Mapping Residual Plastic Strain in Materials Using Electron Backscatter Diffraction

  • Edward M. Lehockey
  • Yang-Pi Lin
  • Olev E. Lepik

Abstract

Residual strains that accrue from stresses imposed on materials during manufacturing, installation, and service often enhance the susceptibility to degenerative effects such as corrosion, cracking, and fatigue. Mapping strains in Alloy 600, a Ni-base non-age hardenable alloy, Steam Generator (SG) tubing used in boiler systems of CANadian Deuterium Uranium (CANDU) reactors is of particular interest to the nuclear industry. Interactions between residual strains from roller-expansion of the tubing during installation with prevailing environmental conditions during reactor operation (e.g., water chemistry and temperature) contribute to initiation and propagation of stress corrosion cracks (SCC), which can influence boiler reliability and service-life (Danko, 1996). Therefore, having a means of accurately characterizing the magnitude and spatial distribution of plastic deformation in relation to material defects including cracks, pits, and dents, is essential for identifying components at high risk of failure. Hardness measurements have traditionally been used to identify regions of high strain in SG tubes. However, obtaining a sufficient number of such measurements to infer details regarding the spatial distribution of complex strain fields is tedious and often impractical. Moreover, in so far as hardness indentations locally alter the strain distribution, these methods can be considered destructive.

Keywords

Plastic Zone Stress Corrosion Crack Angular Deviation Misorientation Distribution Face Centered Cubic 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Reference

  1. Adams, B.L., Wright, S.L, and Kunze, K., 1993, Orientation imaging: the emergence of a new microscopy, Met. Trans. 24A:819.Google Scholar
  2. ASTMa, 1996, Standard test methods for tension testing of metallic materials (metric), ASTM E 8, ASTM Annual Book of Standards, 3.01:55.Google Scholar
  3. ASTMb, 1996, Standard practice for making and using c-ring stress-corrosion test specimens, ASTM G 38 – 73, ASTM Annual Book of Standards, 3.02:132.Google Scholar
  4. ASTMC, 1996, Standard test method for microhardness of materials, ASTM E 384, ASTM Annual Book of Standards, 3.01:385.Google Scholar
  5. Berenson, M.L., 1983, Intermediate Statistical Methods and Applications, Prentice Hall Publishing, New Jersey.Google Scholar
  6. Buchanon, P. J., Rändle, V., and Flewitt P.E. J., 1997, A simple procedure for the assessment of plastic strain in electron back-scatter diffraction patterns, Scripta Metall. 37:1511.CrossRefGoogle Scholar
  7. Cameron, D.W., 1996, Fatigue properties in engineering materials, in: ASM Metals Handbook, S.R. Lampan, ed., American Society of Metals, Metals Park, Ohio.Google Scholar
  8. Danko, J.C., 1996, Corrosion in the nuclear power industry, in: Volume 13 ASM Metals Handbook, S.R. Lampan, ed., American Society of Metals, Metals Park, Ohio.Google Scholar
  9. Dingley, D.J., and Field, D.P., 1997, Electron backscatter diffraction and orientation imaging microscopy, Mat. Sei. Tech. 13:69.CrossRefGoogle Scholar
  10. Hirsch, P.B., Howie, A., Nicholson, R.B., Pashley, D.W., and Whelan, M.J., 1965, Electron Microscopy of Thin Crystals, Butterworths, London.Google Scholar
  11. Nye, J.F., 1953, Some geometrical relations in dislocated crystals, Acta Metall. 1:153.CrossRefGoogle Scholar
  12. Palumbo, G., King, P.J., Aust, K.T., Erb, U., and Lichtenberger, P.C., 1991, Grain boundary design and control for intergranular stress-corrosion resistance, Scripta Metall. 25:1775.CrossRefGoogle Scholar
  13. Quested, P.N., Henderson, P. J., and McLean, M., 1988, Observations of deformation and fracture heterogeneities in a nickel-base superalloy using electron backscatter diffraction, Acta Metall. 36:2743.CrossRefGoogle Scholar
  14. Reed-Hill, R., 1973, Physical Metallurgy Principals, PWS-Kent Publishing, Boston.Google Scholar
  15. Venables, J.A., and Harland, C.J., 1973, Electron back-scattering patterns — a new technique for obtaining crystallographic information in the scanning electron microscope, Phil Mag. 7:1193.CrossRefGoogle Scholar
  16. Wilkinson, A.J., and Dingley, D.J., 1991, Quantitative deformation studies using electron backscatter patterns, Acta Metall. 39:3047.CrossRefGoogle Scholar
  17. Wilkinson, A.J. and Dingley, D.J., 1992, The distribution of plastic deformation in a metal matrix composite caused by straining transverse to the fibre direction, Acta Metall. 40:3357.CrossRefGoogle Scholar
  18. Wright, S.L, 1993, A review of automated orientation imaging microscopy, J. Comp.Micro. 5:207.CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media New York 2000

Authors and Affiliations

  • Edward M. Lehockey
    • 1
  • Yang-Pi Lin
    • 1
  • Olev E. Lepik
    • 1
  1. 1.Ontario Power TechnologiesTorontoCanada

Personalised recommendations