Hydrothermal Growth of Quartz Crystals in KCl Solution

  • Masahiro Hosaka
  • Sadao Taki

Abstract

Quartz crystals were hydrothermally grown in KCl solutions in the range 350–500° C, and it was possible to produce large crystals after a few months. The best conditions to obtain sufficient growth rates were found to be: growth temperatures above 400°C and 10 wt% KCl solution. Striations were observed on the prism face and the relative growth rates were R > r. Furthermore, the solubility of quartz was measured in 2, 10, and 30 wt% KCl solutions in the range 400-440°C. It was found that the solubility obeyed the Van’t Hoff equation with a heat of solution of 7,600, 6,900, and 8,000 cal/mole, respectively, in 2, 10, and 30 wt% KCl solutions.

Keywords

Fluid Inclusion Alkaline Solution Relative Growth Rate Quartz Crystal Hydrothermal Growth 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    M. Hosaka and S. Taki, J. Crystal Growth 51 (1981) 640.CrossRefGoogle Scholar
  2. [2]
    M. Enjoji, Sci. Rept. Tokyo Educ. Univ. Sec. C11 No. 106 (1972) 79.Google Scholar
  3. [3]
    T.M. Sushchevskaya and G.F. Ivanova, Geokhimia 9 (1967) 1099.Google Scholar
  4. [4]
    S. Taki and K. Yamada, Rept. Fac. Educ. Yamanashi Univ. 12 (1961) 146.Google Scholar
  5. [5]
    R.A. Laudise, J. Am. Chem. Soc. 81 (1959) 562.CrossRefGoogle Scholar
  6. [6]
    F. Muto and S. Taki, Rept. Fac. Eng. Yamanashi Univ. 13 (1963) 152.Google Scholar
  7. [7]
    A.J. Cohen, J. Phys. Chem. Solids 13 (1960) 321.CrossRefGoogle Scholar
  8. [8]
    G. Lehmann and H.U. Bambauer, Angew. Chem. Intern Ed. 12 No. 4 (1973) 283.CrossRefGoogle Scholar

Copyright information

© Elsevier Science Publishers Ltd 1989

Authors and Affiliations

  • Masahiro Hosaka
    • 1
  • Sadao Taki
    • 1
  1. 1.Institute of Inorganic Synthesis, Faculty of EngineeringYamanashi UniversityKofuJapan

Personalised recommendations