Oxygen Annealing of YBCO/Gold Thin-Film Contacts

  • Yizi Xu
  • J. W. Ekin
  • C. C. Clickner
  • R. L. Fiske
Part of the Advances in Cryogenic Engineering book series (ACRE, volume 44)

Abstract

The specific contact resistivity, defined as the product of the contact resistance and the contact area, of c-axis YBCO/Au thin-film contacts is measured as a function of oxygen annealing temperature to determine the optimum annealing conditions for this interface system. Square planar junctions with side widths of 2, 4, 8, and 16 μm were fabricated ex situ. Annealing was carried out at constant sample temperature for 10 minutes in atmospheric pressure of oxygen. The junction conductance characteristics were measured after each annealing and the process was repeated at progressively higher annealing temperatures, up to 650 °C. Before oxygen annealing, the junctions had contact resistivities of about 10−4 Ω•em2 or greater. The contact resistivity was unchanged for annealing temperatures below 300 °C. It decreased rapidly in an annealing temperature range from 300 °C to 450 °C. We found that 600 °C was a practical upper limit for annealing, at which temperature a contact resistivity in the 10−6 Ω•cm2 range may be achieved. We conclude that annealing-induced Au diffusion along grain-boundaries was responsible for the reduction in the contact resistivity.

Keywords

Contact Resistance High Temperature Superconductor Rapid Thermal Annealing Contact Resistivity YBCO Film 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Reference

  1. 1.
    J. W. Ekin, S. E. Russek, C. C. Clickner, and B. Jeanneret, In situ noble metal YBa2Cu3O7 thin-film contacts, Appl. Phys. Lett., 62: 369 (1993).ADSCrossRefGoogle Scholar
  2. 2.
    Z. H. Gong, J. K. Grepstad, and R. Fagerberg, The YBCO(001)/Ag Interface: Correlation Between Specific Contact Resistance and Interfacial Microstructure, IEEE Trans. Appl. Supercond. 5: 2412 (1995).CrossRefGoogle Scholar
  3. 3.
    J. W. Ekin, C. C. Clickner, S. E. Russek, and S. C. Sanders, Oxygen Annealing of Ex-Situ YBCO/Ag Thin-Film Interfaces, IEEE Trans. Appl. Supercond., 5: 2400 (1995).CrossRefGoogle Scholar
  4. 4.
    Simon S. Cohen and Gennady Sh. Gildenblat, “VLSI Electronics Microstructure Science 13, Metal-Semiconductor Contacts and Devices,” Academic Press, New York (1986).Google Scholar
  5. 5.
    B. D. Hunt, M. G. Forrester, J. Talvacchio, J. D. McCambridge, and R. M. Young, High-Ta superconductor/normal-metal/superconductor edge junctions and SQUID with integrated groundplanes, Appl. Phys. Lett. 68: 3805 (1996).ADSCrossRefGoogle Scholar
  6. 6.
    H. Terai, A. Fujimaki, Y. Takai, and H. Hayakawa, Electrical interface structure in YBa2Cu307_x/metal contacts, IEEE Trans. Appl. Supercond. 5: 2408 (1995).CrossRefGoogle Scholar
  7. 7.
    J.M.Valles, Jr., R.C. Dynes, A.M. Cucolo, M. Gurvitch, L.F. Schneemeyer, J.P. Garno, and J.V. Waszczak, Electron tunneling into single crystals of YBa2Cu3O7_8, Phys. Rev. B, 44: 11986 (1991).Google Scholar
  8. 8.
    S.C. Sanders, S.E. Russek, C.C. Clickner, and J.W. Ekin, Insulating boundary layer and magnetic scattering in YBa2Cu3O7_6/Ag interfaces over a contact resistivity range of 10–8 to l0 3 S2 cm2, Appl. Phys. Lett. 65: 2232 (1994).ADSCrossRefGoogle Scholar
  9. A.M. Cucolo and R. Di Leo, Zero-bias anomalies in high-To superconductor tunnel junctions, Phys. Rev. B, 47: 2916 (1993).ADSCrossRefGoogle Scholar
  10. 9.
    J. W. Ekin et al., High TT superconductor/noble-metal contacts with surface resistivities in the 1010 0cm2 range, Appl. Phys. Lett. 52: 1819 (1988).ADSCrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media New York 1998

Authors and Affiliations

  • Yizi Xu
    • 1
  • J. W. Ekin
    • 1
  • C. C. Clickner
    • 1
  • R. L. Fiske
    • 1
  1. 1.National Institute of Standards and TechnologyBoulderUSA

Personalised recommendations