Abstract
Oxidation resistant overlay coatings protect the underlying superalloy component in industrial gas turbines from oxidation attack. Rate of depletion of the Al-rich β-phase in the bond coat governs the lifetime of these coatings. The applicability of a computational method in accelerating the development of corrosion resistant coatings and significantly reducing the extensive experimental effort to predict coating lifetimes and microstructural changes in three-coated Ni-based superalloys for real operational durations (20–40 kh) was undertaken in the present study. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), and electron microprobe analysis (EPMA) were employed to characterize MCrAlY-coated superalloy substrates (1483, 247 and X4) after exposure at 900 °C in air + 10% H2O for up to 20,000 h. The model predicted the longest coating lifetime for the coating on X4 substrate. Precipitation of γ′ in the coatings was correctly predicted for all three coating systems. Additionally, the model was able to predict the formation of topologically close packed (TCP)-phases in the investigated coating systems.
This manuscript has been authored by UT-Battelle, LLC, under contract DE-AC05-00OR22725 with the US Department of Energy (DOE). The US government retains and the publisher, by accepting the article for publication, acknowledges that the US government retains a nonexclusive, paid-up, irrevocable, worldwide license to publish or reproduce the published form of this manuscript, or allow others to do so, for US government purposes. DOE will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan (http://energy.gov/downloads/doe-public-access-plan).
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Similar content being viewed by others
References
Goward GW (1998) Progress in coatings for gas turbine airfoils. Surface & Coatings Technology 108(1–3) 73–79.
Quadakkers WJ, Shemet V, Sebold D, Anton R, Wessel E, Singheiser L (2005) Oxidation characteristics of a platinized MCrAlY bond coat for TBC systems during cyclic oxidation at 1000 degrees C. Surface & Coatings Technology 199(1) 77–82.
Haynes JA, Pint BA, Zhang Y, Wright IG (2007) Comparison of the cyclic oxidation behavior of beta-NiAl, beta-NiPtAl and gamma-gamma’ NiPtAl coatings on various superalloys. Surface & Coatings Technology 202(4–7) 730–734.
Naumenko D, Shemet V, Singheiser L, Quadakkers WJ (2009) Failure mechanisms of thermal barrier coatings on MCrAlY-type bondcoats associated with the formation of the thermally grown oxide. Journal of Materials Science 44(7) 1687–1703.
Pint BA, Haynes JA, Zhang Y (2010) Effect of superalloy substrate and bond coating on TBC lifetime. Surface & Coatings Technology 205(5) 1236–1240.
Achar DRG, Munoz-Arroyo R, Singheiser L, Quadakkers WJ (2004) Modelling of phase equilibria in MCrAlY coating systems. Surface & Coatings Technology 187(2–3) 272–283.
Munoz-Arroyo R, Clemens D, Tietz F, Anton R, Quadakkers J, Singheiser L, Influence of composition and phase distribution on the oxidation behaviour of NiCoCrAlY alloys, in: R. Streiff, I.G. Wright, R.C. Krutenat, M. Caillet, A. Galerie (Eds.), High Temperature Corrosion and Protection of Materials 5, Pts 1 and 22001, pp. 165–172.
Pillai R, Taylor MP, Galiullin T, Chyrkin A, Wessel E, Evans H, Quadakkers WJ (2018) Predicting the microstructural evolution in a multi-layered corrosion resistant coating on a Ni-base superalloy. Materials at High Temperatures 35(1–3) 78–88.
Lee EY, Chartier DM, Biederman RR, Sisson RD (1987) Modeling the Microstructural Evolution and Degradation of MCrAlY Coatings During High-Temperature Oxidation. Surf. Coat. Tech. 32(1–4) 19–39.
Nijdam TJ, Sloof WG (2008) Modelling of composition and phase changes in multiphase alloys due to growth of an oxide layer. Acta Materialia 56(18) 4972–4983.
Karunaratne MSA, Di Martino I, Ogden SL, Oates DL, Thomson RC (2012) Modeling of Microstructural Evolution in an MCrAlY Overlay Coating on Different Superalloy Substrates. Metallurgical and Materials Transactions A 43(2) 774–788.
Yuan K, Eriksson R, Peng RL, Li X-H, Johansson S, Wang Y-D (2013) Modeling of microstructural evolution and lifetime prediction of MCrAlY coatings on nickel based superalloys during high temperature oxidation. Surface & Coatings Technology 232 204–215.
Pillai R, Sloof WG, Chyrkin A, Singheiser L, Quadakkers WJ (2015) A new computational approach for modelling the microstructural evolution and residual lifetime assessment of MCrAlY coatings. Materials at High Temperatures 32(1–2) 57–67.
