The Formation/Nucleation of Fatigue Cracks in Aircraft Structural Materials

  • David W. Hoeppner
Conference paper

Abstract

The issue of crack formation/nucleation and propagation related to model development for accurate fatigue life estimation/prediction of aircraft materials has been and is currently a vexing challenge.

In the 1800’s Sorby used the optical microscope to study fatigue deformation of materials. The early investigators of fatigue wanted to learn the mechanism(s) of fatigue crack formation/nucleation and propagation. Many investigators oriented toward developing this understanding aided progress. Many of the studies that were made were “static”. That is, materials were exposed to cyclic loading and then viewed in a light microscope. The paper will illustrate the importance of understanding the formation/nucleation process and its impact on life prediction issues. A few cases will be mentioned where the formation/nucleation of cracks and its relationship to intrinsic and extrinsic factors in aircraft will be presented.

The development of the scanning electron microscope aided the understanding fatigue of materials. Starting in 1970 numerous investigators developed fatigue machines that were either placed in the chamber of an SEM or were attached to the SEM and conducted “dynamic” studies. Many contributions have been made and some will be reviewed briefly in this paper. The past 45 years has seen the development of numerous in-situ systems for studying the process of fatigue crack formation/nucleation and the study of microstructural effects on the early stages of crack propagation of aircraft and other structural materials. This has led to increased understanding of fatigue crack formation/nucleation and propagation of cracks that is based on direct observation rather than speculation. Recently a new in situ SEM fatigue system has been developed at the University of Utah and work also has been done which allows accurate determination of local grain orientation effects and the role of relative orientation on crack nucleation and early crack propagation.

The background of many of the above studies will be presented in the paper. Subsequently, some of the major contributions these workers have made to understand fatigue deformation in aircraft structural materials will be presented. The paper reviews progress of these studies and insights into fatigue with emphasis on aircraft structural materials. The paper concludes with a discussion of some of the opportunities available to develop a greater understanding of the fatigue crack formation/nucleation process and also to develop a greater understanding of microstructurally short crack propagation.

