The Microstructure and Properties of Crazes

Abstract

A brief résumé of the established characteristics of craze deformation and structure is given along with a summary of the significance of crazing in the bulk deformation and fracture of high polymers. This is followed by a more detailed consideration of recent work in two important areas of interest, viz (1) microstructure of crazes and (2) stress-strain response of crazes.

The microstructure of crazes has been studied using high-resolution transmission electron microscopy. The crazes were produced in bulk specimens, microtome thin sections, and solvent-cast thin films. The structure of crazes was similar in all specimens and consisted of highly drawn fibrils normal to the craze-matrix interface with linking, finer cross fibrils. In the thin films it was possible to obtain much larger craze strains and this resulted in a finer fibril structure. A model of the microstructure of a craze is presented.

The stress-strain characteristics of a craze have already been studied by Kambour and Kopp using a method which requires direct observation of the change in thickness of a thick craze during the application of a loading cycle. An alternative approach is described which is based on microstrain measurements of specimens containing a high density of very fine crazes. Quantitative microscopy is used to determine the craze density and average thickness. The results obtained on polystyrene are similar to Kambour and Kopp’s observations on solvent induced crazes in poly-carbonate. The results are discussed in the context of the observed craze microstructure.

Keywords

Glassy Polymer Stress Whitening Craze Growth Craze Formation Molded Polystyrene 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Rabinowitz, S., and Beardmore, P., Critical Reviews in Macromolecular Sciences, CRC Press, Cleveland (1972), Vol. 1., No. 1, p 1.Google Scholar
  2. 2.
    Klemperer, W. B., Theodore von Karman Anniversary Volume, Applied Mech., p. 328, Cal. Tech. (1941).Google Scholar
  3. 3.
    Sternstein, S. S., Ongchin, L., and Silverman, A., Applied Polymer Symposia, Interscience, New York (1968), No. 7, p 175.CrossRefGoogle Scholar
  4. 4.
    Bevis, M., and Hull, D., J. Mat. Sci., 5, 983 (1970).CrossRefGoogle Scholar
  5. 5.
    Sternstein, S. S., and Ongchin, L., ACS Polymer Preprints, 10, 1117 (1969).Google Scholar
  6. 6.
    Kambour, R. P., Applied Polymer Symposia, Interscience, New York (1968), No. 7, p 215.Google Scholar
  7. 7.
    Kambour, R. P., and Holik, A. S., J. Polymer Sci., Part A-2, 7, 1393 (1969).CrossRefGoogle Scholar
  8. 8.
    Beahan, P., Bevis, M., and Hull, D., Phil. Mag., 24, 1267 (1971).CrossRefGoogle Scholar
  9. 9.
    Kambour, R. P., and Russell, R. R., Polymer, 12, 237 (1971).CrossRefGoogle Scholar
  10. 10.
    Van den Boogaart, A., Conference Proceedings, Physical Basis of Yield and Fracture, Oxford University Press (1966), p 167.Google Scholar
  11. 11.
    Murray, J., and Hull, D., Polymer, 10, 451 (1969).CrossRefGoogle Scholar
  12. 12.
    Williams, D.R.G., Applied Polymer Symposia, John Wiley and Sons, Inc. (1971), No. 17, p. 25.Google Scholar
  13. 13.
    Harris, J. S., and Ward, I. M., J. Mat. Sci., 5, 533 (1970).CrossRefGoogle Scholar
  14. 14.
    Owen, T. W., unpublished work.Google Scholar
  15. 15.
    Vadimsky, R. G., Keith, H. D., and Padden, F. J., J. Polymer Sci., Part A-2, 7, 1367 (1969).Google Scholar
  16. 16.
    Woodward, A. E., and Morrow, D. R., J. Polymer Sci., Part A-2, 7, 1651 (1969).CrossRefGoogle Scholar
  17. 17.
    Gent, A. N., J. Mat. Sci., 5, 925 (1970).CrossRefGoogle Scholar
  18. 18.
    Knight, A. C., J. Polymer Sci., Part A, 3, 1845 (1965).Google Scholar
  19. 19.
    Marshall, G. P., Culver, L. E., Williams, J. G., Proc. Roy. Soc., Part A, 319, 165 (1970).Google Scholar
  20. 20.
    Camwell, L., unpublished work.Google Scholar
  21. 21.
    Bucknall, C. B., and Smith, R. R., Polymer, 6, 437 (1965).CrossRefGoogle Scholar
  22. 22.
    Kambour, R. P., Polymer, 5, 143 (1964).CrossRefGoogle Scholar
  23. 23.
    Kambour, R. P., and Holik, A. S., ACS Polymer Preprints, 10, 1182 (1969).Google Scholar
  24. 24.
    Beahan, P., Bevis, M., and Hull, D., unpublished work.Google Scholar
  25. 25.
    Peterlin, A., J. Mat. Sci., 6, 490 (1971).CrossRefGoogle Scholar
  26. 26.
    Bird, R., Rooney, J. G., and Mann, J., Polymer, 12, 742 (1971).CrossRefGoogle Scholar
  27. 27.
    Kambour, R. P., and Kopp, R. W., J. Polymer Sci., Part A-2, 7, 183 (1969).CrossRefGoogle Scholar
  28. 28.
    Hoare, J., and Hull, D., Phil. Mag., 26, 443 (1972).CrossRefGoogle Scholar
  29. 29.
    Kambour, R. P., Polymer Eng. and Sci., 8, 281 (1968).CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media New York 1973

Authors and Affiliations

  • D. Hull
    • 1
  1. 1.University of LiverpoolLiverpoolEngland

Personalised recommendations