Growth of Beta Phase Gallium Oxide Nanostructures on Sapphire Substrate by Chemical Vapour Deposition

  • Thangaraj RajeshEmail author
  • Ganapathy SasikalaEmail author
  • Subramanian Sumathi
  • Subramanian Suguna
Conference paper
Part of the Springer Proceedings in Physics book series (SPPHY, volume 215)

Abstract

In the present research work growth of gallium oxide nanostructures on sapphire substrates using chemical vapour deposition method at different growth time intervals is reported. A thin layer of nickel was initially sputtered on the sapphire substrates, which act as the catalyst to assist the growth. Gallium metal and water vapour were used as the precursors in the presence of nitrogen carrier gas. As grown samples were characterized to observe the changes in their structural, optical and morphological properties by Powder X-Ray Diffraction (XRD), Diffused Reflectance Spectroscopy (DRS) and Scanning Electron Microscopy (SEM) respectively. XRD results were matched with previously reported studies confirming the formation of single phase β-Ga2O3. The bandgaps were calculated, its shows the value from 4.55 eV to 4.66 eV. SEM images show the formation of nano-sheet and wires. EDX and elemental mapping revealed that growth was uniform over the sample.

References

  1. 1.
    S. Kumar, Self-catalytic growth of β-Ga2O3 nanostructures by chemical vapor deposition. Adv. Eng. Mater. (2014)Google Scholar
  2. 2.
    M. Kumar, Diameter tuning of β-Ga2O3 nanowires using chemical vapor deposition technique. Nanoscale Res. Lett. 12, 184 (2017)Google Scholar
  3. 3.
    S. Kumar, Nanofunctional gallium oxide (Ga2O3) nanowires/nanostructures and their applications in nanodevices. Phys. Status Solidi RRL 7(10), 781–792 (2013)ADSCrossRefGoogle Scholar
  4. 4.
    X. Xiang, Synthesis and photoluminescence of gallium oxide ultra-long nanowires and thin nanosheets. J. Crys. Growth 279, 122–128 (2005)ADSCrossRefGoogle Scholar
  5. 5.
    R. Jangir, Photoluminescence study of β-Ga2O3 nanostructures annealed in different environments. J. Appl. Phys. 112, 034307 (2012)ADSCrossRefGoogle Scholar
  6. 6.
    A.E. Morales et al., Use of diffuse reflectance spectroscopy for optical characterization of un-supported nanostructures. Revista Mexicana De Física S 53 (5) 18–22 (2007)Google Scholar
  7. 7.
    M. Orita, Deep-ultraviolet transparent conductive thin films. Appl. Phys. Lett. 77(25), 18 (2000)ADSCrossRefGoogle Scholar

Copyright information

© Springer Nature Switzerland AG 2019

Authors and Affiliations

  1. 1.Crystal Growth Centre, Anna UniversityChennaiIndia

Personalised recommendations