Damage Mechanisms and Energy Absorption in Composite Laminates Under Low Velocity Impact Loads

Chapter
Part of the Solid Mechanics and Its Applications book series (SMIA, volume 192)

Abstract

An extensive study of the behaviour of composite laminates subjected to dynamic loads was carried out by the authors many years in order to understand the complex mechanisms of damage initiation and propagation under low velocity impact loads. A review of the main results is hereafter presented.

The problem is that many parameters are involved in an impact and the induced damage is very complex and not always visible. The present research efforts were undertaken to supply semi empirical and analytical models for the prediction of the impact response in terms of load curve, damage, involved energies and forces, independently of the particular laminate, its thickness and stacking sequence, matrix type and content, fibre type and architecture, fibre orientations and impact conditions such as tup and support diameter, load speed.

Experimental tests were carried out on different material systems varying the initial kinetic energy until the complete penetration. This allows the study of the start and propagation of the failure modes. From the load-deflection curves recorded, all the impact parameters involved like first failure and maximum load and energy, absorbed and penetration energy, were obtained. The influence of the thickness and stacking sequence so that the composite system, constrain condition and tup diameter on the impact parameters was evaluated. Destructive and non-destructive techniques were adopted to investigate the failure modes and the observed damage was correlated to the relative energies.

The analysis highlighted the importance of the penetration energy, Up. An elastic solution available for circular isotropic plates loaded at the centre was modified to model the indentation and applied to the prediction of the load-displacement curve necessary to know the energy that cause the first failure. Interestingly, the force required for damage initiation under form of delamination was found to increase at the increasing of the thickness, t, following a power law whose exponent is very close to 1.5 of the contact law.

Keywords

Impact Energy Residual Strength Glass Fibre Reinforce Plastic Fibre Failure Laminate Thickness 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

