Feasibility of Producing Class F Fly Ash Geopolymer Mortar with Alkaline Water Containing Sodium Carbonate (Na2CO3)

  • Jai Sai TenepalliEmail author
  • D. Neeraja
Conference paper
Part of the Lecture Notes in Civil Engineering book series (LNCE, volume 25)

Abstract

This study investigated the feasibility of substituting demineralized water with alkaline water containing sodium carbonate (Na2CO3) with varying concentrations to prepare alkali reagent (sodium hydroxide solution), which was in turn used for synthesizing class F fly ash based geopolymer mortar. Geopolymer mortar cube specimens were cast using demineralized water, and demineralized water spiked with various concentrations of Na2CO3 as reference and test specimens, respectively. The concentration levels of Na2CO3 in engineered water considered were 0.5, 1.0, 1.5, 2.0, 7, 9, 11, 13, and 15 g/L. The concentration of the alkaline solution and the proportion of Na2SiO3 (water glass solution) to NaOH (sodium hydroxide solution) were fixed constant at 12 M and 1.5. The curing regime of 70 °C for 24 h without any rest period was considered to activate the geopolymerization process for test and reference specimens. The evaluation of compressive strength development after 28 days was interpreted based on the guidelines mentioned by Burea of Indian Standards. Subsequently, a comparison of the morphology and elemental composition of reference and test mortar mixtures was performed by scanning electron microscopic images and energy dispersive x-ray analysis. Results indicated that good strength geopolymer mortar could be developed by replacing demineralized water with alkaline water containing Na2CO3 of 1.0 g/L concentration along with 12 Molarity NaOH solution and 1.5 proportion of alkaline activator solution. The deviations in the compressive strength of the test geopolymer mortar mixture were due to a change in the microstructure and elemental composition which had arrived due to the presence of sodium carbonate in water.

Keywords

Geopolymer mortar Compressive strength Alkaline water SEM + EDAX Na2CO3 

References

  1. 1.
    Lloyd, N., & Rangan, V. (2009). Geopolymer concrete-sustainable cementless concrete. In P. R. Gupta, C. T. Holland, & V. M. Malhotra (ed.), ACI special publication SP-261, 10th ACI international conference on recent advances in concrete technology and sustainability issues, Oct 12, Seville (pp. 33–53). Farmington Hills: American Concrete Institute.Google Scholar
  2. 2.
    ASTM C 618–03. Standard specification for coal fly ash and raw or calcined natural pozzolans for use in concrete, American Society for Testing and Materials, ASTM Annual Book of Standards, ASTM International, West Conshohocken, PA, USA.Google Scholar
  3. 3.
    IS:2386 (Part III). (1963). Methods of test for aggregates for concrete. New Delhi, India: Bureau of Indian Standards.Google Scholar
  4. 4.
    IS 383. (1970). Specification for coarse and fine aggregates from natural sources for concrete. NewDelhi, India: Bureau of Indian Standards.Google Scholar
  5. 5.
    Swanepoel, J. C., & Strydom, C. A. (2002). Utilization of fly ash in a geopolymeric material. Applied Geochemistry, 17(8), 1143–1148.CrossRefGoogle Scholar
  6. 6.
    Venkateswara Reddy, V., Sudarsana Rao, H., & Jayaveera, K. N. (2006). Influence of strong alkaline substances (sodium carbonate and sodium bicarbonate) in mixing water on strength and setting properties of concrete. Indian Journal of Engineering Materials Science, 13, 123–128.Google Scholar
  7. 7.
    Al Bakri Abdullah, M. M., Kamarudin, H., Binhussain, M., Khairul Nizar, I., Rafiza, A. R., & Zarina, Y. (2012). Microstructure study on optimization of high strength fly ash based geopolymer. Advanced Materials Research, 476–478, 2173–2180. http://dx.doi.org/10.4028/www.scientific.net/AMR.476-478.2173.CrossRefGoogle Scholar
  8. 8.
    Hardjito, D., Cheak, C. C., & Lee Ing, C. H. (2008). Strength and setting times of low calcium fly ash-based geopolymer mortar. Modern Applied Science, 29(3), 3–11.Google Scholar
  9. 9.
    Abdulkareem, O. A., & Ramli, M. (2015). Optimization of alkaline activator mixing and curing conditions for A fly ash-based geopolymer paste system. Modern Applied Science, 9, 61–69.CrossRefGoogle Scholar
  10. 10.
    IS 4031(Part 6). (1988). Methods of physical tests for hydraulic cement. New Delhi, India: Bureau of Indian Standards.Google Scholar
  11. 11.
    IS 456. (2000). Plain and reinforced concrete code of practice. New Delhi, India: Bureau of Indian Standards.Google Scholar
  12. 12.
    Tenepalli, J. S., & Neeraja, D. (2018). Properties of class F fly ash based geopolymer mortar produced with alkaline water. Journal of Building Engineering, 19, 42–48.CrossRefGoogle Scholar
  13. 13.
    Chindaprasirt, P., Silva, P. D., Crentsil, K. S., & Hanjitsuwan, S. (2012). Effect of SiO2 and Al2O3 on the setting and hardening of high calcium fly ash-based geopolymer systems. Journal of Material Science, 47, 4876–483.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  1. 1.National Institute of Construction Management and ResearchPuneIndia
  2. 2.Vellore Institute of Technology (VIT)VelloreIndia

Personalised recommendations