional study: Corrosion costs and preventive strategies in the United States. Supplement to Materials Performance, 1–11.
Kofstad, P. (1988). High temperature corrosion (p. 465). London, New York: Elsevier Applied Science. (Chapter 14).
Kolta, G. A., Hewaidy, L. F., & Felix, N. S. (1972). Reactions between sodium sulphate and vanadium pentoxide. Thermochimica Acta, 4, 151–164.
Korpiola, K., & Vuoristo, P. (1996). Effect of HVOF gas velocity and fuel to oxygen ratio on the wear properties of tungsten carbide coating. In C. C. Bernt, (Ed.), Thermal spray: Practical solutions for engineering problems. Cincinnati, USA: ASM, October, 11–17.
Kuroda, S., Kawakita, J., Watanabe, Makoto., & Katanoda, Hiroshi. (2008). Topical review warm spraying—a novel coating process based on high-velocity impact of solid particles. Science and Technology of Advanced Materials, 9, 1–17.
Lambert, P., Champagne, B., & Arseneault, B. (1991). Oxidation and hot corrosion in Na2SO4—10 %V2O5 of Ni-17Cr-6Al-0.5Y and Ni-16Cr-5.7Al-0.47Y-5Si, MCrAlY Alloys at 7000 C. Canadian Metallurgical Quarterly, 30(2), 125–130.
Leblanc, L. (2003). Abrasion and sliding wear of nanostructured ceramic coatings. In C. Moreau & B. Marple (Eds.), Thermal spray 2003: Advancing the science & applying the technology (pp. 291–299). Materials Park, Ohio, USA: ASM International.
Li, Y. S., Spiegel, M., & Shimada, S. (2005). Corrosion behaviour of various model alloys With NaCl–KCl coating. Materials Chemistry and Physics, 93, 217–223.
Liang, Bo., & Ding, Chuanxian. (2005). Thermal shock resistances of nanostructured and conventional zirconia coatings deposited by atmospheric plasma spraying. Surface and Coatings Technology, 197, 185–192.
Lin, Xinhua., Zeng, Yi., Ding, Chuanxian., & Zhang, Pingyu. (2004). Effects of temperature on tribological properties of nanostructured and conventional Al2O3–3 wt% TiO2 coatings. Wear, 256, 1018–1025.
Liu, P. S., Liang, K. M., Zhou, H. Y., Gu, S. R., Sun, X. F., Guan, H. R., et al. (2001). Cyclic oxidation behavior of aluminide coatings on the Co-base superalloy DZ40M. Surface and Coatings Technology, 145, 75–79.
Luthra, K. L., & Shores, D. A. (1980). Mechanism of Na2SO4 induced corrosion at 600–900 °C. Journal of the Electrochemical Society, 127(10), 2202–2210.
Maledi, N. B., Potgieter, J. H., Sephton, M., Cornish, L. A., Chown, L., & Suss, R. (2006). Hot corrosion behaviour of Pt-alloys for application in the next generation of gas turbines. International Platinum Conference ‘Platinum Surges Ahead’, the Southern African Institute of Mining and Metallurgy (pp. 81–90).
Marceau, J. A., & Adjorlolo, A. A. (1995). Commercial aircraft. In ASM, Corrosion tests and standards; application and interpretation (pp. 574–578). American Society for Testing and Material Society.
Matthews S. J. (2004). Erosion-corrosion of Cr3C2–NiCr high velocity thermal spray coatings (Ph.D. thesis). The University of Auckland.
Mevrel, R. (1989). State of the art on high-temperature corrosion-resistant coatings. Materials Science and Engineering: A, 120, 13–24.
Misra, A. K. (1986). Mechanism of Na2SO4-induced corrosion of molybdenum containing nickel-base superalloys at high temperatures. Journal of the Electrochemical Society, 133(5), 1029–1037.
Moujahid, S. E. (1987). High temperature corrosion of cast iron chains by Coal Ash. In Proceedings of the 10th ICMC (Vol. I, pp. 857–860). Madras, India.
Murthy, J. K. N., & Venkataraman, B. (2006). Abrasive wear behaviour of WC–CoCr and Cr3C2–20(NiCr) deposited by HVOF and detonation spray processes. Surface and Coatings Technology, 200, 2642–2652.
Natesan, K. (1985). High-temperature corrosion in coal gasification systems. Corrosion, 41(11), 646–655.
National Materials Advisory Board. (1996). Coatings for high-temperature structural materials: Trends and opportunities (pp. 1–85). Washington, DC: National Academy Press. http://www.nap.edu/openbook/0309053811/html
Nelson, H. W., Krause, H. H., Ungar, E. W., Putnam, A. A., Slunder, C. J., Miller, P. D., et al. (1959). A review of available information on, corrosion and deposits in coal- and oil-fired boilers and gas turbines. Report of ASME research committee on corrosion and deposits from combustion gases. New York: Pergamon Press, ASME.
