Superplasticity in a Chip-Consolidated Mg97Zn1Y2 Alloy with LPSO Phase

  • Kazuha Suzawa
  • Shin-ichi Inoue
  • Michiaki YamasakiEmail author
  • Yoshihito Kawamura
  • Michimasa Miyanaga
  • Katsuhito Yoshida
  • Nozomu Kawabe
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Novel Mg97Zn1Y2 alloy of equiaxed fine grains with long-period stacking ordered (LPSO) phase was prepared by consolidation of chips machined from a twin-roll-cast alloy. The chip-consolidated Mg97Zn1Y2 alloy exhibited superplasticity at a wide initial strain-rate ranging from 1 × 10−3 to 3 × 10−1 s−1 at temperatures of 623 and 673 K. The maximum elongation was approximately 560% at 3 × 10−2 s−1 at 673 K. The strain rate sensitivity index (m-values) was shown to be greater than 0.3 in this study; this value seems to be large enough to ensure uniform elongation during superplastic deformation. SEM/EBSD measurements revealed that the chip-consolidated Mg97Zn1Y2 alloy was composed of mixed equiaxed fine-grains of α-Mg and LPSO phases of a mean size of ~1 μm. The grain boundary sliding in the equiaxed fine-grains appears to account for most of the mechanism of superplastic deformation in this alloy.

Keywords

Mg–Zn–Y Long-period stacking ordered phase Chip consolidation Superplasticity 

Notes

Acknowledgements

This study is supported by grants-in-aid for Scientific Research(A) No. 16H02404 and (B) No. 17H03431 from the MEXT Japan, and by the Sumitomo Electric Industries, Ltd. Endowed Chair in Kumamoto University.

References

  1. 1.
    Aghion E, Bronfin B, Von Buch F, Schumann S, Friedrich H (2003) Newly developed magnesium alloys for powertrain applications, JOM 55(11) 30–33.Google Scholar
  2. 2.
    Easton M, Beer A, Barnett M, Davies C, Dunlop G, Durandet Y, Blacket S, Hilditch T, Beggs P (2008) Magnesium alloy applications in automotive structures, JOM 60(11) 57–62.Google Scholar
  3. 3.
    Kawamura Y, Hayashi K, Inoue A, Masumoto T (2001) Rapidly solidified powder metallurgy Mg97Zn1Y2 alloys with excellent tensile yield strength above 600 MPa, Mater. Trans. 42(7) 1172–1176.Google Scholar
  4. 4.
    Abe E, Kawamura Y, Hayashi K, Inoue A (2002) Acta Mater. 50(15) 3845–3857.Google Scholar
  5. 5.
    Egusa D, Abe E (2012) The structure of long period stacking/order Mg–Zn–RE phases with extended non-stoichiometry ranges, Acta Mater. 60(1) 166–178.Google Scholar
  6. 6.
    Yoshimoto S, Yamasaki M, Kawamura Y (2006) Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloys with 14H Long Period Ordered Structure, Mater. Trans. 47(4) 959–965.Google Scholar
  7. 7.
    Hagihara K, Kinoshita A, Sugino Y, Yamasaki M, Kawamura Y, Yasuda HY, Umakoshi Y (2010) Effect of long-period stacking ordered phase on mechanical properties of Mg97Zn1Y2 extruded alloy, Acta Mater. 58(19) 6282–6293.Google Scholar
  8. 8.
    Yamasaki M, Hashimoto K, Hagihara K, Kawamura Y (2011) Effect of Multimodal Microstructure Evolution on Mechanical Properties of Mg-Zn-Y Extruded Alloy, Acta Mater. 59(9) 3646–3658.Google Scholar
  9. 9.
    Jono Y, Yamasaki M, Kawamura Y (2013) Effect of LPSO Phase-Stimulated Texture Evolution on Creep Resistance of Extruded Mg-Zn-Gd Alloys, Mater. Trans. 54(5) 703–712.Google Scholar
  10. 10.
    Jono Y, Yamasaki M, Kawamura Y (2015) Quantitative evaluation of creep strain distribution in an extruded Mg-Zn-Gd alloy of multimodal microstructure, Acta Materialia, 82(1) 198–211.Google Scholar
  11. 11.
    Pilling J, Ridley N (1989) Superplasticity in Crystalline Solids, The Institute of Metals, Maney Publishing, London.Google Scholar
  12. 12.
    Abu-Farha F, Curtis R (2011) Standard for superplastic forming of metals. in Giuliano G (ed) Superplastic forming of advanced metallic materials, Method and applications. Woodhead Publishing Limited, Cambridge, pp. 34–48.Google Scholar
  13. 13.
    Clarisse L, Bataille A, Pennec Y, Crampon J, Duclos R (1999) Investigation of grain boundary sliding during superplastic deformation of a fine-grained alumina by atomic force microscopy Ceram. Inter. 25(4) 389–394.Google Scholar
  14. 14.
    Mukai T, Watanabe H, Higashi K (2000) Application of superplasticity in commercial magnesium alloy for fabrication of structural components, Mater. Sci. Tech. 16(11–12) 1314–1319.Google Scholar
  15. 15.
    Yamasaki M, Hagihara K, Inoue S, Hadorn JP, Kawamura Y (2013) Crystallographic classification of kink bands in an extruded Mg–Zn–Y alloy using intragranular misorientation axis analysis, Acta Mater. 61(6) 2065–2076.Google Scholar
  16. 16.
    Fudetani S, Itoi T, Kubo T, Kawamura Y, Hirohashi M (2009) Microstructures and Mechanical Properties of Mg96Zn2Y2 Alloy Prepared by Extrusion of Machined Chips, Mater. Trans. 50(2) 349–353.Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2018

Authors and Affiliations

  • Kazuha Suzawa
    • 1
    • 2
  • Shin-ichi Inoue
    • 1
  • Michiaki Yamasaki
    • 1
    Email author
  • Yoshihito Kawamura
    • 1
  • Michimasa Miyanaga
    • 2
  • Katsuhito Yoshida
    • 2
  • Nozomu Kawabe
    • 2
  1. 1.Magnesium Research Center, Department of Materials ScienceKumamoto UniversityKumamotoJapan
  2. 2.Magnesium Alloy Development DivisionSumitomo Electric Industries, Ltd.Itami-shiJapan

Personalised recommendations