Keywords

Fatigue Crack Fatigue Crack Growth Fatigue Crack Propagation Corrosion Fatigue Short Crack 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Griffith, A.A.: The Phenomena and Rupture and Flow in Solids. Philosophical Transactions of the Royal Society of London, Series A 221, 163–198 (1921)CrossRefGoogle Scholar
  2. 2.
    Schijve, J.: Analysis of the Fatigue Phenomenon in Aluminum Alloys. NLR-TR M.2122, National Aerospace Laboratory, Amsterdam (1964)Google Scholar
  3. 3.
    Schijve, J.: Significance of Fatigue Cracks in the Micro-Range and Macro-Range, Fatigue Crack Propagation. In: ASTM STP, vol. 415, pp. 415–459. ASTM (1967)Google Scholar
  4. 4.
    Hoeppner, D.W.: The Effect of Grain Size on Fatigue Crack Propagation in Copper. Fatigue Crack Propagation. In: ASTM STP, vol. 415, pp. 486–504. ASTM (1967)Google Scholar
  5. 5.
    Hoeppner, D. W.: Corrosion Fatigue Considerations in Materials Selection and Design. Invited Keynote paper. International Conference on Corrosion Fatigue (June 1971); Published in the Conference Proceedings, NACE, pp. 3–11 (1972)Google Scholar
  6. 6.
    Hoeppner, D. W.: Initiation of Fatigue in Aluminum Alloys. American Institute of Mining, Metallurgical, and Petroleum Engineers, Symposium on Fatigue of Metals, Atlanta, GA (April 1971)Google Scholar
  7. 7.
    Hoeppner, D. W.: Metallurgical Aspects of Fatigue. In: American Society of Metals, WESTEC Conference, Los Angeles, CA (March 1971)Google Scholar
  8. 8.
    Hoeppner, D. W.: The Mechanisms of Fatigue - Part 1 The Effect of Grain Size on Fatigue (Preliminary Results), Lockheed-California Company, LR 24368 (December 1971)Google Scholar
  9. 9.
    Hoeppner, D.W., Krupp, W.: Prediction of Component Life by Application of Fatigue Crack Growth Knowledge. Engineering Fracture Mechanics 6, 47–70 (1974)CrossRefGoogle Scholar
  10. 10.
    Hoeppner, D.W.: Comments on Initiation and Propagation of Fretting Fatigue Cracks (letter to the editor). Wear 43, 267–270 (1977)CrossRefGoogle Scholar
  11. 11.
    Hoeppner, D.W.: Estimation of Component Life by Application of Fatigue Crack Growth Threshold Knowledge. In: Fatigue, Creep of Pressure Vessels for Elevated Temperature Service, MPC, vol. 17, pp. 1–85. ASME, N.Y (1981)Google Scholar
  12. 12.
    Jeal, R.: Defects and Their Effect on the Behavior of Gas Turbine Engine Discs. In: Maintenance in Service of High Temperature Parts, AGARD Proceedings, vol. 317 (1981); Structures and Materials Panel, Noordwijkerhoot, The Netherlands, NATO-AGARD, France (1981)Google Scholar
  13. 13.
    Hoeppner, D., Venter, R., McCammond, D., Ekvall, J.: Aircraft Structural Fatigue, four volumes of notes for FAA two week course held at U of Toronto (1979-85) and U of Utah (1985-92), FAA, Oklahoma City, OK or available from the authorGoogle Scholar
  14. 14.
    Hoeppner, D. W.: Application of Damage Tolerance Concepts to ’Short Cracks’ in Safety Critical Components. In: ICAF Proceedings of International Committee on Aeronautical Fatigue Symposium, Toulouse, France (May 1983)Google Scholar
  15. 15.
    Hoeppner, D. W.: Parameters that Input to Application of Damage Tolerance Concepts to Critical Engine Components. AGARD Conference, San Antonio, Texas, (April 1985); Published in Conference Proceedings AGARD-CP 393, Damage Tolerance Concepts forCritical Engine Components, pp. 4-1 – 4-16, NATO-AGARD, France, (August 1985) invited keynote paperGoogle Scholar
  16. 16.
    Hoeppner, D. W.: Damage Tolerance in Gas Turbine Engines–Future Technology Requirements. Presented at NATO-AGARD-SMP, meeting held in Mierlo, The Netherlands, October 1988, AGARD/SMP Review Damage Tolerance for Engine Structures, 2. Defects and Quantitative Material Behavior, AGARD report No. 769, NATO-AGARD, Neuilly Sur Seine, France (1989); paper no. 7. Invited keynote paperGoogle Scholar
  17. 17.
    Freudenthal, A.: Fatigue and Fracture Mechanics. Engineering Fracture Mechanics 5, 403–414 (1973)CrossRefGoogle Scholar
  18. 18.
    Swift, S.: Sticks and Stones (Could the words of aeronautical fatigue hurt us?). In: 26th ICAF Symposium, Montreal, Quebec, Canada, June 1-3 (2011)Google Scholar
  19. 19.