Nerz, J. E., Kushner B. A., Jr., & Rotolico, A. J. (1992). Microstructural evaluation of tungsten carbide-cobalt coatings. ASM International (USA) (pp. 115–120).
Nicholls, J. R. (2000). Designing oxidation-resistant coatings. JOM, 52, 28–35.
Nicholls, J. R., Simms, N. J., Chan, W. Y., & Evans, H. E. (2002). Smart overlay coatings—concept and practice. Surface and Coatings Technology, 149, 236–244.
Nickel, H., Quadakkers, W. J., & Singheiser, L. (2002). Analysis of corrosion layers on protective coatings and high temperature materials in simulated service environments of modern power plants using SNMS, SIMS, SEM, TEM, RBS and X-ray diffraction strudies. Analytical and Bioanalytical Chemistry, 374, 581–587.
Nicoll, A. R. (1984). The production and performance evaluation of high temperature coatings. In K. N. Strafford, P. K. Datta, & C. G. Googan (Eds.), Coatings and surface treatment for corrosion and wear resistance. Chichester: Institution of Corros. Sci. and Techol., Birmingham, Pub. Ellis Horwood Ltd. (Chapter 13).
Otero, E., Merino, M. C., Pardo, A., Biezma, M. V., & Buitrago, G. (1987). Study on corrosion products of IN657 alloy in molten salts. In Proceedings of 10th ICMC (Vol. IV, pp. 3583–3591). Madras, India.
Otero, E., Pardo, A., Hernaez, J., & Perez, F. J. (1990). The hot corrosion of IN-657 superalloy in Na2SO4–V2O5 melt eutectic. Corrosion Science, 30, 677–683.
Otsuka, N., & Rapp, R. A. (1990). Effects of chromate and vanadate anions on the hot corrosion of pre oxidized Ni by a thin fused Na2SO4 film at 900 °C. Journal of the Electrochemical Society, 137(1), 53–60.
Pettit, F. (2011). Hot corrosion of metals and alloys. Oxidation of Metals, 76, 1–21.
Pettit, F. S., & Giggins, C. S. (1987). Hot corrosion. In C. T. Sims, N. S. Stollof, & W. C. Hagel (Eds.), Superalloys II. N Y: Pub. Wiley Pub. (Chapter 12).
Pettit, F. S., & Meier, G. H. (1985). Oxidation and hot corrosion of superalloys. In M. Gell, C. S. Kartovich, R. H. Bricknel, W. B. Kent & J. F. Radovich (Eds.), Superalloys 85 (pp. 651–687). Warrendale, Pennsylvania: Met. Soc. of AIME.
Porcayo-Calderon, J., Gonzalez-Rodriguez, J. G., & Martinez, L. (1998). Protection of carbon steel against hot corrosion using thermal spray Si- and Cr-base coatings. Journal of Materials Engineering and Performance, 7, 79–87.
Gitanjaly, & Prakash, S. (1999). Review on effect of additives on the hot corrosion. In 5th NACE Proceedings (pp. 174-182). New Delhi, India, November 22–24.
Prakash, S., Puri, D., & Singh, H. (2005). Hot corrosion behaviour of plasma sprayed coating on Ni-based superalloys in Na2SO4–60 %V2O5 environment. ISIJ International, 45(6), 886–895.
Prakash, S., Singh, S., Sidhu, B. S., & Madeshia, A. (2001). Tube failures in coal fired boilers. In Proceedings of the National Seminar on Advances in Material and Processing (pp. 245–253) IITR, Roorkee, India, November 9–10.
Priyantha, N., Jayaweera, P., Sanjurjo, A., Lau, K., Lu, F., & Krist, K. (2003). Corrosion-resistant metallic coatings for applications in highly aggressive environments. Surface and Coatings Technology, 163–64, 31–36.
Rapp, R. A. (2002). Hot corrosion of materials: A fluxing mechanism. Corrosion Science, 44(2), 209–221.
Rapp, R. A., & Goto, K. S. (1981). The hot corrosion of metals by Molten Salts. In J. Braunstein & J. R. Selman (Eds.), Sympos. fused salts (pp. 159). Pennington, NJ: The Electrochemical Society.
Rapp, R. A., & Mehl, Robert. F. (2000). Some generalities in the analyses of equilibria in lonic solutions. Metallurgical and Materials Transactions A, 31(9), 2105–2118.
Ravindra, T., Raghavan, S., & Kamaraj, M. (2007). Hot corrosion and oxidation behaviour of a directionally solidified nickel base superalloy. Transactions of the Indian Institute of Metals, 60, 385–392.