References

  1. 1.
    Sun CT, Liou WJ (1989) Investigation of laminated composite plates under impact dynamic loading using a three-dimensional hybrid stress finite element method. Comput Struct 33(3):879–884CrossRefGoogle Scholar
  2. 2.
    Cairns DS (1991) Simple elasto-plastic contact laws for composites. J Reinf Plast Compos 10(4):423–433CrossRefGoogle Scholar
  3. 3.
    Bucinell RB, Nuismer RJ, Koury JL (1991) Response of composite plates to quasi-static impact events. In: O’Brien TK (ed) Composite materials: fatigue and fracture. ASTM STP 1110., pp 528–549Google Scholar
  4. 4.
    Abrate S (1994) Impact on laminated composites: recent advances. Appl Mech Rev 47(11):517–544CrossRefGoogle Scholar
  5. 5.
    Hong S, Liu D (1989) On the relationship between impact energy and delamination area. Exp Mech 29(2):115–120CrossRefGoogle Scholar
  6. 6.
    Hull D, Shi YB (1993) Damage mechanism characterisation in composite damage tolerance investigations. Compos Struct 23:99–120CrossRefGoogle Scholar
  7. 7.
    Hitchen SA, Kemp RMJ (1995) The effect of stacking sequence on impact damage in a carbon fibre/epoxy composite. Composites 26:207–214CrossRefGoogle Scholar
  8. 8.
    Richardson MOW, Wisheart MJ (1996) Review of low-velocity impact properties of composite materials. Composites A 27A:1123–1131CrossRefGoogle Scholar
  9. 9.
    Caprino G (1984) Residual strength prediction of impacted CFRP laminates. J Compos Mater 18:508–518CrossRefGoogle Scholar
  10. 10.
    Cantwell WJ, Morton J (1991) The impact resistance of composite materials – a review. Composites 22(5):347–362CrossRefGoogle Scholar
  11. 11.
    Cairns DS, Minuet PJ, Abdallah MG (1993) Theoretical and experimental response of composite laminates with delaminations loaded in compression. Compos Struct 25:113–120CrossRefGoogle Scholar
  12. 12.
    Kim J-K, Mackay DB, Mai Y-W (1993) Drop-weight impact damage tolerance of CFRP with rubber-modified epoxy matrix. Composites 24(6):485–494CrossRefGoogle Scholar
  13. 13.
    Choi HY, Downs RJ, Chang F-K (1991) A new approach toward understanding damage mechanisms and mechanics of laminated composites due to low velocity impact: part I-experiments. J Comp Mater 25:992–1011Google Scholar
  14. 14.
    Choi HY, Chang FK (1992) A model for predicting damage in graphite/epoxy laminated composites resulting from low-velocity point impact. J Compos Mater 26(14):2134–2169CrossRefGoogle Scholar
  15. 15.
    Abrate S (1998) Impact on composite structures. Cambridge University Press, CambridgeCrossRefGoogle Scholar
  16. 16.
    Timoshenko SP, Woinowsky-Krieger S (1959) Theory of plates and shells. McGraw-Hill, SingaporeGoogle Scholar
  17. 17.
    Caprino G, Lopresto V (2000) The significance of indentation in the inspection of CFRP panels damaged by low-velocity impact. Compos Sci Technol 60:1003–1012CrossRefGoogle Scholar
  18. 18.
    Chang FK, Choi HY, Wang HS (1990) Damage of laminated composites due to low velocity impact. In: 31st AIAA/ASME/ASCE/AHS/ASC structures, structural dynamics and Materials conference, Long Beach, CA, 2–4 April 1990, pp 930–940Google Scholar
  19. 19.
    Cantwell WJ, Morton J (1990) Impact perforation of carbon fibre reinforced plastics. Compos Sci Technol 38:119–141CrossRefGoogle Scholar
  20. 20.
    Husman GE, Whitney JM, Halpin JC (1975) Residual strength characterisation of laminated composites subjected to impact loading. ASTM STP 568:92–113Google Scholar
  21. 21.
    Delfosse D, Poursartip A (1985) Experimental parameter study of static and dynamic out-of-plane loading of CFRP laminates. In: Proceedings of the 10th international conference on composite materials (ICCM10), Whistler, Canada, August 1985, pp V-583-590Google Scholar
  22. 22.
    Bibo G, Leicy D, Hogg PJ, Kemp M (1994) High-temperature damage tolerance of carbon fibre-reinforced plastics. Part 1: impact characteristics. Composites 25(6):414–424CrossRefGoogle Scholar
  23. 23.
    Bibo GA, Hogg PJ (1998) Influence of reinforcement architecture on damage mechanisms and residual strength of glass-fibre/epoxy composite systems. Compos Sci Technol 58:803–813CrossRefGoogle Scholar
  24. 24.
