Effect of Cu3N Layer Thickness on Corrosion and Ni Release Properties of Cu3N/NiTiCu Shape Memory Thin Films

  • Navjot Kaur
  • Davinder Kaur
Conference paper
Part of the Environmental Science and Engineering book series (ESE)


In the present study Cu3N/NiTiCu/Si thin films were successfully grown using magnetron sputtering technique. The thickness of nanocrystalline Cu3N was varied from 200 to 415 nm and effect of Cu3N layer thickness on structural, phase transformation, morphological, corrosion and Ni release properties of Cu3N/NiTiCu/Si was studied. The NiTiCu/Si thin films exhibit shape memory effect even after depositing Cu3N protective layer. Cu3N(200, 305 nm)/NiTiCu/Si thin films possess low corrosion current density with higher corrosion potential and therefore exhibit better corrosion resistance as compared Cu3N(415 nm)/NiTiCu/Si film. The amount of Ni ions released in SBF solution was almost not detectable in case of 200, 305 nm thin Cu3N layer but increased significantly on increasing the thickness of Cu3N layer to 415 nm. Cu3N(415 nm)/NiTiCu/Si exhibit much reduced corrosion resistance and Ni ion release impeding capability. This can be explained by decrease in adherence of Cu3N(~415 nm) layer on NiTiCu/Si thin film due to its increased thickness. This work is of immense technological importance due to its variety of its BioMEMS applications.


Thin films Corrosion and Ni release 


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.



The financial support provided by Ministry of Communications and Information Technology (MIT), India, under Nanotechnology Initiative Program with Reference no. 20(11)/2007 VCND is highly acknowledged. The author Navjot Kaur is thankful to Ministry of human Resource and Development (MHRD), India for award of Senior Research Fellowship.


  1. 1.
    N.Kaur, N.Choudhary, R.N.Goyal, S.Viladkar, I.Matai, P.Gopinath, S.Chockalingam and D.Kaur, J Nanopart Res, 15, 1468 (2013).Google Scholar
  2. 2.
    S.K. Wu, C.L. Chu and H.C.Lin, Surf Coat Technol, 92,197 (1997).Google Scholar
  3. 3.
    L.Tan, R.A.Dodd and W.C.Crone, Biomaterials, 24, 3931 (2003).CrossRefGoogle Scholar
  4. 4.
    Y.Fu, H.Du and S.Zhang, Surf Coat Technol, 167,129 (2003).Google Scholar
  5. 5.
    A. Kumar, D. Singh, R. Kumar and D. Kaur, J. Alloys Compd., 479,166 (2009).Google Scholar
  6. 6.
    D.Sheeja, B.K. Tay, K.W. Leong and C.H. Lee, Diamond and Related Materials,11,1643(2002).CrossRefGoogle Scholar

Copyright information

© Springer International Publishing Switzerland 2014

Authors and Affiliations

  1. 1.Functional Nanomaterials Research Lab, Department of Physics and Centre for NanotechnologyIndian Institute of Technology RoorkeeRoorkeeIndia

Personalised recommendations