Microstructure and Performance of WAAM TiB2-Reinforced Al–Si-Based Composites

  • Yaqi DengEmail author
  • Xianfeng Li
  • Liang Wu
  • Qingfeng Yang
  • Yanchi Chen
Conference paper
Part of the Springer Proceedings in Physics book series (SPPHY, volume 217)

Abstract

In this paper, the TiB2-reinforced Al–7Si–Cu–Mg composites manufactured by casting and arc addition were studied. TiB2 particles were nano-sized or submicron-sized and their morphologies were regular and round, thus they improved the mechanical properties of aluminum-based composite. Two different processes were compared in the microstructure and properties of aluminum-based composite. Through the contrast of SEM and EDS analysis, it was found that the distribution of alloying elements in the wire arc additive manufacturing (WAAM) TiB2-reinforced Al–Si-based composites was more dispersed, which reinforced the solid solubility. The size of TiB2 particles decreased and the distribution was more uniform. The hardness increased to 86.2HV10 as compared with as-cast state. The silicon phase of the as-cast sample was large and distributed continuously along the grain boundary, while the silicon phase in the as-deposited microstructure was dispersed and its size reduced to 2 µm. The heat treatment of WAAM Al–Si composites was carried out, and two sets of heat treatment mechanisms, aging and solution post-aging, were compared. The hardness of the material rose to 127HV10 after single aging, and it was improved to 139HV10 under solid solution post-aging condition. The reinforced Al–Si-based composites were found to achieve a supersaturated solution state through WAAM.

Keywords

Wire arc additive manufacturing Al-based composite TiB2 

References

  1. 1.
    S. Herranz, F.J. Campa, L.N.L. de Lacalle et al., The milling of airframe components with low rigidity: a general approach to avoid static and dynamic problems. Proc. Inst. Mech. Eng. Part B J. Eng. Manuf. 219(11), 789–801 (2005)CrossRefGoogle Scholar
  2. 2.
    J, Xiong, Forming Characteristics in Multi-layer Single-Bead GMA Additive Manufacturing and Acurate Control for Deposition Dimension (Harbin Institute of Technology, Harbin, 2014)Google Scholar
  3. 3.
    W.L. Liu, Rapid prototyping technology of Al-alloy parts by AC-TIG (Tianjin University, Tianjin, 2007)Google Scholar
  4. 4.
    J.H. Ouyang, H. Wang, R. Kovacevic et al., Rapid prototyping of 5356-aluminum aloy based on variable polarity gas tungsten arc welding process control and microstructure. Mater. Manuf. Process. 17(1), 103–124 (2002)CrossRefGoogle Scholar
  5. 5.
    J. Bo, J. Wang, J. Shi et al., Microstructure and mechanical properties of 4043 aluminum alloy thin wall parts manufactured by TIG WAAM. Welding 10, 23–26 (2015)Google Scholar
  6. 6.
    B. Cong, J. Ding, S. Williams, The influence of wire properties on the quality and performance of wire+arc additive manufactured aluminium parts. Adv. Manuf. Technol. 76, 1593–1606 (2015)CrossRefGoogle Scholar
  7. 7.
    J. Gu, J. Ding, S.W. Williams, H. Gu, J. Bai, Y. Zhai, P. Ma, The strengthening effect of inter-layer cold working and post-deposition heat treatment on the additively manufactured Al–6.3Cu alloy. Mater. Sci. Eng., A 651, 18–26 (2016)CrossRefGoogle Scholar
  8. 8.
    J.L. Gu, J.L. Ding, B.Q. Cong et al., The influence of wire properties on the quality and performance of wire+arc additive manufactured aluminium parts. Adv. Mater. Res. 1081, 210–214 (2014)CrossRefGoogle Scholar
  9. 9.
    C. Huang, S. Huang, F. Liu, Additive manufacturing technology of Metal material. 2, 37 (2016)Google Scholar
  10. 10.
    Y.M. Zhang, Y. Chen, P. Li, Weld deposition-based rapid prototyping: a preliminary study. J. Mater. Process. Technol. 135, 347–357 (2003)CrossRefGoogle Scholar
  11. 11.
    H.J. Wang, W.H. Jiang, J.H. Ouyang et al., Rapid prototyping of 4043 Al-alloy parts by VP-GTAW. J. Mater. Process. Technol. 148, 93–102 (2004)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • Yaqi Deng
    • 1
    Email author
  • Xianfeng Li
    • 1
  • Liang Wu
    • 1
  • Qingfeng Yang
    • 1
  • Yanchi Chen
    • 1
  1. 1.Shanghai JiaoTong UniversityShanghaiChina

Personalised recommendations