Reduced pO2 Melt Processing of YBa2Cu3O6+x

  • M. A. Black
  • P. J. McGinn
Part of the Advances in Cryogenic Engineering Materials book series (ACRE, volume 42)

Abstract

The melt processing of YBa2Cu3O6+x (Y123) in a reduced oxygen partial pressure has been investigated. Due to the depression of the peritectic in reduced pO2 the maximum temperature of the process cycle was 955°C. The resulting microstructure is comparable to that obtained through melt processing in air. The lower process temperature allows the use of a 90Ag/10Pd alloy sheath to contain the peritectic liquid during the texturing process and to lend additional mechanical strength to textured Y123 wires.

Keywords

Critical Current Density Transverse Cross Section Filament Wire Peritectic Temperature Metallic Inclusion 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    P. McGinn, N. Zhu, W. Chen, M. Lanagan, and U. Balachandran, Zone Melt Texturing of YBa2Cu306+x With Silver Additions, Physica C 167:343 (1990).Google Scholar
  2. 2.
    S. Jin, R C. Sherwood, EM. Gyorgy, T.H. Tiefel, R. B. van Dover, S. Nakahara, L.F. Schneemeyer, RA. Fastnacht, and ME. Davis,Large magnetic hysteresis in a melt-textured Y-Ba-Cu-O superconductor, Appl Phys. Lett. 54: 584 (1989).CrossRefGoogle Scholar
  3. 3.
    K. Salama, X. Chaud, D.F. Lee, in “Proceedings of the Seventh US-Japan Workshop on High-Field Superconducting Materials, Wires and Conductors and Standard Procedures for HFSC Wire Testing” (1991).Google Scholar
  4. 4.
    T. Oka, Y. Itoh, Y. Yanagi, H. Tanaka, S Takashima, Y. Yamada and U. Mitzutani, Critical current density and mechanical strength of YBa2Cu3O7-δ superconducting composites containing Zr, Ag and Y2BaCuO5 dispersions by melt-processing, Physica C 200.55 (1992).CrossRefGoogle Scholar
  5. 5.
    M.J. Day, S.D. Sutton, F Wellhoffer and J.S. Abell, The microstructural and critical current properties of melt-processed YBCO + Ag thick films, Supercond. Sci. Techtiol. 6:96(1993)CrossRefGoogle Scholar
  6. 6.
    J. Zhou, C. Sorell, S. Dou, M. Apperley, Alignment of YBa2Cu3O7-δ and Ag — YBa2Cu3O7–8 Composites at -930C by Eutectic Formation,./ Am. Ceram. Soc. 74: 1541 (1991).CrossRefGoogle Scholar
  7. 7.
    T.B. Lindemer, FA. Washburn, CS MacDougall, R. Feenstra, and OB. Cavin, Decomposition of YBa2Cu3O7-δ and YBa2Cu4O8 for pO2 < 0. IMPa Physica C. 178. 93 (1991). CrossRefGoogle Scholar
  8. 8.
    N.L. Wu, H.H. Zern, C.L. Chen, Low Temperature Melt Growth of YBa2Cu307-x /Silver Composites in Partial Vacuum, Physica C 241: 198 (1994)CrossRefGoogle Scholar
  9. 9.
    J. McManus-Driscoll, J. Bravman, R. Beyers, Phase Equilibria in the Y-Ba-Cu-O System and Melt Processing og AgClad YBa2Cu3O7-x Tapes at Reduced Oxygen Partial Pressures, Physica C 241: 401 (1995)CrossRefGoogle Scholar
  10. 10.
    G. Krabbes, W. Bieger, U. Wiesner, K. Fischer, P. Schatzle, Univarient reactions in the YBCO system and the influence of oxygen on solidification and microstructure, J. Electr. Mater., 23:1135 (1994)CrossRefGoogle Scholar
  11. 11.
    G A Risch, M.T Lanagan, W Wu, K.C. Goretta, and B.M. Moon, YBa2Cu307_g processed with a silver / palladium alloy, Mat. Lett. 12 :291 (1991).CrossRefGoogle Scholar
  12. 12.
    K. Fischer, G. Leitner, G. Fuchs, M. Schubert, B. Schlobach, A. Gladun, and C. Rodig, Preparation and Critical Current Density of Melt-Processed Y-Ba-Cu-0 Thick Films and AgPd-Sheathed Tapes, Cryogenics 33: 97 (1993).CrossRefGoogle Scholar
  13. 13.
    R. Allem, F. Lavalle,, G. L’Espérance, R. Schulz, and ML. Trudeau, Interfacial reactions between YBa2Cu3O7-δ and Ag-Pd alloys during high temperature heat treatments,./ Mater. Res. 7:2936 (1992).CrossRefGoogle Scholar
  14. 14.
    DM. Kroeger, A. Goyal, Z.L. Wang, FA. List, and KB. Alexander, Substrate Reactions and Flux Pinning Structures in Melt-Processed YBa2Cu3O7-x Deposits On Ag-Pd Alloy Substrates, in “Proceedings of the 1992 TCSUH Workshop HTS Materials, Bulk Processing, Bulk Applications” World Scientific, Singapore, (1992), p 329.Google Scholar
  15. 15.
    Y A. Chang and K.C. Hsieh, “Phase Diagrams of Ternary Copper-Oxygen-Metal Systems” American Society for Metals, Metals Park, Ohio, USA, (1989).Google Scholar
  16. 16.
    MA. Black, P.J. McGinn, unpublishedGoogle Scholar

Copyright information

© Springer Science+Business Media New York 1996

Authors and Affiliations

  • M. A. Black
    • 1
  • P. J. McGinn
    • 1
  1. 1.Department of Chemical EngineeringUniversity of Notre DameUSA

Personalised recommendations