High-Jc Reproducibility of Ag-Sheathed Bi-2212 Tapes

  • Yoshiaki Tanaka
  • Tomoyuki Yanagiya
  • Fumiaki Matsumoto
  • Hiroshi Maeda
Part of the An International Cryogenic Materials Conference Publication book series (ACRE, volume 40)

Abstract

In the fabrication of Ag-sheathed Bi-2212 superconducting tapes, J c reproducibility is obstructed by (1) swelling of the Ag sheath, (2) the rough interface of the sheath and core, (3) cracks in the oxide core, (4) inhomogeneities in composition, particle size, and particle hardness of the raw powder. The swelling is caused by the expansion of dissociated 02 gas within the weak, pure-Ag sheath during the high-temperature melting process; it can be eliminated by using powder calcined in low, partial O2 pressure. Complex, misoriented Bi-2212 layer structures often grow from rough interfaces, which are due to improper deformation processes. Cracks in the oxide core, easily introduced by mishandling, can be significantly reduced to achieve a mechanically stronger AgCu-alloy-sheathed tape. Improvement in high-J c reproducibility and the effects of Cu addition into the sheath on increasing J c and mechanical strength are presented.

Keywords

Rough Interface Cold Isostatic Pressing Oxide Core Tape Sample Partial Melting Process 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    T. Hasegawa, T. Kitamura, and H. Ogiwara, 1.5 Tesla Bi-family, oxide coil and its limits as a tool of demonstration of feasibility of superconducting oxide wire/tape, p. 3 in “Proceedings of the Fifth U.S.—Japan Workshop on High Tc Superconductors,” New Superconducting Materials Forum, The Society of Non-Traditional Technology, Tsukuba, Japan (1993).Google Scholar
  2. 2.
    S. Hayashi, K. Shibutani, T. Egi, I. Shigaki, R. Ogawa, Y. Kawate, and P. Lambert, Properties of Bi-2212 silver sheathed superconducting tape and its application to superconducting magnet, p. 49, ibid.Google Scholar
  3. 3.
    T. Maeda, M. Mimura, H. Kikuchi, K. Nemoto, T. Kinoshita, M. Yoshihara, N. Enomoto, N. Uno, and Y. Tanaka, Development high-Ta wires and bulks for practical applications, p. 59, ibid.Google Scholar
  4. 4.
    H. Kumakura, H. Kitaguchi, K. Togano, H. Maeda, J. Shimoyama, and K. Nomura, Properties of Bi-2212 tapes and coils fabricated applying dip-coating process, p. 7, ibid.Google Scholar
  5. 5.
    K. Ohkura, H. Mtikai, T. Hikata, M Ueyama, T. Kato, J. Fujikami, and K. Sato, High-T; (Bi,Pb)2Sr2Ca2Cu3O10 superconducting magnet operating using 20 K Gifford-McMahon-type refrigerator, to be published in Jap. J. Appl. Phys. 32 (1993).Google Scholar
  6. 6.
    Y. Tanaka, T. Alano, T. Yanagiya, M. Fukutomi, K. Komori, and H. Maeda, Fabrication and superconducting properties of AgCu alloy-sheathed BiSrCaCuCuO oxide tapes, Jap. J. Appl. Phys 31: L235 (1992).CrossRefGoogle Scholar
  7. 7.
    K. Osamura, M. Kamo, and J. Kajita, Influence of residual carbon on bubbling and critical current density in Ag/Bi2223 tapes, submitted to Supercond. Sci. Technol Google Scholar
  8. 8.
    Y. Feng, D.C. Larbalestier, S.E. Babcock, and J.B. Vander Sande, (001) faceting and Bi2Sr2CuO6+x (Tc=2–22K) phase formation at the Ag/Bi-Sr-Ca-Cu-O interface in Ag-clad Bi2Sr2CaCu2O8+x (Tc=75–95K) superconducting tapes, Appl. Phys. Lett 61 (10): 1234 (1992).Google Scholar

Copyright information

© Springer Science+Business Media New York 1994

Authors and Affiliations

  • Yoshiaki Tanaka
    • 1
  • Tomoyuki Yanagiya
    • 2
  • Fumiaki Matsumoto
    • 1
  • Hiroshi Maeda
    • 1
  1. 1.National Research Institute for MetalsTsukubaJapan
  2. 2.Sumitomo Heavy IndustriesHiratsukaJapan

Personalised recommendations