Properties of a Highly Crosslinked Elastomer

  • R. F. Landel

Summary

The properties of a highly crosslinked polyurethane elastomer, based on ricinoleic acid (castor oil) as the backbone, have been measured. The rubber, termed Galcit I, has been proposed as a standardized, highly birefringent, nearly elastic rubber for use in testing new apparatus on a material with known properties, and in checking or calibrating existing instruments. Various characterizations have been carried out and the results will be presented briefly. These include stress relaxation and dynamic shear modulus, uniaxial and uniform biaxial tests to failure, some additional biaxial tests in combined shear and tension, and swelling. in several liquids. The tensile modulus at 25°C is high, about 37 bar (535 psi). Mc ≈ 2300g/mole as determined from swelling and ultimate properties. This corresponds to 112 carbon atoms between crosslinks, which would be equivalent to Mc ≈ 1500 in a polybutadiene or 2000 in natural rubber. This is a high enough crosslink density to virtually eliminate the effects of chain entanglements on the time dependence of the modulus and to render the elastomer almost brittle. The stress/strain response is neo-Hookean, i.e. at 25°C and above the material appears to obey the classic, Gaussian-chain theory of rubberlike elasticity for strains up to rupture, though these are only of the order of 60%. At very small strains in biaxial tests, however, there appears to be a departure from the simple kinetic theory response.

Keywords

Mold Rubber Polyurethane Cyclohexane Diene 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    San Miguel, A., and Duran, E, Experimental Mechanics, 4 (3), 84. (1964).CrossRefGoogle Scholar
  2. 2.
    Duran, E., private communications.Google Scholar
  3. 3.
    Knauss, W. G., “A Cross-Linked Polymer Standard: Report on Polymer Selection,” Tech, Rpt. No, AFRPL-TR-65–111, Air Force Rocket Propulsion Lab., Edwards AFB (April 1965).Google Scholar
  4. 4.
    Kuhn, W., Grün, F., and Kallord, F., 101 248 (1942).Google Scholar
  5. 5.
    Treloar, L. R. G,, “The Physics of Rubber Elasticity,” 2nd Edition, Oxford University Press, London, 1958. Chapter 10.Google Scholar
  6. 6.
    Arenz, R. J., Ferguson, C, W., and Williams, M. L,, Experimental Mechanics, 7, 183 (1967).CrossRefGoogle Scholar
  7. 7.
    Smith, T. L., J. Polymer Sci. 20, 90 (1956).Google Scholar
  8. 8.
    Mueller, H, K., and Knauss, W. G., Trans. Soc. Rheol., 14, 000 (1970).Google Scholar
  9. 9.
    Landel, R, F., Froelich, D., and Tschoegl, N, W., Further work is in progress and will be reported subsequently.Google Scholar
  10. 10.
    Knauss, W. G., Clauser, J. F., and Landel, R. F., AFRPL-Tr-6621, Edwards, California, January 1966, MATSCIT PS 66–1, California Institute of Technology, Pasadena, California, January 1966.Google Scholar
  11. 11.
    Reference 5, Chapter 6.Google Scholar
  12. 12.
    Landel, R. F,, and Fedors, R. Fo, Proc, First Int. Conf. on Fracture, Sindai Japan, T. Yokobori, T. Kawasaki and J. L. Swedlow, Edr., I.C.F. Vol. II, 1965, P. 1247. Reprinted in Rubber Chem. and Tech., 40, 1044 (1967).Google Scholar
  13. 13.
    Smith, T. L. and Frederick, Jo E., J. Appl, Phys. 10, 2996 (1965).CrossRefGoogle Scholar
  14. 14.
    Fedora, R. Fs, and Landel, R. F,, Space Program Summary 37–45, Vol, IV, Jet Propulsion Laboratory, Pasadena, California, June 30, 1967, p. 92.Google Scholar
  15. 15.
    Mancke, R. G,, and Landel, R. F., to be submitted. Preliminary results may be found in AFRPL-TR-69–180, Edwards, California, August 1969, CHECIT PL 69–1, California Institute of Technology, Pasadena, California, August 1969.Google Scholar

Copyright information

© Springer Science+Business Media New York 1971

Authors and Affiliations

  • R. F. Landel
    • 1
  1. 1.Jet Propulsion LaboratoryCalifornia Institute of TechnologyPasadenaUSA

Personalised recommendations