High Temperature Creep Properties of Cast Cobalt-Based Superalloys: A Comparison

  • 778 Accesses

Part of the Structural Integrity book series (STIN,volume 8)

Abstract

Cast cobalt-based superalloys have already found applications in the glass industry to construct glass shaping tools. The present study deals with the high temperature characterization of the two cast cobalt-based CoNb and CoTa superalloys which have been developed for precision casting of a rotary fibreglass spinner disc for glass industry. The superalloys have been characterized through constant load creep tests at 1000, 1050 and 1100 °C in a tensile stress range from 20 to 100 MPa, with the aim to simulate the variation of mechanical properties occurring in a rotary fibreglass spinner disc at operational conditions. The results have been compared and discussed, with the aim to link the difference in creep properties to the evolution of creep damage and fracture in superalloys. It was found that the CoNb superalloy possesses longer creep life compared to the CoTa superalloy under the same loading conditions. Fractographic investigations of the creep fractured specimens of the examined superalloys revealed that the dominating creep fracture of the CoTa is of the ductile transgranular dimple fracture mode due to a loss of an external section of specimen (necking). By contrast, the final brittle fracture in the CoNb superalloys occurs via relatively fast propagation of the longest cracks after the ultimate state of creep damage is reach.

Keywords

  • Cobalt-based superalloys
  • Creep damage and fracture
  • Breakage of primary carbides

This is a preview of subscription content, access via your institution.

Buying options

Chapter
USD   29.95
Price excludes VAT (USA)
  • DOI: 10.1007/978-3-030-21894-2_8
  • Chapter length: 6 pages
  • Instant PDF download
  • Readable on all devices
  • Own it forever
  • Exclusive offer for individuals only
  • Tax calculation will be finalised during checkout
eBook
USD   149.00
Price excludes VAT (USA)
  • ISBN: 978-3-030-21894-2
  • Instant PDF download
  • Readable on all devices
  • Own it forever
  • Exclusive offer for individuals only
  • Tax calculation will be finalised during checkout
Softcover Book
USD   199.99
Price excludes VAT (USA)
Hardcover Book
USD   279.99
Price excludes VAT (USA)
Fig. 1.
Fig. 2.
Fig. 3.
Fig. 4.
Fig. 5.

References

  1. Beltran, A.M.: Cobalt-Base Alloys, Superalloys II, Chap. 4, pp. 97–135. Wiley Inc., New York (1987)

    Google Scholar 

  2. Sklenička, V., Kvapilová, M., Král, P., Dvořák, J., Svoboda, M., Podhorná, B., Zýka, J., Hrbáček, K.: Joch, A: Degradation processes in high-temperature creep of cast cobalt-based superalloys. Mater. Character. 144, 479–489 (2018)

    CrossRef  Google Scholar 

  3. Kvapilova, M., Kral, P., Dvorak, J., Sklenicka, V.: Creep fracture ductility of cobalt-based superalloys. In: Gdoutos, E.E. (ed.) Proceedings of ICTAEM_1 Conference. pp. 184–189. Springer International Publishing AG, Cham, Swirtzerland (2018)

    Google Scholar 

  4. Zýka, J. et al.: Research Report No. UJP 1806. UJP PRAHA a.s., Czech Republic (2018)

    Google Scholar 

Download references

Acknowledgements

The authors acknowledge financial support for this study provided by the Ministry of Industry and Trade of the Czech Republic within the framework program MPO ČR Trio under the Project No. FV10699. The research infrastructure IPMinfra supported by the Ministry of Education, Youth and Sports through the Project No. LM2015069 was used.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Marie Kvapilova .

Editor information

Editors and Affiliations

Rights and permissions

Reprints and Permissions

Copyright information

© 2019 Springer Nature Switzerland AG

About this paper

Verify currency and authenticity via CrossMark

Cite this paper

Kvapilova, M., Sklenicka, V., Kral, P., Dvorak, J. (2019). High Temperature Creep Properties of Cast Cobalt-Based Superalloys: A Comparison. In: Gdoutos, E. (eds) Proceedings of the Second International Conference on Theoretical, Applied and Experimental Mechanics. ICTAEM 2019. Structural Integrity, vol 8. Springer, Cham. https://doi.org/10.1007/978-3-030-21894-2_8

Download citation

  • DOI: https://doi.org/10.1007/978-3-030-21894-2_8

  • Published:

  • Publisher Name: Springer, Cham

  • Print ISBN: 978-3-030-21893-5

  • Online ISBN: 978-3-030-21894-2

  • eBook Packages: EngineeringEngineering (R0)