Effectiveness of Application of Additional Strengthening Processing of Surface Plastic Deformation on Increase in Fatigue Life of Parts

  • V. A. LebedevEmail author
  • A. V. Kirichek
  • L. V. Chunakhova
Conference paper
Part of the Lecture Notes in Mechanical Engineering book series (LNME)


The paper presents the results of experimental studies of the effect of additional surface plastic deformation hardening on increasing the fatigue life of parts. Hardening by the surface plastic deformation method leads to surface hardening, to the formation of details of residual stresses of compression in the surface layers, and to the favorable change of microgeometry of surfaces, which result in the increase in their fatigue and contact resistance, wear resistance, and corrosion resistance depending on the functional purpose and an external environment of details. The conducted pilot studies provided reasons for the modes of the vibroshock hardening processing of samples and determination of fatigue longevity of the samples strengthened according to five regulations. It is shown that the application of a single additional vibroshock hardening after intermediate cyclic loading (training) contributes to an increase in the fatigue life of the sample approximately by 1.2 times; double additional vibroshock hardening of samples in combination with a double intermediate cyclic loading increases fatigue durability of samples by 1.1 times; post-deformation rest of the samples has no significant effect on increase in a fatigue longevity that is caused by a stress relief or a softening in the course of aging. It has been specified that additional hardening of parts during operation will have effect under the condition that the degree of hardening of the surface layer provided by the surface plastic deformation does not exceed the maximum permissible value peculiar to a particular material.


Hardening Plastic deformation Fatigue life 


  1. 1.
    Babichev AP, Babichev EA (1999) Basic concepts of vibration technology. Don State Technical University, Rostov-on-Don, 620 pGoogle Scholar
  2. 2.
    Boitsov VB (2005) Technological methods to increase strength and service life. Mashinostroenie, Moscow, 128 pGoogle Scholar
  3. 3.
    Chuchukalov AP (2006) Application of vibration technologies to increase the surface quality and service properties of parts. Don state Technical University, Rostov-on-Don, 215 pGoogle Scholar
  4. 4.
    Kirichek AV, Solovyev DL, Lazutkin AG (2004) Technology and equipment of staticopulse machining by surface plastic deformation. Mashinostroenie, Moscow, 287 pGoogle Scholar
  5. 5.
    Kopilov YR (1999) Shock-vibrating hardening. Institute of Russian Ministry of Home Affairs, Voronezh, 386 pGoogle Scholar
  6. 6.
    Koval NS (2011) Increasing fatigue limit of long complex parts. Problems of vibration technology. In: Proceedings of international seminar application of low-frequency vibrations for technological purposes, Rostov-on-DonGoogle Scholar
  7. 7.
    Lebedev VA (2006) Technology of dynamic methods of surface plastic deformation. Don State Technical University, Rostov-on-Don, 183 pGoogle Scholar
  8. 8.
    Motrenko PD, Prokopets GA, Babichev AP (2003) Shock processes of part vibrating hardening, by surface plastic deformation. Voprosi Vibratsionnoy Tekhologii, Rostov-on-Don, pp 9–11Google Scholar
  9. 9.
    Motrenko PD, Pastukhov FA, Maksimov DV, Vovchenko SV (2018) Premises of using additional surface plastic strain hardening to increase fatigue life of parts. In: Knowledge-intensive and vibtowaving technologies of processing Hi-tech parts. Collection of papers. Don State Technical University, pp 97–99Google Scholar
  10. 10.
    Suslov AG (2006) Engineering support and increasing service properties of parts and their assemblies. Mashinostroenie, Moscow, 447 pGoogle Scholar
  11. 11.
    Lebedev VA (2007) Energetic aspects of parts strengthening by dynamic methods of surface plastic deformation. Don State Technical University, Rostov-on-Don, 156 pGoogle Scholar
  12. 12.
    Ivanova VS (1975) Nature of metal fatigue. Metallurgy, Moscow, 272 pGoogle Scholar
  13. 13.
    Fedorov VV (1985) Kinetics of damageability and destruction of solids. Publishing House FAN, Tashkent, 168 pGoogle Scholar
  14. 14.
    Kirichek AV, Solovyev DL (2001) Kuznechno-Shtampovochnoe Proizvodstvo (Obrabotka Metallov Davleniem). N Engl J Med 7:28–32Google Scholar
  15. 15.
    Kirichek AV, Solovyev DL (2002) Kuznechno-Shtampovochnoe Proizvodstvo (Obrabotka Metallov Davleniem). N Engl J Med 10:35–40Google Scholar
  16. 16.
    Kirichek AV, Solovyev DL (2004) Kuznechno-shtampovochnoe proizvodstvo (obrabotka metallov davleniem). N Engl J Med 2:13–17Google Scholar
  17. 17.
    Kirichek AV, Solovyev DL (2008) Russ Eng Res 28. J Mol Med 3:277–279.
  18. 18.
    Kirichek AV, Soloviev DL (2013) J Nano Electron Phys 5. J Mol Med 4:04009 (4p)Google Scholar
  19. 19.
    Kirichek AV, Soloviev DL (2013) J Nano Electron Phys 5. J Mol Med 4:04010 (5p)Google Scholar
  20. 20.
    Kirichek AV, Soloviev DL (2014) J Nano Electron Phys 6. J Mol Med 3:03069 (4p)Google Scholar
  21. 21.
    Kirichek AV, Soloviev DL, Lazutkin AG, Silantiev SA (2002) STIN. N Engl J Med 5:13–15Google Scholar

Copyright information

© Springer Nature Switzerland AG 2020

Authors and Affiliations

  • V. A. Lebedev
    • 1
    Email author
  • A. V. Kirichek
    • 2
  • L. V. Chunakhova
    • 1
  1. 1.Don State Technical UniversityRostov-on-DonRussia
  2. 2.Bryansk State Technical UniversityBryanskRussia

Personalised recommendations