Sims Analysis of SiC Coated and Uncoated Nicalon Fibers

  • M. Lancin
  • J. S. Bour

Abstract

Pyrolytic SiC deposits were performed on Nicalon 202 SiC fibers using either a static method designed for fiber structure infiltration or a dynamical method designed for fiber coating. A Carbon deposit was sometimes introduced between the fiber and the SiC matrix. The coated fibers were analysed by Secondary Ion Mass Spectrometry (SIMS). The depth profiles obtained show that (i) the fibers retain their composition after the process (static or dynamical), (ii) the deposits prepared using the static method exhibit an heterogeneity of microstructure and composition; these changes are due to a transitory stage at the beginning of the CVD reaction and (iii) the deposits prepared using the dynamical method exhibit a constant carbon content higher than the stoechiometric one (C/Si = 1.4).

Keywords

Chemical Vapor Deposition Depth Profile Electron Energy Loss Spectroscopy Transitory Stage Chemical Vapor Deposition Process 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    - Parlier M., Thèse Ecole Sup. des Mines, Paris (1984).Google Scholar
  2. 2.
    - Anxionnaz F., Thèse Université Paris VI (1987).Google Scholar
  3. 3.
    - Bour J.S., Thèse Université Paris XI (1988).Google Scholar
  4. 4.
    - Brennan J.J., Proc. of the Conference on Tailoring Multiphase and Composite Ceramics. Penn State University (17–19 July 1985).Google Scholar
  5. 5.
    - Lesniewsky, Rapport de Contrat DRET, n°84–447 (1986).Google Scholar
  6. 6.
    - Lancin M., Anxionnaz F., Schuhmacher M., Dugne O., Trebbia P., Mat. Res. Soc. Symp. Proc. 78 (1987) 231–238.CrossRefGoogle Scholar
  7. 7.
    - Anxionnaz F., Schuhmacher M., Trebbia P., Lancin M., J. Microsc. Spectr. Electron. 11 (1986) 421–427.Google Scholar
  8. 8.
    - Rawlins H.H., Nolan T.A., Stinton D.P., Lowden R.A., Mat. Res. Soc Symp. Proc. (1987) 293–230.Google Scholar

Copyright information

© Springer Science+Business Media B.V. 1989

Authors and Affiliations

  • M. Lancin
    • 1
  • J. S. Bour
    • 1
  1. 1.Laboratoire de Physique des MatériauxCNRSMeudonFrance

Personalised recommendations