    Caprino G, Lopresto V, Scarponi C, Briotti G (1999) Influence of material thickness on the response of carbon-fabric/epoxy panels to low-velocity impact. Compos Sci Technol 59:2279–2286CrossRefGoogle Scholar
  25. 25.
    Ghasemi Nejhad MN, Parvizi-Majidi A (1990) Impact behaviour and damage tolerance of woven carbon fibre-reinforced thermoplastic composites. Composites 21(2):155–168CrossRefGoogle Scholar
  26. 26.
    Caprino G, Langella A, Lopresto V (2002) Elastic behaviour of circular composite plates transversely loaded at the centre. Composites A 33:1191–1197CrossRefGoogle Scholar
  27. 27.
    Schoeppner GA, Abrate S (2000) Delamination threshold loads for low velocity impact on composite laminates. Composites A 31:903–915CrossRefGoogle Scholar
  28. 28.
    Sjoblom PO, Hartness TM, Cordell TM (1988) On low-velocity impact testing of composite materials. J Compos Mater 22(1):30–52CrossRefGoogle Scholar
  29. 29.
    Delfosse D, Poursatip A (1997) Energy-based approach to impact damage in CFRP laminates. Composites A 28A:647–655CrossRefGoogle Scholar
  30. 30.
    Liu S, Kutlu Z, Chang FK (1993) Matrix cracking and delamination propagation in laminated composites subjected to transversely concentrated loading. J Compos Mater 27(5):436–470CrossRefGoogle Scholar
  31. 31.
    Herup EJ, Palazotto AN (1997) Low-velocity impact damage initiation in graphite/epoxy/Nomex honeycomb-sandwiche plates. Compos Sci Technol 57(12):282–289Google Scholar
  32. 32.
    Yang SH, Sun CT (1982) Indentation law for composite laminates. In: Daniel I (ed) Composite materials: testing and design (sixth conference), ASTM STP 787, pp 425–449Google Scholar
  33. 33.
    Tan TM, Sun CT (1985) Use of statical indentation laws in the impact analysis of laminated composite plates. J Appl Mech 52(8):6–12CrossRefGoogle Scholar
  34. 34.
    Jackson WC, Poe CC Jr (1993) The use of impact force as a scale parameter for the impact response of composite laminates. J Compos Technol Res 15(4):282–289CrossRefGoogle Scholar
  35. 35.
    Abrate S (2001) Modeling of impacts on composite structures. Compos Struct 51:129–138CrossRefGoogle Scholar
  36. 36.
    Timoshenko SP Strength of materials. McGraw-Hill, New YorkGoogle Scholar
  37. 37.
    Chang FK, Choi HY, Wang HS (1990) Damage of laminated composites due to low velocity impact. In: 31st AIAA/ASME/ASCE/AHS/ASC structures, structural dynamics and materials conference, Long Beach, CA, 2–4 April 1990, pp 930–940Google Scholar
  38. 38.
    Stout MG, Koss DA, Liu C, Idasetima J (1999) Damage development in carbon/epoxy laminates under quasi-static and dynamic loading. Compos Sci Technol 59:2339–2350CrossRefGoogle Scholar
  39. 39.
    Gosse JH, Mori PBY (1988) Impact damage characterization of graphite/epoxy laminates. In: Proceedings of the 3rd technical conference of the American Society for Composites, Seattle, WA, pp 334–353Google Scholar
  40. 40.
    Tsai SW, Hahn HT (1975) Introduction to composite materials. Technomic Publishing Company, LancasterGoogle Scholar
  41. 41.
    Hashin Z (1975) Failure criteria of unidirectional fiber composites. J Appl Mech 47:329–334CrossRefGoogle Scholar
  42. 42.
    Liu S (1994) Quasi impact damage initiation and growth of thick-section and toughened composite materials. Int J Solids Struct 31(22):3079–3098MATHCrossRefGoogle Scholar
  43. 43.
    Siow YP, Shim PW (1998) An experimental study of low velocity impact damage in woven fiber composites. J Compos Mater 32(12):1178–1202CrossRefGoogle Scholar
  44. 44.
    Kaczmerek H (1995) Ultrasonic detection of damage in CFRPs. J Compos Mater 29:59–95CrossRefGoogle Scholar
  45. 45.
    Hosur MV, Murthy CRL, Ramamurthy TS, Shet A (1998) Estimation of impact-induced damage in CFRP laminates through ultrasonic imaging. NDT&E Int 31:359–374CrossRefGoogle Scholar
  46. 46.
    Olsson R (2001) Analytical prediction of large mass impact damage in composite laminates. Composites A 32:1207–1215CrossRefGoogle Scholar
  47. 47.
    Sjoblom P (1987) Simple design approach against low velocity impact damage. In: Proceedings of 32nd SAMPE symposium, Anaheim, CA, pp 529–539Google Scholar
  48. 48.
