Ductile Mode Cutting of Tungsten Carbide

  • Kiu LiuEmail author
  • Hao Wang
  • Xinquan Zhang
Chapter
Part of the Springer Series in Advanced Manufacturing book series (SSAM)

Abstract

Cutting experiments are carried out to evaluate the cutting performance of tungsten carbide under nanometer scale chip thickness using a 5-axis CNC machining centre with CBN tools. The cutting forces are measured using a three-component dynamometer. Machined workpiece surface topography, chip formation, and tool wear are examined using an OMIS and SEM. Tool flank wear VBmax is also measured using the OMIS. Surface roughness is measured using a stylus profiler. Experimental results indicate that radial force Fx is much larger than tangential force Fz and axial force Fy. Under different cutting conditions, three types of surfaces of machined workpiece are achieved: ductile mode cutting surface, semi fractured surface and fractured surface. Continuous chips and discontinuous chips are formed under different cutting conditions. Surface roughness increases monotonically when the depth of cut and feed rate being increased. Tool wear occurs mainly on the flank face in ductile mode cutting of tungsten carbide and tool wear mechanisms are dominated by abrasion, adhesion and diffusion wear. SEM observations on machined workpiece surfaces and chip formation indicate that ductile mode cutting is mainly determined by undeformed chip thickness when the tool cutting edge radius is fixed. Ductile mode cutting of tungsten carbide is achieved when undeformed chip thickness is less than a critical value.

References

  1. 1.
    Liu K (2002) Ductile cutting for rapid prototyping of tungsten carbide tools. NUS Ph.D. thesis, SingaporeGoogle Scholar
  2. 2.
    Jenkins I, Wood J (1991) Cemented carbide powders and processing, powder metallurgy: an overview. Institute of Metals, London, pp 312–330Google Scholar
  3. 3.
    Mohan K (1996) Microstructure of consolidated nanocomposite tungsten carbide – cobalt. University of Connecticut, Ph.D. thesis, USAGoogle Scholar
  4. 4.
    Exner HE (1979) Physical and chemical nature of cemented carbide. Int Met Rev 24:149–174CrossRefGoogle Scholar
  5. 5.
    Chermant JL, Osterstock F (1976) Fracture toughness and fracture of WC-Co composites. J Mater Sci 11:1936–1951CrossRefGoogle Scholar
  6. 6.
    Schubert WD, Neumeister H, Kinger G et al (1998) Hardness to toughness relationship of fine-grained WC-Co hardmetals. Int J Refract Met Hard Mater 16:133–142CrossRefGoogle Scholar
  7. 7.
    Takahashi T, Freise EJ (1965) Determination of the slip systems in single crystals of tungsten monocarbide. Philos Mag 12:1–8CrossRefGoogle Scholar
  8. 8.
    Korner A, Karnthaler HP (1983) Eeak-beam study of glide dislocation in h.c.p. cobalt. Philos Mag A 48:469–477CrossRefGoogle Scholar
  9. 9.
    Vaidya S, Mahajan S (1980) Accommodation and formation of {\(11\bar{2}1\)} twins in Co single crystals. Acta Metall 28:1123–1131Google Scholar
  10. 10.
    Johnston TL, Davies RG, Stoloff NS (1965) Slip character and the ductile to brittle transition of single-phase solids. Philos Mag 12:305–317CrossRefGoogle Scholar
  11. 11.
    Greenwood RM, Loretto MH, Smallman RE (1982) The defect structure of tungsten carbide in deformed tungsten carbide-cobalt composites. Acta Metall 30:1193–1196CrossRefGoogle Scholar
  12. 12.
    Mehan RL, Hejna CI, McConnell MD (1985) Dry sliding wear of hard materials against a diamond composite. J Mater Sci 20:1222–1236CrossRefGoogle Scholar
  13. 13.
    Jia K, Fischer TE (1997) Sliding wear of conventional and nanostructured cemented carbides. Wear 203–204:310–318CrossRefGoogle Scholar
  14. 14.
    Rowcliffe DJ, Jayaram V, Hibbs MK et al (1988) Compressive deformation and fracture in WC materials. Mater Sci Eng A 105(106):299–303CrossRefGoogle Scholar
  15. 15.
    Engqvist H, Ederyd S, Axen N et al (1999) Grooving wear of single-crystal tungsten carbide. Wear 230:165–174CrossRefGoogle Scholar
  16. 16.
    Shetty DK, Wright IG, Mincer PN et al (1985) Indentation fracture of WC-Co cermets. J Mater Sci 20:1873–1882CrossRefGoogle Scholar
  17. 17.
    Schmid HG (1987) The mechanisms of fracture of WC-11 wt%Co between 20 °C and 1000 °C. Mater Forum 10:184–197Google Scholar
  18. 18.
    Fischmeister HF, Schmauder S, Sigl LS (1988) Finite element modelling of crack propagation in WC-Co hart metals. Mater Sci Eng A 105(106):305–311CrossRefGoogle Scholar
  19. 19.
    James MN, Human AM, Luyckx S (1990) Fracture toughness testing of hardmetals using compression-compression precracking. J Mater Sci 25:4810–4814CrossRefGoogle Scholar
  20. 20.
    Han D, Mecholsky JJ Jr (1990) Fracture analysis of cobalt-bonded tungsten carbide composites. J Mater Sci 25:4949–4956CrossRefGoogle Scholar
  21. 21.
    Liu K, Li XP, Liang YS (2004) Nanometer-scale ductile cutting of tungsten carbide. J Manuf Process 6:187–195CrossRefGoogle Scholar
  22. 22.
    Liu K, Li XP, Liang SY (2007) The mechanism of ductile chip formation in cutting of brittle materials. Int J Adv Manuf Technol 33:875–884CrossRefGoogle Scholar
  23. 23.
    Liu K, Li XP, Rahman M et al (2003) CBN tool wear in ductile cutting of tungsten carbide. Wear 255:1344–1351CrossRefGoogle Scholar
  24. 24.
    Liu K, Li XP, Rahman M (2003) Characteristics of high speed micro cutting of tungsten carbide. J Mater Process Technol 140:352–357CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2020

Authors and Affiliations

  1. 1.Singapore Institute of Manufacturing TechnologySingaporeSingapore
  2. 2.Department of Mechanical EngineeringNational University of SingaporeSingaporeSingapore
  3. 3.School of Mechanical EngineeringShanghai Jiao Tong UniversityShanghaiChina

Personalised recommendations