Single Stage Ageing Property and Precipitation Variation of a High-Zinc Al–Zn–Mg–Cu Alloy

  • Yun-Qiang Fan
  • Kai Wen
  • Zhi-Hui Li
  • Xi-Wu Li
  • Yong-An Zhang
  • Bai-Qing Xiong
  • Jian-Xin Xie
Conference paper

Abstract

In order to analyze single stage ageing behavior of a high-zinc Al–Zn–Mg–Cu alloy, the microstructure and property variations of the alloy treated by various temperatures were explored by hardness, conductivity, tensile properties, transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HREM) techniques. The results indicated that a long time was needed to reach a peak hardness value for the alloy treated at 100 and 120 °C and the peak hardness value could sustain a relatively long time interval. The alloy treated at 120 °C adopted a shorter time to reach peak hardness values and its peak hardness value was larger compared with that at 120 °C. The hardness treated at 140 °C reached the peak rapidly and then diminished continuously. With ageing time prolonging, the conductivities of the alloy treated at various temperatures increase persistently. After a peak ageing regime of 120 °C/24 h, the alloy possessed fine and dispersedly distributed matrix precipitates (MPs) and the ultimate tensile strength (UTS), yield strength (YS), elongation and electrical conductivity were 697 MPa, 655 MPa, 12.9% and 17.3 MS m−1, respectively. With the alloy temper varying from under-ageing to peak-ageing to over-ageing, the variety of MPs changed from GPI zone, GPII zone and η′ phase to GPII zone and η′ phase to η′ phase. During this process, the size distribution of MPs became broader and average precipitate size became larger.

Keywords

Al–Zn–Mg–Cu alloy High-zinc Ageing property Precipitation variation 

Notes

Acknowledgements

This study was financially supported by the National Key R&D Program of China (No. 2016YFB0300803, 2016YFB0300903).

References

  1. 1.
    Y. Chi, G. Gu, H. Yu, C. Hu, C. Chen, Laser surface alloying on aluminum and its alloys: a review, Opt. Laser Eng. 100 (2018) 23–37.Google Scholar
  2. 2.
    T. Dursun, C. Soutis, Recent developments in advanced aircraft aluminium alloys, Mater. Des. 56 (2014) 862–871.Google Scholar
  3. 3.
    S. Barter, M. Burchill, M. Jones, Measured fatigue crack growth increments versus predictions for small cracks in 7XXX aluminium alloys, Int. J. Fatigue 105 (2017) 144–159.Google Scholar
  4. 4.
    K. Wen, B. Xiong, Y. Zhang, Z. Li, X. Li, S. Huang, L. Yan, H. Yan, H. Liu, Over-aging influenced matrix precipitate characteristics improve fatigue crack propagation in a high Zn-containing Al-Zn-Mg-Cu alloy, Mater. Sci. Eng. A 716 (2018) 42–54.Google Scholar
  5. 5.
    I. Kalemba, C. Hamilton, S. Dymek, Natural ageing in friction stir welded 7136-T76 aluminum alloy, Mater. Des. 60 (2014) 295–301.Google Scholar
  6. 6.
    H. Zhang, N.P. Jin, J.H. Chen, Hot deformation behavior of Al-Zn-Mg-Cu-Zr aluminum alloys during compression at elevated temperature, T. Nonferr. Metals Soc. 21 (2011) 437–442.Google Scholar
  7. 7.
    K. Izabela, M. Krzysztof, W. Miroslaw, D. Stanislaw, H. Carter, EBSD Analysis of Friction Stir Welded 7136-T76 Aluminum Alloy, Solid State Phenom. 204 (2013) 258–261.Google Scholar
  8. 8.
    E. Acer, E. Çadırlı, H. Erol, T. Kırındı, M. Gündüz, Effect of heat treatment on the microstructures and tensile properties of Al-5.5Zn-2.5 Mg alloy, Mater. Sci. Eng. A 662 (2016) 144–156.Google Scholar
  9. 9.
    G.W. Zheng, H. Li, C. Lei, J. Fu, T.J. Bian, J.C. Yang, Natural aging behaviors and mechanisms of 7050 and 5A90 Al alloys: A comparative study, Mater. Sci. Eng. A 718 (2018) 157–164.Google Scholar
  10. 10.
    F.D. Zhang, H. Liu, C. Suebka, Y.X. Liu, Z. Liu, W. Guo, Y.M. Cheng, S.L. Zhang, L. Li, Corrosion behaviour of laser-cleaned AA7024 aluminium alloy, Appl. Surf. Sci. 435 (2018) 452–461.Google Scholar
  11. 11.
    S. Gang, C. Alfred, Early-stage precipitation in Al-Zn-Mg-Cu alloy (7050), Acta Mater. 52 (2004) 4503–4516.Google Scholar
  12. 12.
    Y. Liu, S. Liang, D. Jiang, Influence of repetitious non-isothermal ageing on microstructure and strength of Al-Zn-Mg-Cu alloy, J. Alloy Compd. 689 (2016) 632–640.Google Scholar
  13. 13.
    D. Liu, B. Xiong, F. Bian, Z. Li, X. Li, Y. Zhang, Q. Wang, G. Xie, F. Wang, H. Liu, Quantitative study of nanoscale precipitates in Al–Zn–Mg–Cu alloys with different chemical compositions, Mater. Sci. Eng. A 639 (2015) 245–251.Google Scholar
  14. 14.
    K. Wen, Y. Fan, G. Wang, L. Jin, X. Li, Z. Li, Y. Zhang, B. Xiong, Ageing behavior and precipitate characterization of a high-zinc Al-Zn-Mg-Cu alloy with various tempers, Mater. Des. 101 (2016) 16–23.Google Scholar
  15. 15.
    R. Ferragut, A. Somoza, A. Tolley, Microstructural variation of 7012 alloy during the early stages of artificial ageing, Acta Mater. 47 (1999) 4355–4364.Google Scholar
  16. 16.
    D. Liu, B. Xiong, F. Bian, X. Li, Z. Li, Y. Zhang, F. Wang, H. Liu, Quantitative study of precipitates in an Al-Zn-Mg-Cu alloy aged with various typical tempers, Mater. Sci. Eng. A 588 (2013) 1–6.Google Scholar
  17. 17.
    A.S. Prosviryakov, K.D. Shcherbachev, Strengthening of mechanically alloyed Al-based alloy with high Zr contents, Mater. Sci. Eng. A 713 (2018) 174–179.Google Scholar
  18. 18.
    G.H. Tao, C.H. Liu, J.H. Chen, Y.X. Lai, P.P. Ma, L.M. Liu, The influence of Mg/Si ratio on the negative natural ageing effect in Al-Mg-Si-Cu alloys, Mater. Sci. Eng. A 642 (2015) 241–248.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Yun-Qiang Fan
    • 1
    • 2
  • Kai Wen
    • 1
  • Zhi-Hui Li
    • 1
  • Xi-Wu Li
    • 1
  • Yong-An Zhang
    • 1
  • Bai-Qing Xiong
    • 1
  • Jian-Xin Xie
    • 2
  1. 1.State Key Laboratory of Nonferrous Metals and ProcessesGeneral Research Institute for Nonferrous MetalsBeijingChina
  2. 2.University of Science and Technology BeijingBeijingChina

Personalised recommendations