    Caprino G, Langella A, Lopresto V (2003) Prediction of the first failure energy of circular carbon fibre reinforced plastic plates loaded at the centre. Composites A 34:349–357CrossRefGoogle Scholar
  49. 49.
    Zhang X (1998) Impact damage in composite aircraft structures-experimental testing and numerical simulation. Proc Inst Mech Eng 212(4):245–259Google Scholar
  50. 50.
    Davies GAO, Zhang X, Zhou G, Watson S (1994) Numerical modelling of impact damage. Composites 25(5):342–350CrossRefGoogle Scholar
  51. 51.
    Davies GAO, Zhang X (1995) Impact damage prediction in carbon composite structures. Int J Impact Eng 16(1):149–170CrossRefGoogle Scholar
  52. 52.
    Olsson R (1999) A review of impact experiments at FFA during 1986 to 1998. The Aeronautical Research Institute of Sweden, FFA TN 1999–08Google Scholar
  53. 53.
    Lesser AJ, Filippov AG (1991) Kinetics of damage mechanisms in laminated composites. In: International SAMPE symposium and exhibition, vol 36, part 1, pp 886–900Google Scholar
  54. 54.
    Crivelli Visconti I, Caprino G, Di Ilio A, Carrino L (1983) Impact tests on CFRP: a static-dynamic analogy. In: High performance composite materials – new applications and industrial production, acts of 4th international SAMPE conference-SAMPE Euro chapter, Bordeaux, 17–20 October 1983, pp 189–196Google Scholar
  55. 55.
    Lesser AJ, Filippov AG (1991) Kinetics of damage mechanisms in laminated composites. In: International SAMPE symposium and exhibition, vol 36, part 1, pp 886–900Google Scholar
  56. 56.
    Srinivasan K, Jackson WC, Hinkley JA (1991) Response of composite materials to low velocity impact. In: International SAMPE symposium and exhibition, vol 36, part 2, pp 850–862Google Scholar
  57. 57.
    Shivakumar KN, Elber W, Illg W (1985) Prediction of low velocity impact damage in thin circular laminates. AIAA J 23(3):442–449MATHCrossRefGoogle Scholar
  58. 58.
    Caprino G, Crivelli Visconti I, Di Ilio A (1984) Composite materials response under low-velocity impact. Compos Struct 2:261–271CrossRefGoogle Scholar
  59. 59.
    Wu E, TSai CZ, Chen YC (1994) Penetration into glass/epoxy composite laminates. J Compos Mater 28:1783–1802CrossRefGoogle Scholar
  60. 60.
    Zenkour AM, Mashat DS (2009) Exact solutions for variable-thickness inhomogeneous elastic plates under various boundary conditions. Meccanica 44(4):433–447MathSciNetMATHCrossRefGoogle Scholar
  61. 61.
    Agarwal BD, Broutman LJ (1980) Analysis and performance of fiber composites. Wiley, New YorkGoogle Scholar
  62. 62.
    Grediac M (1999) A procedure for designing laminated plates with required stiffness properties. Application to thin quasi-isotropic quasi-homogeneous uncoupled laminates. J Compos Mater 33:1939CrossRefGoogle Scholar
  63. 63.
    Park JW, Kim YH (1999) Predictor-corrector procedure for displacements, stresses and their sensitivity coefficients in composite panels. J Compos Mater 33:1222CrossRefGoogle Scholar
  64. 64.
    Wang CM, Reddy JN, Lee KH (2000) Shear deformable beams and plates. Elsevier, AmsterdamMATHGoogle Scholar
  65. 65.
    Scarponi C, Briotti G, Barboni R, Marcone A, Iannone M (1996) Impact testing on composite laminates and sandwich panels. J Compos Mater 30(17):1873–1911CrossRefGoogle Scholar
  66. 66.
    Lagace PA, Wolf E (1993). Impact damage resistance of several laminated material systems. In: 34th AIAA structures, structural dynamics and materials conference, La Jolla, CA, Pt. 4, pp 1863–1872Google Scholar
  67. 67.
    Lopresto V, Caprino G (2002) Elastic response of circular CFRP plates under low-velocity impact. In: Proceedings of ECCM10, 3–7 giugno 2002, Bruge, BelgioGoogle Scholar
  68. 68.
    Sun CT, Chen JK (1985) On the impact of initially stressed composite laminates. J Compos Mater 19:490–503CrossRefGoogle Scholar
  69. 69.
    Davies GAO, Hitchings D, Wang J (2000) Prediction of threshold impact energy for onset of delamination in quasi-isotropic carbon/epoxy composite laminates under low-velocity impact. Compos Sci Technol 60:1–7CrossRefGoogle Scholar
  70. 70.
    Cartiè DDR, Irving PE (2002) Effect of resin and fibre properties on impact and compression after impact performance of CFRP. Composites A 33:483–493CrossRefGoogle Scholar