    Halford, G.: Low-Cycle Thermal Fatigue. NASA TM 87225, p. 11 (February 1986); Halford G.: Low-Cycle Thermal Fatigue. Thermal Stresses II, ch. 6, pp. 330-428. Elsevier Science, Amsterdam (1987)Google Scholar
  20. 20.
    NTSB/AAR-90/06, PB90-910406, Aircraft accident report, UA 232, McDonnell Dougas DC-10-10, Sioux Gateway Airport, Sioux City, Iowa (July 19, 1989)Google Scholar
  21. 21.
    Gumbel, E.J.: Statistics of Extremes. Columbia University Press, N.Y (1958)MATHGoogle Scholar
  22. 22.
    Elliott, T. S.: East Coker in the Four Quartets, the Complete Poems and Plays- 1909- 1950, p. 128. Harcourt, Brace and World, Inc., N.Y (1971) Google Scholar
  23. 23.
    Costa, J., et al.: Titanium Rotating Components Review Team Report, USA FAA, Engine and Propellor Directorate, Burlington, MA (December 14, 1990)Google Scholar
  24. 24.
    ASTM, E 1823-10, Standard Terminology Relating to Fatigue and Fracture Testing, ASTM International, West Conshohocken, PA, USA (2010)Google Scholar
  25. 25.
    ASTM E2714 – 09, Standard Test Method for Creep-Fatigue Testing, International, West Conshohocken, PA, USA 9 (This test method is the responsibility of Subcommittee E08.05 on Cyclic Deformation and Crack Formation)Google Scholar
  26. 26.
    ASTM Standard Guide for Fretting Fatigue Testing ASTM E2789-10, International, West Conshohocken, PA, USAGoogle Scholar
  27. 27.
    Williams, Steve.: Associate Fellow - High temperature lifing, Critical Parts Lifing and Integrity, Rolls Royce Aeroengine Co., discussion at HOLSIP 10, Snowbird, UT (February 27, 2011)Google Scholar
  28. 28.
    Wood, W.A.: Four Basic Types of Metal Fatigue, Treatise in Materials Science and Technology, vol. 5, pp. 129–179. Academic Press, New York (1974)Google Scholar
  29. 29.
    Cameron, D.W., Jeal, R.H., Hoeppner, D.W.: SEM Investigations of Fatigue Crack Propagation in RR 58 Aluminum Alloy. Transactions of ASME, Journal of Engineering for Gas Turbines and Power 107, 238–241 (1985)CrossRefGoogle Scholar
  30. 30.
    Cameron, D.W., Jeal, R.H., Hoeppner, D.W.: SEM Investigations of Fatigue Crack Propagation in RR 58 Aluminum Alloy. Transactions of ASME, Journal of Engineering for Gas Turbines and Power 107, 238–241 (1985)CrossRefGoogle Scholar
  31. 31.
    Smith, F., Hoeppner, D.W.: Observations on Fatigue Crack Growth/Microstructure Interactions Using Advanced Techniques. In: Proceedings of the 16th Annual Meeting of IMS/ASM, Corrosion, Microstructure and Metallography, Microstructural Science, Northwood, White, and Vanderwoort ASM, Metals Park, OH, vol. 1, pp. 435–443 (1985)Google Scholar
  32. 32.
    Hoeppner, D.W., Sherman, I.: Fractographic Observations of Corrosion Fatigue and Fretting Fracture Surfaces. In: Corrosion, Microstructure and Metallography, Northwood, White, and Vanderwoort, pp. 117–125. American Society for Metals (1985)Google Scholar
  33. 33.
    Wu, D., Hoeppner, D.W.: Observations and Characterization Considerations of Fatigue Crack Growth in a Single Crystal Nickel-Base Superalloy. Scripta Metallurgica, vol. 19, pp. 493–498. Pergamon Press Ltd, USA (1985)Google Scholar
  34. 34.
    Smith, F., Hoeppner, D.W.: Observations on Fatigue Crack Growth/Microstructure Interactions Using Advanced Techniques. In: Proceedings of the 16th Annual Meeting of IMS/ASM Corrosion, Microstructure and Metallography, Microstructural Science, Northwood, White, Vanderwoort ASM, Metals Park, OH, pp. 435–443 (1985)Google Scholar
  35. 35.
    Smith, F.M., Hoeppner, D.W.: Quantitative Representation of Microstructural Contributions in Fatigue Crack Nucleation and Growth. In: The 1987 ASME Design Technology Conferences – 7th Biennial Conference of Failure and Prevention and Reliability, Boston, Mass, September 27-30 (1987); Published in Conference Proceedings, DE – Vol.9, pp. 87-90Google Scholar
  36. 36.
    Wu, D.C., Cameron, D.W., Hoeppner, D.W.: Observations of Microstructural and Geometrical Influences of Fatigue Crack Growth in Single Crystal and Polycrystal Nickel-Base Superalloys. In: Duhl, D.N., et al. (eds.) Superalloys 1988, AIME, pp. 605–614. The Metallurgical Society (1988)Google Scholar
  37. 37.
    Song, Z., Hoeppner, D.W.: Dwell Time Effects on Material Fatigue Behavior-Titanium Alloys. International Journal of Fatigue 10(4), 211–218 (1988)CrossRefGoogle Scholar
  38. 38.
