Advances in Superconductivity pp 341-345 | Cite as
Preparation of Superconducting Thick Films of Y-Ba-Cu-O by Gas Deposition of Ultrafine Powder
Conference paper
Abstract
Superconducting thick(∿20 μm) films of YBd2Cu3Ox have been successfully made by gas deposition of ultrafine(<0.1 μm) powder of Y, Ba and Cu on MgO substrates. After high temperature anneal, films are superconducting with Tc ∿76 K and ΔTc ∿5 K. Because of excellent sintering properties of ultrafine powder, critical current densities are relatively large (in excess of 10000A/cm2 at 4.2 K) and resistivities at room temperature are about 0.3 mΩcm.
Keywords
Thick Film Critical Current Density Deposition Chamber Oxide Superconductor Heat Treated Sample
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
Preview
Unable to display preview. Download preview PDF.
References
- [1]J. B. Bedonorz and K. A. Muller: Z. Phys. B64 (1986) 189ADSCrossRefGoogle Scholar
- [2]Y. Enomoto, T. Murakami, M. Suzuki and K. Moriwaki: Jpn. J. Appl. Phys. 26 (1987) L1248ADSCrossRefGoogle Scholar
- [3]T. Terashima, K. Iijima, K. Yamamoto, Y. Bando and H. Mazaki: Jpn. J. Appl. Phys. 27(1988) L91ADSCrossRefGoogle Scholar
- [4]H. Koinuma, T. Hashimoto, T. Nakamura, K. Kishio, K. Kitazawa and K. Fueki: Jpn. J. Appl. Phys. 26 (1987) L761ADSCrossRefGoogle Scholar
- [5]K. Terashima, K. Eguchi, T. Yoshida and K. Akashi: Appl. Phys. Lett. 52(1988) 1274ADSCrossRefGoogle Scholar
- [6]S. Shibata, T. Kitazawa, H. Okazaki and T. Kimura: Jpn. J. Appl. Phys. 27 (1988) L646ADSCrossRefGoogle Scholar
- [7]S. Kashu, E. Fuchita, T. Manabe and C. Hayashi: Jpn. J. Appl. Phys. 23 (1984) L910ADSCrossRefGoogle Scholar
- [8]C. Hayashi: PHYSICS TODAY, December 1987, 1Google Scholar
- [9]LAKE SHORE CRYOTRONICS, INC., Model PT-103Google Scholar
- [10]VACUUM METALLURGICAL CO.LTD., Model TC-201MGoogle Scholar
Copyright information
© Springer Japan 1989