Influence of Metakaolin and Red Mud Blended Cement on Reinforcement Corrosion in Presence of Chloride and Sulfate Ions

  • Sondi SudheerEmail author
  • Uppara Raghu Babu
  • B. Kondraivendhan
Conference paper
Part of the Lecture Notes in Civil Engineering book series (LNCE, volume 25)

Abstract

This paper investigates the impact of partial replacement of Ordinary Portland Cement (OPC) with Metakaolin (MK) and Red Mud (RM) on reinforcement corrosion in presence of both chloride and sulfate ions. To achieve this objective, 36 slab specimens of size 300 × 300 × 52 mm were cast. First set of slabs had been cast with water to binder ratio 0.48, with the replacement of OPC by 5% of RM and 10% of MK one after the other. Similarly, the second set of slabs cast with water to binder ratio 0.51. Each set was admixed with 5% NaCl, 2% MgSO4, 5% NaCl + 2% MgSO4 by using weight of water. The corrosion behavior of reinforcing bars was monitored through half-cell potentials based on ASTM C876. To make sure the compressive strength of slabs, concrete cubes were tested. The numerous results, which indicate the effects of MK, RM, w/b ratios and concomitant presence of chloride and sulfate ions on reinforcement corrosion have been provided and compared the same. At higher w/b ratios (0.51), it was observed that the specimens with RM had lowest corrosion potentials as compared to OPC specimens and MK in the presence of chloride ions. Further in the presence of combined chloride and sulfate ions, corrosion potentials of MK and RM are less in comparison to the OPC concrete at higher water to binder ratios.

Keywords

Red mud Metakaolin Corrosion Chloride ions Sulfate ions 

References

  1. 1.
    Pradhan, B. (2014). Corrosion behavior of steel reinforcement in concrete exposed to composite chloride-sulfate environment. Construction and Building Materials, 72, 398–410.CrossRefGoogle Scholar
  2. 2.
    Santhanam, M., Cohen, M., & Olek, J. (2006). Differentiating seawater and groundwater sulfate attack in Portland cement mortars. Cement and Concrete Research, 36(12), 2132–2137.CrossRefGoogle Scholar
  3. 3.
    Maslehuddin, M., Rasheeduzzafar, R., Al-Amoudi, O. S. B., & Al-Mana, A. I. (1995). Concrete durability in a very aggressive environment. American Concrete Institute, SP, 92(3), 191–211.Google Scholar
  4. 4.
    Issn, O. (2018). The role of metakaolin in the protection of concrete against the deleterious action of chlorides. Revista IBRACON de Estruturas e Materiais, pp. 1–27.Google Scholar
  5. 5.
    Kim, H. S., Lee, S. H., & Moon, H. Y. (2007). Strength properties and durability aspects of high strength concrete using Korean metakaolin. Construction and Building Materials, 21(6), 1229–1237.CrossRefGoogle Scholar
  6. 6.
    udovít Krajči, L., Mojumdar, S. C., Janotka, I., Puertas, F., Palacios, M., & Kuliffayová, M. (2015). Performance of composites with metakaolin-blended cements. Journal of Thermal Analysis and Calorimetry, 119(2), 851–863.CrossRefGoogle Scholar
  7. 7.
    Díaz, B., Joiret, S., Keddam, M., Nóvoa, X. R., Pérez, M. C., & Takenouti, H. (2004). Passivity of iron in red mud’s water solutions. Electrochimica Acta, 49(17–18), 3039–3048.CrossRefGoogle Scholar
  8. 8.
    Rocha, F. C., Medeiros-JUNIOR, R. A., Helene, P., Medeiros M. H. F. (2017). Corrosion potential: Influence of moisture, water-cement ratio, chloride content and concrete cover. Revista IBRACON de Estruturas e Materials, 10(4), pp. 864–885.CrossRefGoogle Scholar
  9. 9.
    Wang, P., & Liu, D. Y. (2012). Physical and chemical properties of sintering red mud and bayer red mud and the implications for beneficial utilization. Materials (Basel), 5(10), 1800–1810.CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • Sondi Sudheer
    • 1
    Email author
  • Uppara Raghu Babu
    • 1
  • B. Kondraivendhan
    • 1
  1. 1.Applied Mechanics DepartmentSardar Vallabhbhai National Institute of TechnologySuratIndia

Personalised recommendations