Abstract
Recentely, Si3N4 has been used as cutting tools in several alloys machining. Such materials shows SiAlONs and β-Si3N4, that it has excellent thermomachanical properties. This work had as objetive to develop and to apply β-Si3N4 cutting tools in machining of gray cast iron, starting from a mixture composed by 78.30 wt % α-Si3N4, 1.00 wt % A12O3, 14.40 wt % A1N, 3.15 wt % CeO2 and 3.15 wt % Y2O3, that was pressed and sintered at 1900°C. After characterization, cutting tools showed, HV = 20.50 GPa, KIC = 6.45 MPa.m1/2, with 95 % β-Si3N4 phase. Then, it were submited to machining of gray cast iron using: 1a step - Vc=180, 240, 300 and 360 m/min, f = 0.12mm/rot and ap = 1.00 mm; and 2a step — Vc = 300m/min, f = 0.23, 0.33 and 0.40 mm/rot and ap = 1.00 mm. For 7500 m cutting length, results showed excellent performace.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
ASM. Speciality Handbook: Cast Irons. Estados Unidos: ASM International, 1996, p. 33–267.
Ezugwu, E. O.; Bonney, J.; Yamane, Y., (2003), Journal of materials processing and technology, Vol 134, 233–253.
Dawson, S., Würtenberg, J. M. von, (1993), Experiências Práticas com Ferro Fundido de Grafita Compactada Como Material para Componentes Automotivos, Anais do 26o Simpósio Internacional sobre Tecnologia Automotiva e Automação.
Würtemberg, J. M. von, (1994), The Diesel Engine: Lean, Clean and “Green”. SinterCast S.A, Switzerland.
Hick, H., Langmayr, F, (2000), Engine Tecnology International, Germany, p. 40–42.
Lanna, M. A., (2004), Otimização de custos de produção de ferramentas utilizando sinterização normal. Anais do 48o Congresso Brasileiro de Cerâmicas.
Georgiou, G., Machining Solutions for Compacted Graphite Iron. Disponível em: <htpp://www.machineshopguide.com> Acesso em: 30/01/2002.
Reuter, U.; et al., (2000), The Wear Process of CGI Cutting Machining Developments. Anais do Compacted Graphite Iron — Machining Workshop (Darmstadt).
Devezas, T., (1985), Cerâmicos especiais estruturais: 2o Parte: cerâmicos covalentes, ITA Engenharia, vol 6/4.
Gonzaga, R. “Injluência da substituição da SiO 2 por A1 2 O 3 e AIN na mistura de aditivos Y 2 O 3 /SiO2 e CTR2O3/SiO2 na microestrutura e propriedades mecânicas de cerâmicas a base de Si 3N4” Mestrado em Engenharia de Materiais, Departamento de Engenharia de Materiais (DEMAR)/Faculdade de Engenharia Química de Lorena (Faenquil), 1998, 62 p.
Baud, S., Thévenot, F., (2001), Materials Chemistry and Physics, Vol. 67/1–3, 165.
DUTTA, S., (1982), Journal of the American Ceramic Society, Vol. 68/5, 2.
Shin, I.H., Kim, D.J., (2001), Materials Letters, Vol. 47, 329–333.
Silva, O.M.M. “Processamento e caracterização do nitreto de silício aditivado com carbonato de ítrio e concentrado de terras raras”, Tese de Doutorado, Faculdade de Engenharia de Guaratinguetá (FEG/UNESP), 2000, 169 p.
ASTM: C1327-99, “Standard test method for vickers indentation hardness of advanced ceramics”, 1999, 1–8.
ASTM: C-1421-99, “Standard test method for determination of fracture toughness of advanced ceramics at ambient temperature”, 1999, 1–32.
TECHNICAL ARTICLES, Mechanical Properties of Compacted Graphite Iron. Disponível em: http://www.castingsource.com/tech_art_grapnite.asp. Acesso em: 29/08/2000
Santos, C, Strecker, K., Ribeiro S., (2000), Sinterização e propriedades mecânicas do nitreto de silício (Si3N4) aditivado com misturas de Al2O3/Y2O3 ou Al2O3/CTR2O3, Anais do 14o Congresso Brasileiro de Ciência e Engenharia de Materiais (14o-CBECIMAT). 2702–2712.
Silva, V.A “Fabricação de ferramentas de corte cerâmico à base de Si 3N4 dopadas com adição de Y2O3, A12O3 e CTR2O3, com modificação superficial dos sinterizados por aplicação de diamante-CVD.” Tese de doutorado, Instituto Técnico Aeroespacial (ITA), 1998, 166 p.
Santos, C, Baldacim, S. A., Silva, O. M. M., Silva, C. R. M., (2004), Materials Science Engineering A, Vol. 367/1–2, 312–316.
Lanna, M. A., Bello, A. A.AL., Souza, J. V. C, (2004), Avaliação das Tensões e Deformações em Ferramentas Cerâmicas de Nitreto de Silício, Anais do 48o Congresso Brasileiro de Cerâmica.
Vilella, R. C. “Metodologia prática visando à otimização das condições de usinagem em células de fabricação” Dissertção de Mestrado em Engenharia Mecânica, Universidade Estadual de Campinas (UNICAMP), 1998, 105 p.
Cunha, E.A., Ribeiro, M.V., (2004), Revista Máquinas e Metais, Vol. 40/457, 132–138.
Brandt, G., (1986), Wear, Vol. 112, 39–56.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2005 CISM, Udine
About this paper
Cite this paper
Souza, J.V.C., Kelly, C.A., Moreira, M.R.V., Ribeiro, M.V., Lanna, M.A., Silva, O.M.M. (2005). β-SI3N4 Cutting Tools Obtaining for Machining of the Gray Cast Iron. In: Kuljanic, E. (eds) AMST’05 Advanced Manufacturing Systems and Technology. CISM International Centre for Mechanical Sciences, vol 486. Springer, Vienna. https://doi.org/10.1007/3-211-38053-1_55
Download citation
DOI: https://doi.org/10.1007/3-211-38053-1_55
Publisher Name: Springer, Vienna
Print ISBN: 978-3-211-26537-6
Online ISBN: 978-3-211-38053-6
eBook Packages: EngineeringEngineering (R0)