Chemical Resistance of Vinyl-Ester Concrete with Waste Mineral Dust Remaining After Preparation of Aggregate for Asphalt Mixture

Conference paper

Abstract

The aim of the research was to test the ability of vinyl-ester concrete containing waste powder to resist chemical attacks of sulfuric acid and sodium hydroxide. Tested composites contained mineral dust remaining after preparation of aggregates for mineral-asphalt composites. It was experimentally confirmed that from the point of view of chemical composition, granulometry, specific surface area, and density, the waste dust appeared to be a good substitute for commercial quartz powder used in polymer concrete. The evaluation of chemical resistance of polymer concrete with waste dust was done in terms of mass loss and change in compressive strength of composite after its exposition to aggressive media. The tests were performed according to the modified method described in guidelines for the precast elements production. Analysis of test results showed that even the high substitution of quartz powder with waste mineral dust (up to ~85%) in vinyl-ester concrete is possible and such composite presents high mechanical properties (though in some cases it requires using larger amounts of polymer) – not much worse than in case of non-modified composites.

References

  1. 1.
    Bignozzi, M. C., Saccani, A., & Sandrolini, F. (2004). Glass waste valorization in advanced composite materials. In Proceedings of the 11th int. congress on polymers in concrete – ICPIC ‘04 (pp. 587–595). Berlin.Google Scholar
  2. 2.
    Varughese, K. T., & Chaturvedi, B. K. (1996). Fly ash as fine aggregate in polyester based polymer concrete. Cement & Concrete Composites, 18, 105–108.CrossRefGoogle Scholar
  3. 3.
    Gorninski, J. P., Dal Molin, D. C., & Kazmierczak, C. S. (2007). Strength degradation of polymer concrete in acidic environments. Cement & Concrete Composites, 29, 637–645.CrossRefGoogle Scholar
  4. 4.
    Harja, M., Bărbuţă, M., & Rusu, L. (2009). Obtaining and characterization of the polymer concrete with fly ash. Journal of Applied Sciences, 9, 88–96.CrossRefGoogle Scholar
  5. 5.
    Łukowski, P., Sokołowska, J. J., Adamczewski, G., & Jaworska, B. (2013). Waste perlite powder as the potential microfiller of polymer composites. Mechanics and Materials, 1, 201–211.Google Scholar
  6. 6.
    Łukowski, P., & Salih, A. (2015). Durability of mortars containing ground granulated blast-furnace slag in acid and sulphate environment. Procedia Engineering, 108, 47–54.CrossRefGoogle Scholar
  7. 7.
    Jaworska, B., Sokołowska, J. J., Łukowski, P., & Jaworski, J. (2015). Waste mineral powders as a components of polymer-cement composites. Archives of Civil Engineering, 61(4), 199–210.CrossRefGoogle Scholar
  8. 8.
    Czarnecki, L., Garbacz, A., & Sokołowska, J. J. (2010). Fly ash polymer concretes. In Proceedings of the 2nd international conference on sustainable construction materials and technologies (pp. 28–30). Ancona.Google Scholar
  9. 9.
    Garbacz, A., & Sokołowska, J. (2010). Effect of calcium fly ash on PC properties. In Proceedings of the 13th international congress on polymers in concrete – ICPIC 2010 (pp. 281–288). Funchal-Madeira.Google Scholar
  10. 10.
    Garbacz, A., & Sokołowska, J. J. (2013). Concrete-like polymer composites with fly ashes – Comparative study. Construction and Building Materials, 38, 689–699.CrossRefGoogle Scholar
  11. 11.
    Sokołowska, J. J., Woyciechowski, P., Łukowski, P., & Kida, K. (2015). Effect of perlite waste powder on chemical resistance of polymer concrete composites. Advanced Materials Research, 1129, 516–522.CrossRefGoogle Scholar
  12. 12.
    Sokołowska, J. J. (2016). Technological properties of polymer concrete containing vinyl-ester resin waste mineral powder. Journal of Building Chemistry, 1(1), 84–91.Google Scholar
  13. 13.
    Czarnecki, L., & Sokołowska, J. J. (2011). Optimization of polymer-cement coating composition using material model. Key Engineering Materials, 466, 191–199.CrossRefGoogle Scholar
  14. 14.
    Czarnecki, L., & Sokołowska, J. J. (2015). Material model and revealing the truth. Bulletin of the Polish Academy of Sciences Technical Sciences, 63, 7–14.Google Scholar
  15. 15.
    Kępniak, M., Woyciechowski, P., & Franus, W. (2017). Chemical and physical properties of the waste limestone powder as a potential microfiller of polymer composites. Archives of Civil Engineering, 2(53), 67–78.Google Scholar

Copyright information

© Springer International Publishing AG, part of Springer Nature 2018

Authors and Affiliations

  • Joanna J. Sokołowska
    • 1
  • Piotr P. Woyciechowski
    • 1
  1. 1.Warsaw University of Technology, Faculty of Civil EngineeringWarsawPoland

Personalised recommendations