Rapidly Solidified Superconducting Film on Metallic Wire

  • S. A. Akbar
  • M. L. Chretien
  • J. Huang

Abstract

For technological applications of high-Tc superconductors, it will be necessary to overcome the inherent problem of brittleness, to develop materials with high current carrying capacity, and to devise ways of joining superconductors with other materials. This article attempts to address these aspects by focusing on superconducting films coated on metallic wires by solidification from melt. The composite systems are expected to produce flexible wires with desirable properties. Results of some preliminary investigations are reported.

Keywords

Critical Current Density Superconducting Phase Metallic Wire Bulk Superconductor Superconducting Film 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Y. Enomoto, T. Marakami, M. Suzuki and K. Moriwaki, Jpn. J. Appl. Phys., 26, L1248 (1987).ADSCrossRefGoogle Scholar
  2. 2.
    R. E. Somekh et al., Nature, 326, 857 (1987).ADSCrossRefGoogle Scholar
  3. 3.
    Y. Yamada, N. Fukushima, S. Nakyama, H. Yoshino and S. Murase, Jpn. J. Appl. Phys., 26, L865 (1987).ADSCrossRefGoogle Scholar
  4. 4.
    O. Kohno, Y. Lkeno, N. Sadakata, S. Aoki, M. Sugimoto and N. Nakagawa, Jpn. J. Appl. Phys., 26., L1527 (1987).CrossRefGoogle Scholar
  5. 5.
    S. Jin, R. S. sherwood, T. H. Tiefel, R. B. van Dover and D. W. Johnson, Jr., Appl. Phys. Lett., 51, 203 (1987).ADSCrossRefGoogle Scholar
  6. 6.
    R. W. McCallum et al., Adv. Ceram. Mater., 2, 388 (1987).Google Scholar
  7. 7.
    Y. Tanaka, K. Yamada and T. Sano, Japan. J. Appl. Phys., 27, L799 (1987).CrossRefGoogle Scholar
  8. 8.
    T. Goto and M. Kada, Japan. J. Appl. Phys., 26, L1327 (1987).Google Scholar
  9. 9.
    M. B. Brodsky, MRS Meeting, Anaheim, CA (1987).Google Scholar
  10. 10.
    S. Jin, T. H. Tiefel, R. C. Sherwood, G. W. Kammlot and S. M. Zahurak, Appl. Phys. Lett., 11, 943 (1987).ADSCrossRefGoogle Scholar
  11. 11.
    N. Alford, W. J. Clegg, M. A. Harmer, J. D. Birchall, K. Kendall and D. H. Jones, Nature, 332, 58 (1988).ADSCrossRefGoogle Scholar
  12. 12.
    N. Sadakata, Y. Ikeno, M. Nakagawa, K. Gotoh and O. Kohno, MRS Proc., 99, 293 (1988).ADSCrossRefGoogle Scholar
  13. 13.
    M. Kawashima, M. Nagata, Y. Hosoda, S. Takano, N. Shibuta, H. Mukai and T. Hikata, Applied Superconductivity Conference, San Francisco, CA (1988).Google Scholar
  14. 14.
    D. Shi and K. C. Goretta, Materials Lett., (1989).Google Scholar
  15. 15.
    K. Heine, J. Tenbrink and M. Thoner, preprint (1989).Google Scholar
  16. 16.
    N. McN Alford, J. D. Birchall, T. W. Button, W. J. Clegg and K. Kendall, Annual Meeting of the Am. Ceram. Soc., Indianapolis (1989).Google Scholar
  17. 17.
    T. R. Dinger, T. K. Worthington, W. J. Gallagher and R. L. Sandstrom, Phys. Rev. Lett., 58, 2687 (1987).ADSCrossRefGoogle Scholar
  18. 18.
    Y. Kioke, T. Nakanomyo and T. Fukase, Japan. J. Appl. Phys., 27, L841, (1988).ADSCrossRefGoogle Scholar
  19. 19.
    T. Takena, H. Nada, A. Yoneda and K. Sakata, Jpn. J. Appl. Phys., 27, L1209 (1988).ADSCrossRefGoogle Scholar
  20. 20.
    J. W. Ekin, Adv. Ceram. Mater., 2, 586 (1987).Google Scholar
  21. 21.
    S. Jin et al., Appl. Phys. Lett., 51, 943 (1987).ADSCrossRefGoogle Scholar
  22. 22.
    R. S. Feigelson, D. Gazit, D. K. Fork and T. H. Geballe, Science, 240, 1624 (1988).CrossRefGoogle Scholar
  23. 23.
    S. A. Akbar, M. J. Botelho, M. S Wong and M. Alauddin, “A Systematic Study of Superconductivity in Bi-Pb-Sb-Sr-Ca-Cu-O System,” submitted to Physica C.Google Scholar
  24. 24.
    K. Oka, K. Nakane, M. Ito and M. Saito, Jpn. J. Appl. Phys., 27, L1065 (1988).ADSCrossRefGoogle Scholar
  25. 25.
    R. S. Roth, K. L. Davis and J. R. Dennis, Adv. Ceram. Mater., 2., 303 (1987).Google Scholar
  26. 26.
    S. Takekawa and N. lyi, Jpn J. Appl. Phys., 26, L851 (1987).ADSCrossRefGoogle Scholar
  27. 27.
    D. L. Kaiser, F. Holtzberg, M. F. Chisholm and T. K. Worthington, J. Cryst. Growth, 15, 593 (1987).ADSCrossRefGoogle Scholar
  28. 28.
    H. J. Scheel, Physica C, 153–155 44 (1988).ADSGoogle Scholar
  29. 29.
    D. Shi, M. Blank, M. Patel, D. G. Hinks and A. W. Mitchell, Physica C, 156, 822 (1988).ADSCrossRefGoogle Scholar
  30. 30.
    D. G. Hinks, L. Soderholm, D. W. Capone II, B. Dabrowski, A. W. Mitchell and D. Shi, Appl. Phys. Lett., 53, 423 (1988).ADSCrossRefGoogle Scholar
  31. 31.
    D. Shi, M. Tang, K. Vandervoort and H. Claus, Phys. Rev. B, in print.Google Scholar

Copyright information

© Springer Science+Business Media New York 1990

Authors and Affiliations

  • S. A. Akbar
    • 1
  • M. L. Chretien
    • 1
  • J. Huang
    • 1
  1. 1.Department of Materials Science and EngineeringThe Ohio State UniversityColumbusUSA

Personalised recommendations