Testing of Copper Based Journal Bearing Fabricated with Powder Metallurgy Method

  • Abhay A. UtpatEmail author
  • S. B. Bhosale
  • Mahesh P. Kamble
Conference paper

Abstract

Journal bearings can be manufactured by several manufacturing processes such as PM, casting, coating and so on. In the presented research PM process has been selected, although the developed compositions can be manufactured with other manufacturing processes. Powder metallurgy is the manufacturing science of producing solid parts of desired geometry and material from powders. Powders are compacted into certain geometry then heated, (sintered), to solidify the part. Nowadays lead-free bronze based and copper based composites with the newly developed Tribology alloy additives are being used for manufacturing of Journal Bearing material. Hence, this project is aimed to develop copper-based journal bearing materials with Graphite as additive. The copper is added with 9% & 10% tin in addition with graphite percentage 1% & 1.5%. The specimens are fabricated using the powder metallurgy (PM) and isostatic pressing & then sintered in a Nitrogen environment. The tests were performed on the fabricated specimen’s viz. microstructure test, hardness test, density test, braking load. The microstructure shows more amount of Graphite increases porosity also, increase in the amount of Graphite leads to a decline in hardness. The effect of more Graphite amount decreases the breaking load capacity & density of the material. The experimental results show that the composition Cu-90-10Sn-1%Graphite has greater strength.

Keywords

Journal braring Copper powder Powder metallurgy Testing 

References

  1. 1.
    Hirotaka Kato, Masahiro Takama, Yoshiro Iwai, Kazuo Washida, Yoshinori Sasaki (2013) Wear and mechanical properties of sintered copper-tin composities containing graphite or molybdenum disulfide. Published in ELSEVIERGoogle Scholar
  2. 2.
    Khoei AR, Keshavarz S, Biabanaki SOR (2010) Optimal design of powder compaction processes via genetic algorithm technique. Finite Elem Anal Des 46(10):843–861CrossRefGoogle Scholar
  3. 3.
    Olsson M, Bexell U (2011) Friction characteristics and material transfer tendency in metal powder compaction. Wear 271(9–10):1903–1908CrossRefGoogle Scholar
  4. 4.
    Mori K, Maki S, Tanaka Y (2005) Warm and hot stamping of ultra high tensile strength steel sheets using resistance heating. CIRP Ann Manuf Technol 54(1):209–212CrossRefGoogle Scholar
  5. 5.
    Arash Tavakoli (2007) Development of tin-bronze and copper based journal bearing materials with tribaloy alloy additives. A thesis submitted to the Faculty of Graduate Studies and Research, Department of Mechanical and Aerospace Engineering Carleton University Ottawa, Ontario Canada on August 2007Google Scholar
  6. 6.
    Marinković A (2005) Structural optimization of journal porous metal bearing. FME Trans 33(1):25–31Google Scholar

Copyright information

© Springer Nature Switzerland AG 2020

Authors and Affiliations

  • Abhay A. Utpat
    • 1
    Email author
  • S. B. Bhosale
    • 1
  • Mahesh P. Kamble
    • 2
  1. 1.Department of Mechanical EngineeringSVERI’s College of Engineering PandharpurPandharpurIndia
  2. 2.Specialty Sintered Pvt. Ltd., ShirvalPuneIndia

Personalised recommendations