Magnetic Properties of Compositionally-Modulated Thin Foils and Their Hydrides

  • N. K. Flevaris
  • D. Baral
  • J. E. Hilliard
Part of the NATO Advanced Study Institutes Series book series (NSSB, volume 76)

Abstract

Preliminary measurements have been made on the magnetic properties of compositionally-modulated ferromagnetic thin foils of Pd-Ni and Pd-Co, using ferromagnetic resonance and a torsion balance magnetometer. Qualitative studies have also been made of the effect of the introduction of hydrogen on the structure and magnetization of the foils. The addition of hydrogen changed the amplitude of modulation as well as the state of stress of the foils. The magnetization density and the magnetic anisotropy coefficient were also affected. In foils with and without the hydrogen we observed a peak below 50° K in the FMR linewidth versus temperature curves. When the modulation amplitude was reduced by annealing, a double resonance spectrum was observed. Measurements were also made of the ac susceptibility of a hydrogenated Pd-Ni foil in very low applied magnetic fields.

Keywords

Magnetic Anisotropy Double Resonance Torsion Balance Magnetization Density Flat Portion 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. E. Hilliard, A.I.P. Conf. Proc. 53, 507 (1979). T. Tsakalakos and J. E. Hilliard, (to be published). G. E. Henéin and J. E. Hilliard, (to be published).Google Scholar
  2. 2.
    B. Thaler, J. B. Ketterson and J. E. Hilliard, Phys. Rev. Letters 41, 336 (1978).CrossRefGoogle Scholar
  3. 3.
    V. A. Colttson et al., Phys. Chem. Mech. Materials 5, 597 (1969)Google Scholar
  4. 4.
    D. Sain and J. S. Kouvel, Phys. Rev. B 17, 2257 (1978). Also a private communication with J. S. Kouvel about recent unpublished data.Google Scholar
  5. 5.
    Considering the problem of interfaces in CMA, this makes Pd-Ni quite a bit more interesting than the Cu-Ni system where eight nearest neighbors of Ni atoms are necessary for the alloy to be ferromagnetic.Google Scholar
  6. 6.
    T. Tokunaga and H. Fujiwara, J. Phys. Soc. Japan 45, 1232 (1978)CrossRefGoogle Scholar
  7. 7.
    G. Fischer et al., J. Appl. Phys. 39, 545 (1968).CrossRefGoogle Scholar
  8. 8.
    J. H. Van Vleck, Phys. Rev. 52, 1178 (1937).CrossRefGoogle Scholar
  9. 9.
    J. Condon, Ph.D. Thesis, Northwestern University (unpublished ), 1963.Google Scholar
  10. 10.
    C. A. Neugebauer, Structure and Properties of Thin Films, p, 358, J. Wiley and Sons, Inc. New York (1959).Google Scholar
  11. 11.
    D. W. Carnegie and H. Clauss, J. Appl. Phys. 50, 1738 (1979).CrossRefGoogle Scholar
  12. 12.
    C. L. Foiles, Solid State Commun. 33, 125 (1980).CrossRefGoogle Scholar
  13. 13.
    J. R. MacDonald, Phys. Rev. 106, 890 (1957).CrossRefGoogle Scholar
  14. 14.
    C. J. Gadsden and M. Heath, J. Phys. F. 7, 1273 (1977).CrossRefGoogle Scholar
  15. 15.
    J. F. Dillon, Phys. Rev. 105, 759 (1957)CrossRefGoogle Scholar
  16. 16.
    See e.g. J. F. Dillon and J. W. Nielson, Phys. Rev. Letters 3, 30 (1959)Google Scholar
  17. E. C. Spencer, R. C. Le Craw and A. M. Glogston, Phys. Rev. Letters 3, 32 (1959).CrossRefGoogle Scholar
  18. 17.
    C. J. Gadsden and M. Heath, J. Phys. F. 8, 521 (1978).CrossRefGoogle Scholar
  19. 18.
    G. V. Skrotskii and L. V. Kurbatov, Sov. Phys. JETP 35, 148 (1959).Google Scholar
  20. 19.
    P. E. Tannenwald and M. H. Seavey, Phys. Rev. 105, 337 (1957).CrossRefGoogle Scholar
  21. 20.
    A. Van Itterbeek et al., J. Phys. Radium 21, 81 (1960).CrossRefGoogle Scholar
  22. 21.
    D. Chen and A. H. Morrish, J. Appl. Phys. Suppl. 33, 1146 (1962).CrossRefGoogle Scholar
  23. 22.
    C. A. Neugebauer, Z. Angew. Physik 14, 182 (1962)Google Scholar

Copyright information

© Springer Science+Business Media New York 1981

Authors and Affiliations

  • N. K. Flevaris
    • 1
  • D. Baral
    • 1
  • J. E. Hilliard
    • 1
  1. 1.Materials Research Center and Department of Materials Science and EngineeringNorthwestern UniversityEvanstonUSA

Personalised recommendations