Preparation of Al2O3 Ceramic Cores by Dry-Pressing Assisted of Precursor-Derived Ceramic Technology

  • Zhigang Yang
  • Zhijia Zhao
  • Qian Li
  • Jianbo YuEmail author
  • Zhongming Ren
  • Zhi Wang
  • Shuxia Ren
Conference paper
Part of the Springer Proceedings in Physics book series (SPPHY, volume 216)

Abstract

Porous Al2O3 ceramic cores were prepared successfully by dry-pressing assisted of precursor-derived ceramic technology. Among, Al2O3 powders with flake shape were used as the matrix and silicone resin powders were used as the precursor. The effects of sintering temperatures on the properties of Al2O3 ceramic cores were researched. Results showed that the silicone resin powders had well-cohesive property, making the Al2O3 grains bond closely under pressure. During the sintering, the pyrolysis of silicone resin happened and the amorphous silica formed firstly at low temperature. The increasing temperatures made the amorphous silica gradually crystallize. And when the temperature was more than 1500 °C, the silica reacted with Al2O3 to form the mullite phases. With the increase of temperature, the shrinkage rate reached the maximum value of 0.95%, and the bulk density reached the maximum value of 2.53 g cm−3, and the porosity reached the minimum value of 33.11%, and the bending strength had the highest value of 105 MPa at 1500 °C.

Notes

Acknowledgements

We would like to acknowledge the financial support provided by United Innovation Program of Shanghai Commercial Aircraft Engine (AR910), the National Natural Science Foundation of China (Nos. U1560202, 51690162), the Natural Science Foundation of Hebei Province (Grant No. A2018210123), Open Project of State Key Laboratory of Advanced Special Steel, Shanghai University (SKLASS 2017-03).

References

  1. 1.
    J.J. Liang, Q.H. Lin, X. Zhang, T. Jin, Y.Z. Zhou, X.F. Sun, B.G. Choi, I.S. Kim, J.H. Do, C.Y. Jo, Effects of alumina on cristobalite crystallization and properties of silica-based ceramic cores. J. Mater. Sci. Technol. 33, 204–209 (2017)CrossRefGoogle Scholar
  2. 2.
    W.G. Jiang, K.W. Li, J.H. Xiao, L.H. Lou, Effect of silica fiber on the mechanical and chemical behavior of alumina-based ceramic core material. J. Asian Ceram. Soc. 5, 410–417 (2017)CrossRefGoogle Scholar
  3. 3.
    A. Kazemi, M.A. Faghihi-Sani, H.R. Alizadeh, Investigation on cristobalite crystallization in silica-based ceramic cores for investment casting. J. Eur. Ceram. Soc. 33, 3397–3402 (2013)CrossRefGoogle Scholar
  4. 4.
    G.H. Gu, L.M. Cao, Development of ceramic cores for investment casting hollow blades. Found. Technol. 23, 81–83 (2002)Google Scholar
  5. 5.
    A. Hamimah, Y. Dzul Hafez, Effect of thermal treatment on properties and micro-structure of porous alumina. Solid State Sci. Technol. 18, 155–163 (2010)Google Scholar
  6. 6.
    Y. Yang, S.Z. Shimai, Y. Sun, M.J. Dong, H. Kamiya, S.W. Wang, Fabrication of porous Al2O3 ceramics by rapid gelation and mechanical foaming. J. Mater. Res. 28, 2012–2016 (2013)CrossRefGoogle Scholar
  7. 7.
    J.B. Yu, Z.G. Yang, C.J. Li, K. Deng, Z.M. Ren, Investigation on properties of the silica ceramic cores for the hollow blades prepared by the conversion of the silicon resin. Key Eng. Mater. 680, 267–271 (2016)CrossRefGoogle Scholar
  8. 8.
    Z.G. Yang, J.B. Yu, C.J. Li, W.D. Xuan, Z.Q. Zhang, K. Deng, Z.M. Ren, Preparing porous Si-based ceramic core using thermosetting silicon resin injection method. J. Inorg. Mater. 30(2), 147–152 (2015)Google Scholar
  9. 9.
    Z.G. Yang, J.B. Yu, Z.M. Ren, C.J. Li, K. Deng, Fabrication and characterization of porous alumina-based ceramics using silicone resin as binder. Trans. Indian Ceram. Soc. 75, 40–46 (2016)CrossRefGoogle Scholar
  10. 10.
    Z.G. Yang, J.B. Yu, C.J. Li, K. Deng, Z.M. Ren, Effect of silicone resin on the properties of silica ceramic cores by heating treatment. J. Adhes. Sci. Technol. 30(24), 2667–2677 (2016)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • Zhigang Yang
    • 1
    • 2
  • Zhijia Zhao
    • 1
  • Qian Li
    • 2
  • Jianbo Yu
    • 2
    Email author
  • Zhongming Ren
    • 2
  • Zhi Wang
    • 1
  • Shuxia Ren
    • 1
  1. 1.Hebei Provincial Key Laboratory of Traffic Engineering Materials, School of Materials Science and EngineeringShijiazhuang Tiedao UniversityShijiazhuangChina
  2. 2.State Key Laboratory of Advanced Special Steels, School of Materials Science and EngineeringShanghai UniversityShanghaiChina

Personalised recommendations