Study on Mechanical Properties and Leaching of Heavy Metals in the Artificially Produced Fly Ash Aggregates

  • M. Roshan
  • K. N. Shivaprasad
  • Bibhuti Bhusan Das
Conference paper
Part of the Lecture Notes in Civil Engineering book series (LNCE, volume 25)

Abstract

The present study focusses on fly ash as an industrial by-product which can be utilised in the production of artificial lightweight aggregates using activator solution as a binder. Artificial aggregates in the form of pellets would be an alternative for the natural coarse aggregates which is currently being used in the construction industry. The production of pellets was done such that the water content in the pellets were fixed at 20% of the weight of fly ash, and the Na2O content in the pellets was varied between 4 and 7% of the weight of the pellets. The mechanical properties were studied such as specific gravity, particle-size distribution (sieve analysis), water absorption, crushing strength of individual pellets and aggregate impact value. Further, the leaching tests were carried out to estimate the leaching of metals such as iron, chromium and sodium from the pellets. The effect of different curing conditions such as ambient, heat and solution was also studied in this study. From the test results, the pellets size distribution was found to be well graded and specific gravity of pellets was found to be in the range from 1.88 to 1.96. There was an improvement in the mechanical properties of the artificially produced fly ash aggregates as the Na2O content increased in the alkaline solution. It was found that heat-cured pellets showed a significant advantage over solution and ambient-cured pellets in crushing strength. It was found that leaching of the heavy metals are decreased as the percentage of Na2O content increased, indicating that the addition of Na2O enhances the encapsulation of heavy metals.

Keywords

Fly ash aggregates Na2O content Curing regime Aggregate mechanical properties Leaching tests 

References

  1. 1.
    Central Electricity Authority (CEA) Report. (2017, December). Fly ash generation at coal/lignite based thermal power stations and its utilization in the country for the year 2016–17. New Delhi: Central Electricity Authority, Ministry of Power, Government of India.Google Scholar
  2. 2.
    IS 3812. (2013). Part 2, Specification for pulverized fuel ash: For use as admixture in cement mortar and concrete. New Delhi: Bureau of Indian Standards.Google Scholar
  3. 3.
    IS 1727. (1967). Methods of test for pozzolanic materials. New Delhi: Bureau of Indian Standards.Google Scholar
  4. 4.
    Mustafa Al Bakri, A. M., Kamarudin, H., Bnhussain, M., Rafiza, A. R., & Zarina Y. (2012). Effect of Na2SiO3/NaOH ratios and NaOH molarities on compressive strength of flyash-based geopolymer. ACI Materials Journal, 109(5), 503–508.Google Scholar
  5. 5.
    Rangan, B. V., Hardjito, D., Steenie, E. W., & Dody, M. J. S. (2005). Studies on fly ash-based geopolymer concrete. In Proceedings of the world congress geopolymer (Vol. 28, pp. 133–137). Saint Quentin, France.Google Scholar
  6. 6.
    Rahim, A., Rosniza, H., Khairun, A. A., Zakaria, M., Rahmiati, T., & Lukman, I. (2014). Effect of solid to liquid ratio on the mechanical and physical properties of fly ash geopolymer without sodium silicate. Applied Mechanics and Materials, 625, 46–49.CrossRefGoogle Scholar
  7. 7.
    IS 383. (2016). Specification for coarse and fine aggregates from natural sources for concrete. New Delhi: Bureau of Indian Standards.Google Scholar
  8. 8.
    Baykal, G., & Döven, A. G. (2000). Utilization of fly ash by pelletization process; theory, application areas and research results. Resources, Conservation and Recycling, 30(1), 59–77.CrossRefGoogle Scholar
  9. 9.
    Priyadharshini, P., Mohan Ganesh, G., & Santhi, A. S. (2011). Experimental study on cold bonded fly ash aggregates. International Journal of Civil and Structural Engineering, 2(2), 493–501.Google Scholar
  10. 10.
    Gomathi, P., & Sivakumar, A. (2012). Characterization on the strength properties of pelletized fly ash aggregate. ARPN Jouranl of Engineering and Applied Sciences, 7(11), 1523–1532.Google Scholar
  11. 11.
    Gomathi, P., & Sivakumar, A. (2014). Fly ash based lightweight aggregates incorporating clay binders. Indian Journal of Engineering and Materials Science, 21(2), 227–232.Google Scholar
  12. 12.
    Shivaprasad, K. N., & Das, B. B. (2018). Determination of optimized geopolymerization factors on the properties of pelletized fly ash aggregates. Construction and Building Materials, 163, 428–437.CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • M. Roshan
    • 1
  • K. N. Shivaprasad
    • 1
  • Bibhuti Bhusan Das
    • 1
  1. 1.Department of Civil EngineeringNational Institute of Technology KaranatakaSurathkal, MangaloreIndia

Personalised recommendations