Ren, X., & Wang, F. (2006). High-temperature oxidation and hot-corrosion behavior of a sputtered NiCrAlY coating with and without aluminizing. Surface and Coatings Technology, 201, 30–37.
Salmenoja, K., Makela, K., Hupa, M., & Backman, R. (1996). Superheater corrosion in environments containing potassium and chlorine. Journal of the Institute of Energy, 69, 155–162.
Saravanan, P., Selvarajan, V., Rao, D. S., Joshi, S. V., & Sundararajan, G. (2000). Influence of process variables on the quality of detonation gun sprayed alumina coatings. Surface and Coatings Technology, 123, 44–54.
Seiersten, M., & Kofstad, P. (1987). The effect of SO3 on vanadate-induced hot corrosion. High Temperature Technology, 5(3), 115–122.
Seybolt, A. U. (1968). Hot corrosion mechanism. Transactions of the Metallurgical Society of AIME, 242, 1955–1961.
Sharma, R. N. (1996). Hot corrosion behaviour of iron- and nickel-base superalloys in salt environments at elevated temperatures (Ph.D. thesis). Met. Mat. Engg. Deptt., University of Roorkee, Roorkee, India.
Shaw, L. L., Goberman, D., Ren, R., Gell, M., Jiang, S., Wang, Y., et al. (2000). The dependency of microstructure and properties of nanostructured coatings on plasma spray conditions. Surface and Coatings Technology, 130, 1–8.
Shi, L., Zhang, Y., & Shih, S. (1992). The effect of K2SO4 additive in Na2SO4 deposits on low temperature hot corrosion of iron-aluminum alloys. Oxidation of Metals, 38, 385–405.
Shih, S., Zhang, Y., & Li, X. (1989). Sub-melting point hot corrosion of alloys and coatings. Materials Science and Engineering A, 120, 277–282.
Sidhu, T. S., Prakash, S., & Agrawal, R. D. (2006a). Performance of high velocity oxy fuel—sprayed coating on an Fe-based superalloy in Na2SO4–60 % V2O5 environment at 900 °C part II: Hot corrosion behaviour of coating. Journal of Materials Engineering and Performance, 15, 130–138.
Sidhu, T. S., Prakash, S., & Agrawal, R. D. (2006b). Hot corrosion studies of HVOF sprayed Cr3C2–NiCr and Ni–20Cr coatings on nickel-based superalloy at 900 °C. Surface and Coatings Technology, 201(3-4), 792–800.
Sidhu, T. S., Prakash, S., & Agrawal, R. D. (2006c). Hot corrosion studies of HVOF NiCrBSi and stellite-6 coatings on a Ni-based superalloy in an actual industrial environment of a coal fired boiler. Surface and Coatings Technology, 201(3/4), 1602–1612.
Sidhu, T. S., Prakash, S., & Agrawal, R. D. (2006d). Characterisation of NiCr wire coatings on Ni- and Fe-based superalloys by the HVOF process. Surface and Coatings Technology, 200, 5542–5549.
Sidhu, T. S., Prakash, S., & Agrawal, R. D. (2006e). Studies of the metallurgical and mechanical properties of high velocity oxy-fuel sprayed stellite-6 coatings on Ni- and Fe-based superalloys. Surface and Coatings Technology, 201(1/2), 273–281.
Sidhu, H. S., Sidhu, B. S., & Prakash, S. (2006f). The role of HVOF coatings in improving hot corrosion resistance of ASTM-SA210 GrA1 steel in the presence of Na2SO4–V2O5 salt deposits. Surface and Coatings Technology, 200, 5386–5394.
Sidky, P. S., & Hocking, M. G. (1999). Review of inorganic coatings and coating processes for reducing wear and corrosion. British Corrosion Journal, 34(3), 171–183.
Simons, E. L., Browning, G. V., & Liebhatsky, H. A. (1955). Corrosion, 11, 505.
Singh, H., Puri, D., & Prakash, S. (2005a). Some studies on hot corrosion performance of plasma sprayed coatings on a Fe-based superalloy. Surface and Coatings Technology, 192(1), 27–38.
Singh, H., Puri, D., & Prakash, S. (2005b). Corrosion behaviour of plasma sprayed coating on Ni-based superalloys in Na2SO4–60%V2O5 environment at 900 °C. ISIJ International, 45(6), 886–895.
Sobolev, V.V., Guilemany, J.M., & Nutting, J. (2004). HVOF spraying. B0655, Maney, IOM3 (pp. 5).
Soltani, R., Coyle, T. W., & Mostaghimi, J. (2003). Wear resistance of nanostructured thermal barrier coatings. In C. Moreau & B. Marple (Eds.), Thermal spray 2003: Advancing the science & applying the technology (pp. 1535–1540). Materials Park, Ohio, USA: ASM International.
