Effect of Substrate Temperature Variation and Tartarization on micro-Structural and Optical Properties of Pulsed DC Sputtered Hydrogenated ZnO: Al Films

  • Chandra Bhal Singh
  • Surajit Sarkar
  • Vandana Singh
Conference paper
Part of the Environmental Science and Engineering book series (ESE)

Abstract

In this work, hydrogenated ZnO: Al films have been deposited on glass substrate by pulsed dc magnetron sputtering unit at various substrate temperatures. The effect of substrate temperature on microstructural and optical properties of deposited films in hydrogen and Argon ambient was analyzed. Transmittance of films improved for films deposited at higher substrate temperature and reflectance decrease which is good as transparent conducting oxide for solar cells application. The wet chemical etching of hydrogenated films was performed to improve the light trapping in films. Films deposited at 250 °C showed lower resistivity and higher roughness after wet chemical etching than films deposited at room temperature. Films deposited at 150 °C shows better films quality as well as lower resistivity than films deposited at room temperature and 250 °C. This suggests that film’s microstructural, optical and electrical properties behave differently in hydrogen gas ambient and hydrogen improve films quality and conductivity at lower temperature.

Keywords

Thin films Substrate temperature Transparent conductive oxide and band gap 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    G. J. Exarhos, and X. D. Zhou, Thin Solid Films 515, 7025 (2007).CrossRefGoogle Scholar
  2. 2.
    C.B Singh, S. Bhattacharya, V. Singh, P.B. Bhargav, S. Sarkar, V. Bhavnasi, N. Ahmed, J. Renewable Sustainable Energy 5, 031605 (2013)Google Scholar
  3. 3.
    S. Major, S. Kumar, M. Bhatnagar, K.L. Chopra, Appl. Phys. Lett. 49, 394(1986).CrossRefGoogle Scholar
  4. 4.
    S. J. Tark, M. G. Kang, S. Park, J.H. Jang, J. C. Lee, W. M. Kim, J. S. Lee, and D. Kim, Current Applied Physics 9, 1318 (2009).CrossRefGoogle Scholar
  5. 5.
    H. B. Zhou, H. Y. Zhang, Z. G. Wang, and M. L. Tan, Materials Letters 74, 96 (2012).CrossRefGoogle Scholar
  6. 6.
    V. Bhavnasi, C. B. Singh, D. Datta, V. Singh, K. Shahi and S. Kumar, Optical Materials 35, 1352 (2013)CrossRefGoogle Scholar
  7. 7.
    Z. Yu, A. Raman, S. Fan, PNAS 107, 17491 (2010).Google Scholar
  8. 8.
    F. Couzinié-Devy, N. Barreau, J. Kessler, Thin Solid Films 516, 7094 (2008).CrossRefGoogle Scholar
  9. 9.
    J. Tauc, R. Grigorovici, A. Vancu, Phys. State Solid 15, 627 (1966)Google Scholar
  10. 10.
    R. Menon, V. Gupta, H. H. Tan, K. Sreenivas, C. Jagadish, J. Appl.Phys. 109, 064905 (2011).Google Scholar
  11. 11.
    R. Swanepoel, J. Phys. E:Sci. Intrum. 17, 896 (1984).Google Scholar
  12. 12.
    F. Urbach, Phys. Rev 92, 1324 (1953).Google Scholar

Copyright information

© Springer International Publishing Switzerland 2014

Authors and Affiliations

  • Chandra Bhal Singh
    • 1
  • Surajit Sarkar
    • 2
  • Vandana Singh
    • 3
  1. 1.SSN Research CentreKalavakkamIndia
  2. 2.Department of PhysicsIIT KanpurKanpurIndia
  3. 3.Samtel Centre for Display TechnologiesIIT KanpurKanpurIndia

Personalised recommendations