  71. 71.
    Lopresto V, Melito V, Leone C, Caprino G (2006) Effect of stitches on the impact behaviour of graphite/epoxy composites. Compos Sci Technol 66/2:233–239Google Scholar
  72. 72.
    Lagace PA, Williamson JE, Tsang PHW, Wolf E, Thomas SA (1993) A preliminary proposition for a test method to measure (impact) damage resistance. J Reinf Plast Compos 12(5):584–601CrossRefGoogle Scholar
  73. 73.
    Poe Jr CC (1991) Relevance of impacter shape to non visible damage and residual tensile strength of a thick graphite/epoxy laminate. In: O’Brien TK (ed) Composite materials: fatigue and fracture, vol 3, ASTM STP 1110. American Society for Testing and Materials, Philadelphia, PA, pp 501–527Google Scholar
  74. 74.
    Sutherland LS, Guedes Soares C (2005) Impact on low fibre-volume, glass/polyester rectangular plates. Compos Struct 68:13–22CrossRefGoogle Scholar
  75. 75.
    Wardle MW, Tokarsky EW (1983) Drop weight impact testing of laminates reinforced with Kevlar aramid fibres, E-glass and graphite. Compos Technol Rev 5(1):4–10CrossRefGoogle Scholar
  76. 76.
    Hsieh CY, Mount A, Jang BZ, Zee RH (1990) Response of polymer composites to high and low velocity impact. In: Proceedings of the 22nd international SAMPE technical conference, 6–8 November 1990, pp 14–27Google Scholar
  77. 77.
    Caprino G, Lopresto V (2000) Factors affecting the penetration energy of glass fibre reinforced plastics subjected to a concentrated transverse load. In: ECCM–9, Brighton, 4–7 June 2000Google Scholar
  78. 78.
    Babic L, Dunn C, Hogg PJ (1989) Damage development and its significance in GRP subjected to impact. Plast Rubb Process Appl 12(4):199–207Google Scholar
  79. 79.
    Cantwell WJ, Morton J (1989) The influence of varying projectile mass on the impact response of CFRP. Compos Struct 13:101–104CrossRefGoogle Scholar
  80. 80.
    Caprino G (1989) Results of instrumented drop-weight impact tests on polycarbonate and glass fibre reinforced plastics panels. Istituto Donegani internal reportGoogle Scholar
  81. 81.
    Strait LH, Karasek ML, Amateau MF (1992) Effects of stacking sequence on the impact resistance of fiber reinforced thermoplastic toughened epoxy laminates. J Compos Mater 26(12):1725–1740CrossRefGoogle Scholar
  82. 82.
    Chotard TJ, Benzeggagh ML (1998) On the mechanical behaviour of pultruded sections submitted to low-velocity impact. Compos Sci Technol 58(6):839–854CrossRefGoogle Scholar
  83. 83.
    Wu E, Shyu K (1993) Response of composite laminates to contact loads and relationship to low-velocity impact. J Compos Mater 27(15):1443–1464CrossRefGoogle Scholar
  84. 84.
    Wang H, Vu-Khanh T (1994) J Compos Mater 28:684Google Scholar
  85. 85.
    Cantwell WJ, Morton J (1990) An assessment of the residual strength of an impact-damaged carbon fibre reinforced epoxy. Compos Struct 14:303–317CrossRefGoogle Scholar
  86. 86.
    Ilcewicz I (1997). Impact damage in composite structures. Polymer matrix composites, MIL- handbook 17Google Scholar
  87. 87.
    Davidson BD, Kumar M, Soffa MA (2009) Influence of mode ratio and hygrothermal condition on the delamination toughness of a thermoplastic particulate interlayered carbon/epoxy composite. Composites A 40:67–79CrossRefGoogle Scholar
  88. 88.
    Scarponi C, Briotti G, Barboni R (1999) Reduction of tensile strength in angle-ply composite laminates due to low-velocity impact. J Reinf Plast Compos 18(1):63–85Google Scholar
  89. 89.
    Morton J, Godwin EW (1989) Impact response of tough carbon fibre composites. Compos Struct 13:1–19CrossRefGoogle Scholar
  90. 90.
    Liu D (1988) Impact-induced delamination – a view of bending stiffness mismatching. J Compos Mater 22:674–692CrossRefGoogle Scholar
  91. 91.
    Kumar P, Rai B (1993) Delaminations of barely visible impact damage in CFRP laminates. Compos Struct 23:313–318CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media Dordrecht 2013

Authors and Affiliations

  1. 1.Department of Materials and Production EngineeringUniversity of Naples Federico IINaplesItaly

Personalised recommendations