Pillai R, Jalowicka A, Galiullin T, Naumenko D, Ernsberger M, Herzog R, Quadakkers WJ (2019) Simulating the effect of aluminizing on a CoNiCrAlY-coated Ni-base superalloy. Calphad-Computer Coupling of Phase Diagrams and Thermochemistry 65 340–345.
Schindelin J, Arganda-Carreras I, Frise E, Kaynig V, Longair M, Pietzsch T, Preibisch S, Rueden C, Saalfeld S, Schmid B, Tinevez J-Y, White DJ, Hartenstein V, Eliceiri K, Tomancak P, Cardona A (2012) Fiji: an open-source platform for biological-image analysis. Nature Methods 9(7) 676–682.
Chan KS, Cheruvu NS, Leverant GR (1998) Coating life prediction under cyclic oxidation conditions. Journal of Engineering for Gas Turbines and Power-Transactions of the Asme 120(3) 609–614.
Larsson H, Strandlund H, Hillert M (2006) Unified treatment of Kirkendall shift and migration of phase interfaces. Acta Materialia 54(4) 945–951.
Larsson H, Engstrom A (2006) A homogenization approach to diffusion simulations applied to alpha + gamma Fe-Cr-Ni diffusion couples. Acta Materialia 54(9) 2431–2439.
TCNi8, Thermo-Calc Software TCNi8/Ni-based superalloys database version 8, 2018.
MobNi4, Thermo-Calc Software MobNi4/Ni-alloys mobility database version 4, 2018.
Achar DRG, Munoz-Arroyo R, Singheiser L, Quadakkers WJ (2004) Modelling of phase distributions in MCrAlY coatings and their interactions with nickel based alloys. Journal De Physique Iv 120 231–238.
Chyrkin A, Swadzba R, Pillai R, Galiullin T, Wessel E, Gruner D, Quadakkers WJ (2018) Stability of External alpha-Al2O3 Scales on Alloy 602 CA at 1100–1200 A degrees C. Oxidation of Metals 90(1–2) 119–133.
Naumenko D, Pillai R, Chyrkin A, Quadakkers WJ (2017) Overview on Recent Developments of Bondcoats for Plasma-Sprayed Thermal Barrier Coatings. Journal of Thermal Spray Technology 26(8) 1743–1757.
Gheno T, Liu XL, Lindwall G, Liu ZK, Gleeson B (2015) Experimental study and thermodynamic modeling of the Al-Co-Cr-Ni system. Sci Technol Adv Mat 16(5).
Liu XL, Gheno T, Lindahl BB, Lindwall G, Gleeson B, Liu ZK (2015) First-Principles Calculations, Experimental Study, and Thermodynamic Modeling of the Al-Co-Cr System. Plos One 10(4).
Matthew J. Donachie SJD, Superalloys: A Technical Guide, 2 ed., ASM International 2002.
Pillai R, Wessel E, Nowak WJ, Naumenko D, Quadakkers WJ (2018) Predicting Effect of Base Alloy Composition on Oxidation- and Interdiffusion-Induced Degradation of an MCrAlY Coating. Jom 70(8) 1520–1526.
Anton R, Quadakkers J, Untersuchung zu den Versagensmechanismen von Wärmedämmschicht-Systemen im Temperaturbereich von 900°C bis 1050°C bei zyklischer Temperaturbelastung, RWTH Aachen, Julich, 2003.
Darolia R, Lahrman DF, Field RD (1988) Formation of topologically closed packed phases in Nickel base single crystal superalloys. Superalloys 1988 255–264.
Rae CMF, Karunaratne M, Small CJ, Broomfield RW, Jones CN (2000) Topologically close packed phases in an experimental Rhenium-containing single crystal superalloy. Superalloys 2000 767–776.
Acknowledgements
G. Garner assisted with the experimental work at ORNL. T. Lowe and M. Romedenne are thanked for helping with microstructural characterization. This research was sponsored by the U.S. Department of Energy, Office of Fossil Energy, Advanced Turbine Program (R. Dennis program manager). The authors would like to thank K. Murphy at Howmet and A. Kulkarni at Siemens for providing superalloys.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2020 The Minerals, Metals & Materials Society
About this paper
Cite this paper
Pillai, R., Kane, K., Lance, M., Pint, B.A. (2020). Computational Methods to Accelerate Development of Corrosion Resistant Coatings for Industrial Gas Turbines. In: Tin, S., et al. Superalloys 2020. The Minerals, Metals & Materials Series. Springer, Cham. https://doi.org/10.1007/978-3-030-51834-9_81
Download citation
DOI: https://doi.org/10.1007/978-3-030-51834-9_81
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-030-51833-2
Online ISBN: 978-3-030-51834-9
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)