Microstructure and Properties of Rare-Earth B4C–Copper Composites

  • Yan LiEmail author
  • Meihui Song
  • Yu Zhang
  • Yanchun Li
  • Xiaochen Zhang
Conference paper
Part of the Springer Proceedings in Physics book series (SPPHY, volume 217)

Abstract

The B4C/Cu composites were prepared by powder metallurgy. Scanning electron microscopy, transmission electron microscopy, hardness tester, conductivity meter, and other analytical tests were used to study the effects of alloying elements and rare-earth modification processes on the microstructure and properties of composites. The results showed that the B4C/Cu composites prepared by powder metallurgy were densely packed, and the Y2O3 modified layer was uniformly coated on the surface of B4C particles. The modified B4C particles had a good interface with Cu and no interfacial reaction occurred. The addition of low melting point alloying element Bi could improve the hardness and electrical conductivity of B4C/Cu composites, but had little effect on the thermal conductivity. Surface modification of B4C with rare-earth salt could effectively increase the bonding ability between B4C particles and Cu, and endowed B4C/Cu composite materials with excellent physical and mechanical properties. For the composite with 2 wt% B4C particles, 2 wt% Bi particles, and 96 wt% copper powder, B4C/Cu composites had good mechanical and physical properties, of which the hardness was 179 HB; the density was 99.6%; the electrical conductivity was 66 %IACS; and the thermal conductivity could reach 262 W/m °C. These properties meet the requirements of electrical contact materials.

Keywords

Power metallurgy Modification Rare-earth salt Electric contact materials 

References

  1. 1.
    H.-R. Zhao, W. Luo, Y.-Z. Xie et al., Study advance of contact material in 2015. Electr. Eng. Mater. 1, 24–28 (2016)Google Scholar
  2. 2.
    R. Jamaati, M.R. Toroghinejad, Application of ARB process for manufacturing high-strength, finely dispersed and highly uniform Cu/Al2O3 composite. Mater. Sci. Eng. A 527(27), 7430–7435 (2010)CrossRefGoogle Scholar
  3. 3.
    Y. Jiang, M.-G. Yang, Z.-C. Yang et al., Research status of copper-based electrical contact materials for medium and high voltage apparatus. Electr. Eng. Mater. 4, 27–30, 35 (2013)Google Scholar
  4. 4.
    S.G. Savio, K. Ramanjaneyulu, V. Madhu, T. Balakrishna Bhat, An experimental study on ballistic performance of boron carbide tiles. Int. J. Impact Eng. 38, 535–541 (2011)CrossRefGoogle Scholar
  5. 5.
    K. Rajkumar, K. Kundu, S. Aravindan et al., Accelerated wear testing for evaluating the life characteristics of copper-graphite tribological composite. Mater. Des. 32, 3029–3035 (2011)CrossRefGoogle Scholar
  6. 6.
    J. Zhang, L. He, Y. Zhou, Highly conductive and strengthened copper matrix composite reinforced by Zr2Al3C4 particulates. Scripta Mater. 60, 976–979 (2009)CrossRefGoogle Scholar
  7. 7.
    X. Tang, Hot Deformation Behavior and Hot Extrusion Process of ZnSnO3/Cu Electrical Contact Materials (Harbin Institute of Technology, 2015)Google Scholar
  8. 8.
    Z.Y. Xiao, M.Y. Ke, L. Fang et al., Die wall lubricated warm compacting and sintering behaviors of pre-mixed Fe–Ni–Cu–Mo–C powders. J. Mater. Process. Technol. 209, 4527–4530 (2009)CrossRefGoogle Scholar
  9. 9.
    G.-L. Li, X.-C. Jiang, M. Wen et al., Studies of B4C particles reinforced copper matrix composite. J. Mater. Eng. 8, 32–35 (2001)Google Scholar
  10. 10.
    J.-P. Li, S.-H. Meng, J.-C. Han, Structure and flaws of CuCr alloys by explosive compaction. J. Harbin Inst. Technol. 12(2), 135–138 (2005)Google Scholar
  11. 11.
    S.J. Sun, S. Sakai, H.G. Suzuki, TEM observation of Cr fibers in Cu–15Cr–0.5Fe in situ composites. Mater. Trans. 41(5), 613–616 (2000)CrossRefGoogle Scholar
  12. 12.
    Z. Mu, H.-R. Geng, M.-M. Li et al., Effects of Y2O3 on the property of copper based contact materials. Compos. B 52, 51–55 (2013)CrossRefGoogle Scholar
  13. 13.
    C.J. Tu, D. Chen, Z.H. Chen, Improving the tribological behavior of graphite/Cu matrix self-lubricating composite contact strip by electroplating Zn on graphite. Tribol. Lett. 31, 91–98 (2008)CrossRefGoogle Scholar
  14. 14.
    Y. Li, M. Song, Y. Zhang et al., Influence of the ball mill process on titanium alloy powder particle size. Chem. Eng. 06, 13–15, 53 (2017)Google Scholar
  15. 15.
    Y. Li, M. Song, Q. Yu, X. Zhang, Improvement of anti-hydrolytic property of AlN powder modified by the rare-earth salts. Mater. Sci. Forum 816, 9–14 (2015)CrossRefGoogle Scholar
  16. 16.
    M.K. Habibi, A.S. Hamouda, M. Gupta, Hybridizing boron carbide particles with aluminum to enhance the mechanical response of magnesium based nano-composites. J. Alloy. Compd. 550, 83–93 (2013)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • Yan Li
    • 1
    Email author
  • Meihui Song
    • 1
  • Yu Zhang
    • 1
  • Yanchun Li
    • 1
  • Xiaochen Zhang
    • 1
  1. 1.Institute of Advanced Technology, Heilongjiang Academy of SciencesHarbinChina

Personalised recommendations