Copper mosaic crystals for Laue lenses

  • P. Courtois
  • K. H. Andersen
  • P. Bastie
Chapter

Abstract

Large single crystals of copper with an uniform and very narrow mosaic spread between 25 seconds and 1 minute of arc are now available at I.L.L. This result is of great interest in the construction of a Laue lens for astrophysical applications for which such quality copper single crystals may be used. The X-ray diffraction properties of copper single crystals produced at I.L.L. were studied for x-ray energies ranging from 100 keV to 400 keV. Several monocrystalline plates with different thicknesses and mosaic distributions were then prepared from the as-grown crystals in order to measure their diffraction efficiency as a function of energy. As expected, the value of the peak reflectivity depends on the crystal thickness. Reflectivity measurements show the excellent properties of copper crystals for gamma-ray diffraction. A peak reflectivity of 24% was measured at 220 keV from a copper single crystal of 3.75 mm thickness having a mosaic spread of 1.5 minutes of arc. Some technical aspects on the preparation of copper single crystal plates are also discussed.

Keywords

Copper Crystal growth Mosaic crystal Lens X-ray diffraction Reflectivity 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Barrière, N. et al.: Experimental Astronomy 20, DOI:10.1007/s10686-006-9058-xGoogle Scholar
  2. 2.
    Courtois, P., Hamelin, B., Andersen, K.H.: Nuclear Instruments and Methods in Physics Research A529, 157–161 (2004)ADSGoogle Scholar
  3. 3.
    Pisa, A.: SPIE Proc. 5536, 39 (2004)CrossRefADSGoogle Scholar
  4. 4.
    Bastie, P., Hamelin, B., Courtois, P.: J.de Phys. IV France 10, 10–21 (2000)Google Scholar
  5. 5.
    Courtois, P.: ILL Annual Report, 100–101 (2002)Google Scholar
  6. 6.
    Schneider, J.R.: Nuclear Science Applications 1, 227–27 (1981)Google Scholar

Copyright information

© Springer 2006

Authors and Affiliations

  1. 1.Institut Laue LangevinGrenoble Cedex 9France
  2. 2.Laboratoire de Spectrométrie Physique de Grenoble, UMR 5588 du CNRSUniversité Joseph Fourier, GrenobleISaint Martin d’Hères cedexFrance

Personalised recommendations