Effect of EPS Porogen on Microstructure and Properties of ZTAp/High Chromium Cast Iron Composites

Conference paper

Abstract

The expandable polystyrene was added to the gap in the ceramic preform which was made of ZrO2 toughened Al2O3 (ZTA) ceramic particles. Increasing the porosity of the preform is beneficial to the high chromium cast iron infiltration and can obtain the composites of ZTA particles reinforced high chromium cast iron matrix. In this paper, studied the residues amount of the different porogen in the preform such as 10 ~ 20 mesh, 20 ~ 40 mesh, 40 ~ 80 mesh, 80 ~ 120 mesh and mixing particle sizes were heated to the temperature of 250, 350, 450, 550 °C. The corresponding composites were obtained under the different conditions and the interfacial effect, the wear resistance of the composites were observed. At the same time, the fracture mode of the composites was analyzed. The results showed that the porosity of preform with mixing particle sizes was the lowest at 550 °C and had the best interfacial, the highest wear resistance. The fracture mode of the composites was the particles fracture, metal matrix brittle fracture and the particles shedding from the matrix.

Keywords

Porogenin Metal matrix composites Preform Three-body abrasive wear 

References

  1. 1.
    Prasad D S, Shoba C, Hybrid composites—a better choice for high wear resistant materials, J Mater Res Technol. 3 (2014) 172–178.Google Scholar
  2. 2.
    Ge S, Wang Q, Wang J, The impact wear-resistance enhancement mechanism of medium manganese steel and its applications in mining machines, Wear. (2017) 376–377.Google Scholar
  3. 3.
    Miracle D B, Metal matrix composites-from science to technological significance, Compos Sci Technol. 65 (2005) 26–40.Google Scholar
  4. 4.
    Zhang Di, Zhang Guoding, Li Zhiqiang, The current state and trend of metal matrix composites, Materials China. 29 (2010) 1–7.Google Scholar
  5. 5.
    Zhao H, Li J, Guo S, et al, Fast preparation of ZTA-TiC-FeCrNi cermets by high-gravity combustion synthesis, Ceram Int. 2017.Google Scholar
  6. 6.
    Gao Mingxia, Pan Yi, F. J. Oliveria, J. L. Baptista, J. M. Vieira, Pressureless melt infiltration processing awnd the microstructural characteristics of TiC/NiAl composites, Acta Materiae compositae sinica. 21 (2004) 11–15.Google Scholar
  7. 7.
    Si C, Tang X, Zhang X, et al, Microstructure and mechanical properties of particle reinforced metal matrix composites prepared by gas-solid two-phase atomization and deposition technology, Mater Lett. 201 (2017) 78–81.Google Scholar
  8. 8.
    Clarke D R, Interpenetrating Phase Composites, J Am Ceram Soc. 75 (1992) 739–758.Google Scholar
  9. 9.
    Clegg W J, Kendall K, Alford N M, et al, A simple way to make tough ceramics, Nature. 347 (1990) 455–457.Google Scholar
  10. 10.
    Zhang Zhihui, Li Nan, Manufacturing process of porous ceramic material, Mater Lett. 17 (2003) 30–31, 49.Google Scholar
  11. 11.
    Pia G, Casnedi L, Ionta M, et al, On the elastic deformation properties of porous ceramic materials obtained by pore-forming agent method, Ceram Int. 41 (2015) 11097–11105.Google Scholar
  12. 12.
    Du Cheng, Yang Jun, Expanded Polystyrene (EPS) Geofoam: An analysis to characteristics and applications, Journal of southeast university (Natural Science Edition). 31 (2001) 138–142.Google Scholar
  13. 13.
    Zhou M J, Jiang Y H, Chong X Y. Interface transition layer interaction mechanism for ZTAP/HCCI composites[J]. Science & Engineering of Composite Materials, 2017.Google Scholar
  14. 14.
    Xu Guangdong, Xu Qiang, Pan Renming, Research on the thermal decomposition characteristics for the thermal insulation material of EPS in air, China plastics industry. 40 (2012) 67–70.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Mojin Zhou
    • 1
  • Yehua Jiang
    • 1
  • Xiaozu Zhang
    • 1
  • Nan Wang
    • 1
  1. 1.Faculty of Material Science and EngineeringKunming University of Science and TechnologyKunmingChina

Personalised recommendations