Ferroelectric Thin Films from Metallo-organics: The Influence of Different Atmospheres during RTA Processing

  • Y. Shi
  • E. Sánchez-Carambot
  • W. Otaño
  • L. J. Martínez-Miranda
  • J. J. Santiago-Avilés

Abstract

Barium Titanate (BaTiO3) films have been deposited on platinum via spin-casting metallo-organic compounds and rapid thermal annealing (RTA). This method, called metallo-organic decomposition (MOD), produces tetragonal BaTiO3 films with easily controllable stoichiometry as determined by x-ray diffraction (XRD) and Auger electron spectroscopy (AES). The precursors used were barium neodecanoate and titanium dimethoxy dineodecanoate. The film precursor is obtained by mixing the individual precursors in a nearly 1∶1 molar ratio before processing. Variable thickness (0.1–3 µm) is achieved by spin-casting multiple layers of the films. The films were RTA processed to 650° for 30s or to 950° for 15s under controlled atmosphere (O2, Ar, and partial vacuum). The films processed under O2 showed better stoichiometry and purity than the ones processed under partial vacuum (10−3 Torr) as evidenced by XRD and AES. The carbon contamination from pyrolysis residues, prevalent in the partial vacuum processed films, fell below the instrument detection limit for the O2 and Ar processed films. All the films are uniform and crack-free as shown in the scanning electron micrograph (SEM). Average grain size determined by SEM ranged from 0.01 µm to 0.5 µm, depending on the annealing condition.

Keywords

Scanning Electron Micrograph Auger Electron Spectroscopy Rapid Thermal Annealing Barium Titanate Ferroelectric Thin Film 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J.R. Hanrahan, E. Sánchez-Carambot, Q. Jiang, D. Berry and J.J. Santiago-Avilés, Proc. of 1st International Ceramic Science and Technology Congress, American Ceramic Society, Anaheim, CA (1989).Google Scholar
  2. 2.
    X.Y. Hung, J.J. Santiago-Avilés and D. Berry, Abstract to Alfreds Conference on Electronic Ceramics, Alfred, NY (1987).Google Scholar
  3. 3.
    R.W. Vest and J. Xu, Ferroelectrics, 93, 21 (1989).CrossRefGoogle Scholar
  4. 4.
    R.W. Vest and J. Xu, IEEE Trans. UFFC (November 1988).Google Scholar
  5. 5.
    J.J. Xu, A.S. Shaikh and R.W. Vest, IEEE Trans. UFFC, 36, 307 (1989).CrossRefGoogle Scholar
  6. 6.
    J.R. Hanrahan, E. Sánchez-Carambot, D. Berry, Q. Jiang and J.J. Santiago-Avilés, Thin Solid Films, in press.Google Scholar
  7. 7.
    J.J. Santiago-Avilés, C.S. Wei and J. Van der Spiegel, Materials Letters 2(6A), 477 (1984).CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media Dordrecht 1990

Authors and Affiliations

  • Y. Shi
    • 1
  • E. Sánchez-Carambot
    • 1
  • W. Otaño
    • 1
  • L. J. Martínez-Miranda
    • 1
  • J. J. Santiago-Avilés
    • 1
  1. 1.University of PennsylvaniaPhiladelphiaUSA

Personalised recommendations