Selection of Materials Exposed to High Flow Velocities

  • Johann Friedrich GülichEmail author
Chapter

Abstract

Degradation or failures of materials due to fatigue, corrosion, abrasion and cavitation erosion time and again cause costly problems to pump operators. This could be avoided in most cases by a careful material selection. Frequently one of two causes can be made responsible for a wrong material selection: (1) the corrosive properties of the liquid pumped are not clearly specified (or are unknown), or (2) for cost reasons (competitive pressure) the least expensive material is chosen which appears just to be able to do the job.

References

  1. 1.
    ASM Handbook volume 13A, Corrosion: Fundamentals, Testing, and Protection. ASM International (2003). ISBN 0-87170-705-5 (2003)Google Scholar
  2. 2.
    Berger, C., Schlücker, E.: Untersuchungen zur verbesserten Auslegung von Bauteilen aus Duplexstahle oder Superaustenit unter Schwingungsrisskorrosionsbelastung in wässrigen Medien. AiF report 13248 N (2005)Google Scholar
  3. 3.
    Berten, S.: Hydrodynamics of High Specific Power Pumps for Off-Design Operating Conditions. Diss, EPF Lausanne (2010)Google Scholar
  4. 4.
    Bolliger, W.: Advancements in Material Technologies For Longer Life When Pumping Difficult Liquids. Proc Indian Pump Manufacturers Association, Mumbai (2001)Google Scholar
  5. 5.
    Brendel, H., Dwars, A.: Neue Anwendungsgebiete für Umwälzpumpen in der Industrie- und Verfahrenstechnik. Industriepumpen und Kompressoren 1, 20–26 (1999)Google Scholar
  6. 6.
    Bursik, A.: Vergleichende Untersuchungen zur Konditionierung von Kesselspeisewasser. VGB-Konferenz Chemie im Kraftwerk (1981)Google Scholar
  7. 7.
    Cooper, P., et al.: Reduction of cavitation damage in a high-energy water injection pump. ASME AJK2011–06092Google Scholar
  8. 8.
    Dechema Werkstofftabellen E 40 für Meerwasser (1998)Google Scholar
  9. 9.
    Effertz, P.H., Forchhammer, P., Hickling, J.: Spannungsrißkorrosionsschäden an Bauteilen in Kraftwerken – Mechanismen und BeispieleGoogle Scholar
  10. 10.
    Galsterer, D., Heimgartner, P.: Analyzing and effectively avoiding corrosion. Sulzer Tech. Rev. 1, 22–25 (2013)Google Scholar
  11. 11.
    Grein, H., Krause, M.: Research and prevention of hydroabrasive wear. In: XVII IAHR Symposium, Beijing (1994)Google Scholar
  12. 12.
    Grein, H., Schachenmann, A.: Abrasion an Maschinen hydraulischer Kraftwerke. Sulzer Techn. Rundsch. 1/92Google Scholar
  13. 13.
    Gülich, J.F.: Bedeutung der thermohydraulischen Verhältnisse für die Korrosionssicherheit von DWR-Dampferzeugern. Atomwitschaft 2, 82–87 (1975)Google Scholar
  14. 14.
    Gülich, J.F.: Abtragsraten bei der Erosionskorrosion unlegierter Stähle in Kesselspeisewasser. Techn. Rundsch. Sulzer. 4, 19–22 (1986)Google Scholar
  15. 15.
    Gülich, J.F.: Calculation of metal loss under attack of erosion-corrosion or cavitation erosion. In: International Conference on Advances in Material Technology Fossil Power Plants. Chicago (1987)Google Scholar
  16. 16.
    Gülich, J.F., et al.: L’érosion-corrosion dans les pompes d’alimentation et d’extraction. Colloque EdF “Chimie de 1’eau et corrosion, Seillac (1980)Google Scholar
  17. 17.
    Gülich, J.F., Bolleter, U.: Pressure pulsations in centrifugal pumps. ASME J. Vibr. Acoust. 114, 272–279 (1992)CrossRefGoogle Scholar
  18. 18.
    Günther, R., Knapp, P., Scherrer, G.: Erfahrungen über die Beständigkeit verschiedener Werkstoffe gegenüber hydroabrasivem Verschleiß in Kalksteinsuspensionen. Pumpentagung Karlsruhe, C8 (1988)Google Scholar
  19. 19.
    Hagen, M., Bolliger, W., Schöffler, W.: Influence of fluoride in chloride-containing FGD suspensions on the corrosion of duplex stainless steel. Vortrag DECHEMA (1997)Google Scholar
  20. 20.
    Heil, K.: Erosionskorrosion an unlegierten Fe-Werkstoffen in schnellströmenden Wässern. Dissertation, TH Darmstadt (1979)Google Scholar
  21. 21.
    Heimgartner, P., Schöffler, W., Bitterwolf, F.: Kreiselpumpen in Rauchgas-Entschwefelungsanlagen. Techn Rundsch. Sulzer. 3, 13–19 (1987)Google Scholar
  22. 22.
    Heitmann, H.G., et al.: Erosionskorrosion in Wasser-Dampfkreisläufen. VGB-Konferenz Chemie im Kraftwerk (1981)Google Scholar
  23. 23.
    Heitz, E., Litzkendorf, M., Meysenburg, C.M., Weber, J.: Das Verhalten rostfreier Stahlgußlegierungen unter gleichzeitiger mechanischer und korrosiver Belastung. Z Werkstofftechnik. 11, 244–258 (1980)CrossRefGoogle Scholar
