RETRACTED CHAPTER: An Intense Green Emission From ZnO Nanoparticles Coated with MgO

  • K. Sowri Babu
  • A. Ramachandra Reddy
  • K. Venugopal Reddy
Conference paper
Part of the Environmental Science and Engineering book series (ESE)

Abstract

This paper addresses the effects of annealing temperature on photoluminescence of ZnO nanoparticles coated with MgO. ZnO nanoparticles as well as ZnO coated with MgO showed only a sharp UV emission peak positioned at 396 nm at an annealing temperature of 600 °C. As the annealing temperature increased from 600 to 900 °C, the intensity of green emission enhanced monotonously. The green emission intensity at 900 °C is 18 times higher than its value at 700 °C. But at 1,000 °C, green emission intensity decreased. FT-IR spectra of ZnO@MgO showed that MgO evaporation took place with increase of temperature from 700 to 1,000 °C. These results indicates that intensity of green emission depends on thickness of MgO shell coated over the ZnO nanoparticles.

Keywords

ZnO nanoparticles Photoluminescence Annealing temperature MgO 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Y.G. Wang, S.P. Lau, H.W. Lee, S.F. Yu, B.K. Tay, X.H. Zhang and H.H. Hng, J Appl Phys, 94:354 (2003).Google Scholar
  2. 2.
    A. Sharma, B.P. Singh, S. Dhar S, A. Gondorf, M. Spasova, Surf. Sci. 606, L13, (2012).Google Scholar
  3. 3.
    B. Guo, Z.R. Qiu, K.S. Wong, Appl Phys Lett, 82, 2290 (2003).Google Scholar
  4. 4.
    H.F. Liu, S.J. Chua, G.X. Hu, H. Gong and N. Xiang, J Appl Phys, 102, 043530 (2007).Google Scholar
  5. 5.
    K. Sowri Babu, A. Ramachandra Reddy, Ch. Sujatha and K.V.G. Reddy, Mater. Lett. 99, 97 (2013).Google Scholar
  6. 6.
    K. Sowri Babu, A. Ramachandra Reddy, Ch. Sujatha, K.V.G. Reddy and A.N. Mallika, Mater. Lett. 110, 10 (2013).Google Scholar
  7. 7.
    X. Q. Meng, Haowei Peng, Y. Q. Gai, and Jingbo Li, J. Phys. Chem. C, 114,1467, (2010).Google Scholar
  8. 8.
    Z. Fu, W. Dong, B. Yang, Z. Wang, Y. Yang, H. Yan, S. Zhang, J. Zuo, M. Ma and X. Liu, Solid. State. Commun, 138, 179, (2006).Google Scholar
  9. 9.
    G. N. Panin, A. N. Baranov, I. A. Khotina and T. W. Kang, J. Korean Phys. Soc.53, 48, (2012).Google Scholar
  10. 10.
    K. Sowri Babu, A. Ramachandra Reddy and K.V.G. Reddy, Sol-gel synthesis and optical properties of ZnO@MgO nanocrystals, under revision in Materials science in semiconductor processing.Google Scholar
  11. 11.
    J. Zhang, Z. Zhang and T. Wang, Chem. Mater.,16,768 (2004).CrossRefGoogle Scholar

Copyright information

© Springer International Publishing Switzerland 2014

Authors and Affiliations

  • K. Sowri Babu
    • 1
  • A. Ramachandra Reddy
    • 1
  • K. Venugopal Reddy
    • 1
  1. 1.Department of Physics, Materials Science LaboratoryNational Institute of Technology WarangalWarangalIndia

Personalised recommendations