Stokes, J., & Looney, L. (2001). HVOF system definition to maximise the thickness of formed components. Surface and Coatings Technology, 148, 18–24.
Stott, F. H., De Wet, D. J., & Taylor, R. (1994). The degradation resistance of thermal barrier coatings to molten deposits at very high temperatures. Transactions of the Materials Research Society of Japan, 14A, 135–140.
Stringer, J. (1977). Hot corrosion of high temperature alloys. Annual Review of Materials Research, 7, 477–509.
Stringer, J. (1987). High temperature corrosion of superalloys. Materials Science and Technology, 3(7), 482–493.
Stringer, J. (1998). Coatings in the electricity supply industry: past, present, and opportunities for the future. Surface and Coatings Technology, 108–109, 1–9.
Stroosnijder, M. F., Mevrel, R., & Bennet, M. J. (1994). The interaction of surface engineering and high temperature corrosion protection. Materials at High Temperatures, 12(1), 53–66.
Suito, H., & Gaskell, D. R. (1971). The thermodynamics of melts in the system VO2–V2O5. Metallurgical and Materials Transactions B, 2, 3299–3303.
Taylor, M. P., & Evans, H. E. (2001). The influence of bond coat surface roughness and structure on the oxidation of a thermal barrier coating system. Materials Science Forum, 369–372, 711–717.
Tiwari, S. N. (1997). Investigations on hot corrosion of some Fe-, Ni- and Co-base superalloy in Na2SO4–V2O5 environment under cyclic conditions (Ph.D. thesis). Met. Mat. Engg. Deptt., University of Roorkee, Roorkee, India.
Tiwari, S. N., & Prakash, S. (1996). Hot corrosion behaviour of an iron-base superalloy in salt environment at elevated temperatures. In Proceedings of the Symposium Metals and Materials Research, Indian Institute of Technology Madras (pp. 107–117) Madras, July 4–5.
Tiwari, S. N., & Prakash, S. (1997). Studies on the hot corrosion behaviour of some superalloys in Na2SO4–V2O5. In Proceedings of the SOLCEC, Kalpakkam, India, January 22–24, Paper C33.
Tiwari, S. N., & Prakash, S. (1998). Literature review-magnesium oxide as inhibitor of hot oil ash corrosion. Materials Science and Technology, 14, 467–472.
Tzvetkoff, T., & Gencheva, P. (2003). Mechanism of formation of corrosion layers on nickel and nickel-based alloys in melts containing Ox anions—A review. Materials Chemistry and Physics, 82(3), 897–904.
Uusitalo, M. A., Vuoristo, P. M. J., & Mantyla, T. A. (2004). High temperature corrosion of coatings and boiler steels below chlorine-containing salt deposits. Corrosion Science, 46(6), 1311–1331.
Valdes, C. J., Dooley, R. B., & Wilson, J. R. (1973). The corrosion of A.I.S.I 446 stainless steel in Molten Vanadates in the temperature range 700–900 °C (Grant No. 7535-14). Report Defense Research Board Canada.
Wagner, N., Gnadic, K., Kreye, H., & Kronewetter, H. (1984). Particle velocity in hypersonic flame spraying of WC-Co. Surface and Coatings Technology, 22, 61–71.
Wang, Q. M., Wu, Y. N., Ke, P. L., Cao, H. T., Gong, J., Sun, C., et al. (2004). Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys. Surface and Coatings Technology, 86, 389–397.
Yoshiba, M. (1993). Effect of hot corrosion on the mechanical performances of superalloys and coating systems. Corrosion Science, 35(5–8), 1115–1124.
Zhang, Y. S., & Rapp, R. A. (1987). Solubilities of CeO2, HfO2 and Y2O3 in fused Na2SO4–30 mol% NaVO3 and CeO2 in pure Na2SO4 at 900 °C. Corrosion, 43(6), 348–352.
Zheng, D., Zhu, S., & Wang, F. (2006). Oxidation and hot corrosion behavior of a novel enamel-Al2O3 composite coating on K38G superalloy. Surface and Coatings Technology, 200, 5931–5936.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2017 Springer International Publishing Switzerland
About this chapter
Cite this chapter
Kamal, S., Sharma, K.V., Srinivasa Rao, P., Mamat, O. (2017). Thermal Spray Coatings for Hot Corrosion Resistance. In: Korada, V., Hisham B Hamid, N. (eds) Engineering Applications of Nanotechnology. Topics in Mining, Metallurgy and Materials Engineering. Springer, Cham. https://doi.org/10.1007/978-3-319-29761-3_10
Download citation
DOI: https://doi.org/10.1007/978-3-319-29761-3_10
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-29759-0
Online ISBN: 978-3-319-29761-3
eBook Packages: EngineeringEngineering (R0)