    Stephens, R.R., Hoeppner, D.W.: A New Apparatus for Studying Fatigue Deformation at High Magnifications. Review of Scientific Instruments 59(8), 1412–1419 (1988)CrossRefGoogle Scholar
  39. 39.
    Stephens, R.R., Grabowski, L., Hoeppner, D.W.: Situ/SEM Studies of Short Crack Growth Behavior at Ambient and Elevated Temperature in a Nickel Base Superalloy. In: Miller, K.J., de los Rios, E.R. (eds.) Short Fatigue Cracks, ESIS, vol. 13, pp. 335–348. Mechanical Engineering Publications, London (1992)Google Scholar
  40. 40.
    Hoeppner, D.W.: History and Prognosis of Material Discontinuity Effects on Engine Components Structural Integrity. Published in Proceedings of 74th AGARD Structures and Materials Panel Meeting, Patras, Greece, May 25-29, 1992, AGARD Report No. 790, NATO-AGARD, Neuilly Sur Seine, France, Paper No. 1-1, pp. 1–8 (1993) (Invited keynote paper)Google Scholar
  41. 41.
    Elliott, C., Hoeppner, D.W.: A Fretting Fatigue System Usable In a Scanning Electron Microscope. In: International Conference on Fretting Fatigue, England, April 19. University of Sheffield, Sheffield (1993) ; Fretting Fatigue. In: ESIS, vol.18, pp. 211–218.Mechanical Engineering Publications, London (1994) Google Scholar
  42. 42.
    Stephens, R.R., Grabowski, L., Hoeppner, D.W.: The Effect of Temperature on the Behaviour of Short Fatigue Cracks in Waspaloy Using an In Situ SEM Fatigue Apparatus. International Journal of Fatigue 15(4), 273–282 (1993)CrossRefGoogle Scholar
  43. 43.
    Thomsen, M.L., Hoeppner, D.W.: Microstructurally Based Variations on the Dwell Fatigue Life of Titanium Alloy IMI 834. Presented at the FAA/NASA International Symposium on Advanced Structural Integrity Methods for Airframe Durability and Damage Tolerance, Part 2, Hampton, Virginia, May 4-6, vol. 3274, pp. 871–889. NASA Conference Publication (1994)Google Scholar
  44. 44.
    Elliott, III C. B., Hoeppner, D. W.: Fretting As a Fatigue Crack Nucleation Mechanism-A Close-up View. Presented at the USAF Conference on Structural Integrity (December 1997); published in the Conference ProceedingsGoogle Scholar
  45. 45.
    Taylor, A. M. H., Hoeppner, D. W.: The Effect of Prior Corrosion Damage on the Short Crack Growth Rates of Two Aluminum Alloys. Presented at the USAF conference on Structural Integrity (December 1997); published in the Conference ProceedingsGoogle Scholar
  46. 46.
    Thomsen, M.L., Hoeppner, D.W.: The Effect of Dwell Loading on the Strain Accumulation Behavior of Titanium Alloys. International Journal of Fatigue 20(4), 309–317 (1998)CrossRefGoogle Scholar
  47. 47.
    Okada, T., Hoeppner, D.W.: The Behavior of Short Cracks in Corrosive Environments for 7075 Al Alloy. In: Donne, C.D. (ed.) Proceedings of the 23rd Symposium of the International Committee on Aeronautical Fatigue, Presented at ICAF 2005 Structural Integrity of Advanced Aircraft and Life Extension for Current Fleets - Lessons Learned in 50 Years after the Comet Accidents, Hamburg, Germany, vol. 2, pp. 613–622 (2005)Google Scholar
  48. 48.
    Smiltneek, L., Shinde, S., Hoeppner, D.: A Single Cylinder In-Situ SEM Fatigue System. Review of Scientific Instruments, American Institute of Physics 77, 1–4 (2006)Google Scholar
  49. 49.
    Hoeppner, D.W.: From No-life to safe life to HOLISTIC Structural Integrity Based Design. Invited Presentation and Paper for the workshop on Structures, Materials, and Propulsion, Held at National Research Council-Canada, Ottawa, Ontario, Canada (July 2002); published in the workshop proceedingsGoogle Scholar
  50. 50.
    Brooks, C. et al.: AP/ES, http://apesolutions.com/; There are many relevant publications
  51. 51.
  52. 52.
    Yamagiwa, K., Kataoka, S., Izumi, S., Sakai, S.: Measurement of Three Dimensional Geometry of Creep Void and Grain Boundary with Combining 3D-EBSD Method and SEM Images. Trans. of Japan Society of Mech. Eng. (A) 76(772), 1799–1805Google Scholar
  53. 53.
    Yamagiwa, K.: Evolution of Creep Damage. Presentation at HOLSIP 10 held in Snowbird, UT (February 27-March 3, 2011)Google Scholar

Copyright information

© Springer-Verlag Berlin Heidelberg 2011

Authors and Affiliations

  • David W. Hoeppner
    • 1
  1. 1.Mechanical EngineeringU. of UtahSalt Lake City

Personalised recommendations