Effects of Treatment on Microstructure and Deformation Behavior of Dissimilar Welded Joint Between Single Crystal and Polycrystalline Superalloy

  • 779 Accesses

Part of the Structural Integrity book series (STIN,volume 8)

Abstract

Dissimilar welding of Al + Ti rich and Nb rich nickel base superalloy has good welding performance. In this work, the tensile behavior of dissimilar Between Single Crystal and Polycrystalline Superalloy welded joint near its service temperatures (600–700 °C) was studied. The results show that the deformation behavior of the welded joint is closely related to the strength difference between difference regions. The yield strength (YS) and ultimate tensile strength (UTS) of the welded joint is dominated by the region with lower YS and UTS, which is Single Crystal Superalloy at 25–650 °C and Polycrystalline Superalloy at 660–700 °C. The plasticity of welded joint depends primarily on the magnitude of strength difference between different regions. Lower strength difference results in higher elongation. Both the UTS and elongation have peak values at 660 °C. The welded joints fail at Single Crystal Superalloy base metal at 25–650 °C while at Polycrystalline Superalloy base metal at 660–700 °C. The FZ has high strength and sufficient plasticity. Soft dendrites are surrounded and constrained by hard interdendrites. Fine discrete MC carbides and Laves phases in the interdendrites can effectively block the movement of dislocations from dendrites.

Keywords

  • Single crystal superalloy
  • Polycrystalline superalloy
  • Laser welding
  • Dissimilar welding
  • High temperature deformation

This is a preview of subscription content, access via your institution.

Buying options

Chapter
USD   29.95
Price excludes VAT (USA)
  • DOI: 10.1007/978-3-030-21894-2_10
  • Chapter length: 6 pages
  • Instant PDF download
  • Readable on all devices
  • Own it forever
  • Exclusive offer for individuals only
  • Tax calculation will be finalised during checkout
eBook
USD   149.00
Price excludes VAT (USA)
  • ISBN: 978-3-030-21894-2
  • Instant PDF download
  • Readable on all devices
  • Own it forever
  • Exclusive offer for individuals only
  • Tax calculation will be finalised during checkout
Softcover Book
USD   199.99
Price excludes VAT (USA)
Hardcover Book
USD   279.99
Price excludes VAT (USA)
Fig. 1.
Fig. 2.
Fig. 3.
Fig. 4.
Fig. 5.

References

  1. Karadge, M., Preuss, M., Withers, P., Bray, S.: Mater. Sci. Eng., A 491, 446–453 (2008)

    CrossRef  Google Scholar 

  2. Moosavy, H., Aboutalebi, M., Seyedein, S., Mapelli, C.: Mater. Charact. 82, 41–49 (2013)

    CrossRef  Google Scholar 

  3. Moosavy, H., Aboutalebi, M., Seyedein, S., Goodarzi, M., Mapelli, C.: Mater. Sci. Technol. 30, 339–347 (2014)

    CrossRef  Google Scholar 

  4. Roder, O., Albrecht, J., Lütjering, G.: Mater. High Temp. 23, 171–177 (2014)

    Google Scholar 

  5. Liang, T., Wang, L., Liu, Y., Song, X.: Met. Mater. Int. 7, 710–722 (2018)

    Google Scholar 

  6. Dupont, J.N., Lippold, J.C., Kiser, S.D.: Welding Metallurgy and Weldability of Nickel-base Alloys. Wiley, Canada (2009)

    CrossRef  Google Scholar 

  7. Xu, Y., Zhang, L., Li, J., Xiao, X., Cao, X., Jia, G., Shen, Z.: Mater. Sci. Eng., A 544, 48–53 (2012)

    CrossRef  Google Scholar 

  8. Wang, Y.L., Ojo, O.A., Ding, R.G., Chaturvedi, M.C.: Mater. Sci. Technol. 25, 68–75 (2009)

    CrossRef  Google Scholar 

  9. Xiao, H., Li, S., Han, X., Mazumder, J., Song, L.: Mater. Des. 122, 330–339 (2017)

    CrossRef  Google Scholar 

  10. Antonsson, T., Fredriksson, H.: Metall. Mater. Trans. B 36, 85–96 (2005)

    CrossRef  Google Scholar 

  11. Liang, T., Wang, L., Liu, Y., Song, X.: J. Mater. Eng. Perform. 27, 721–727 (2018)

    CrossRef  Google Scholar 

  12. Xie, H., Yu, T., Yin, F., Tang, C.: Mater. Sci. Eng., A 580, 99–104 (2013)

    CrossRef  Google Scholar 

  13. Xie, H.X., Wang, C.Y., Yu, T.: J. Mater. Res. 23, 1597–1603 (2008)

    CrossRef  Google Scholar 

  14. Sun, F., Zhang, J., Harada, H.: Acta Mater. 67, 45–57 (2014)

    CrossRef  Google Scholar 

Download references

Acknowledgements

This work was financially supported by the National Natural Science Foundation of China (51571052 and U1708253), and the Science and Technology Major Project (2017-VI-0002).

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Yang Liu .

Editor information

Editors and Affiliations

Rights and permissions

Reprints and Permissions

Copyright information

© 2019 Springer Nature Switzerland AG

About this paper

Verify currency and authenticity via CrossMark

Cite this paper

Liu, Y., Wang, L., Song, X., Liang, T., Hua, G. (2019). Effects of Treatment on Microstructure and Deformation Behavior of Dissimilar Welded Joint Between Single Crystal and Polycrystalline Superalloy. In: Gdoutos, E. (eds) Proceedings of the Second International Conference on Theoretical, Applied and Experimental Mechanics. ICTAEM 2019. Structural Integrity, vol 8. Springer, Cham. https://doi.org/10.1007/978-3-030-21894-2_10

Download citation

  • DOI: https://doi.org/10.1007/978-3-030-21894-2_10

  • Published:

  • Publisher Name: Springer, Cham

  • Print ISBN: 978-3-030-21893-5

  • Online ISBN: 978-3-030-21894-2

  • eBook Packages: EngineeringEngineering (R0)