  24. 24.
    Held, H.D.: Zur Frage der Magnetitablagerungen in Zwangsdurchlaufkesseln. VGB Kraftwerkstech. 54(6), 406–408 (1974)Google Scholar
  25. 25.
    Heubner, U., et al.: Nickelwerkstoffe und hochlegierte Sonderedelstähle, 2. Aufl., Bd. 153. Kontakt & Studium Werkstoffe, expert verlag. ISBN 3-8169-1011-4 (1993)Google Scholar
  26. 26.
    Heumann, A.: Konstruktive Gestaltung von Spiralgehäusepumpen sowie Werkstoffauswahl für schleißendes Fördergut. Pumpentagung Karlsruhe, A3-03 (1992)Google Scholar
  27. 27.
    Höppel, H.W.: Schädigungsmechanismen und hydroabrasives Verschleißverhalten unterschiedlicher Hartstoffsysteme. Dissertation Universität Erlangen-Nürnberg (1997)Google Scholar
  28. 28.
    Hutchings, L.M.: Tribology, Friction and Wear of Engineering Materials. Edward Arnold. ISBN 0-340-56184-x (1992)Google Scholar
  29. 29.
    Kaesche, H.: Die Korrosion der Metalle. Springer, Berlin (1990)Google Scholar
  30. 30.
    Kastner, W., Riedle, K., Tratz, H.: Untersuchungen zum Materialabtrag bei Erosionskorrosion. VGB Kraftwerkstech. 64(5), 452–465 (1984)Google Scholar
  31. 31.
    Kastner, W., Hofmann, P., Nopper, H.: Erosionskorrosion in Kraftwerksanlagen – Entscheidungshilfe für Maßnahmen zur Schadensvermeidung. VGB Kraftwerkstech. 70(11), 939–948 (1990)Google Scholar
  32. 32.
    Keller, H.: Erosionskorrosion an Naßdampfturbinen. VGB Kraftwerkstech. 54(5), 292–295 (1974)Google Scholar
  33. 33.
    Kießling, R.: Zur Modellierung und Simulation des hydroabrasiven Verschleißes ringförmiger Strömungsspalte. Dissertation Universität Erlangen-Nürnberg (1994)Google Scholar
  34. 34.
    Knapp, P., et al.: Werkstoffe für Pumpen in der Rauchgasentschwefelung – Langzeiterfahrungen und neue Entwicklungen. Pumpentagung Karlsruhe A2-01 (1992)Google Scholar
  35. 35.
    Kovach, C.W.: High performance stainless steels. NiDI Reference book Series 11021, Nickel Development InstituteGoogle Scholar
  36. 36.
    Kratzer, A., Tischner, H.: Noridur 9.4460, ein ferritisch-austenitischer CrNiMo-Stahlguß für Pumpen und Armaturen in Rauchgasentschwefelungsanlagen. KSB Techn Berichte 18Google Scholar
  37. 37.
    Kunze, E. (Hrsg): Korrosion und Korrosionsschutz, 6 Bände. Wiley. ISBN 3-527-29994-7 (2001)Google Scholar
  38. 38.
    Landolt, B.: Zahlenwerte und Funktionen, 6. Auflage, Bd. 2, Teil 5a, S. 575 (1969)Google Scholar
  39. 39.
    Materials for saline water, desalination and oilfield brine pumps. NiDI Reference book No 11004, 2nd edn. Nickel Development Institute (1995)Google Scholar
  40. 40.
    Naidu, B.S.K.: Silt erosion problems in hydro power stations and their possible solutions. Workshop on silt damages in hydro power stations, New Delhi (1996)Google Scholar
  41. 41.
    Offenhäuser, H.: Druckschwankungsmesssungen an Kreiselpumpen mit Leitrad. VDI Ber. 193, 211–218 (1973)Google Scholar
  42. 42.
    Palgrave, R.: Personal communicationGoogle Scholar
  43. 43.
    Pini, G., Weber, J.: Werkstoffe für die Förderung von Meerwasser und hochchloridhaltigen Medien. Techn. Rundsch. Sulzer. 2, 69–80 (1979)Google Scholar
  44. 44.
    Plant, W.H.D., Mathay, W.L.: Nickel-Containing Materials in Flue Gas Desulphurisation Equipment. Nickel Development InstituteGoogle Scholar
  45. 45.
    Practical Guidelines for the Fabrication of Duplex Stainless Steels. Intl Molybdenum Association, Nickel Development Institute (2001)Google Scholar
  46. 46.
    Radke, M., et al.: Neue konstruktive Entwicklungen für Kreiselpumpen in Rauchgasentschwefelungsanlagen. Konstruktion 42, 53–60 (1990)Google Scholar
  47. 47.
    Radke, M., et al.: Untersuchung kostenbestimmender Faktoren bei Kreiselpumpen in Rauchgasentschwefelungsanlagen. VGB Kraftwerkstech. 71, 455–461 (1991)MathSciNetGoogle Scholar
  48. 48.
    Roark, R.J., Young, W.C.: Formulas for Stress and Strain, 5th edn. McGraw-Hill (1986)Google Scholar
  49. 49.
    Schläpfer, H.W., Weber, J.: Austenitic-Ferritic Duplex Steels. Material und Technik 14 H 2 (1986)Google Scholar
  50. 50.
    Sedricks, A.J., Money, K.L.: Corrosion fatigue properties of Nickel-containing materials in seawater. NiDI Druckschrift Nr 1258 (1977)Google Scholar
  51. 51.
    Stainless steels and specialty alloys for modern pulp and paper mills. NiDI Reference book Series 11025, Nickel Development Institute. (2002)Google Scholar
  52. 52.
    Stoffhütte. Taschenbuch der Werkstoffkunde. 4. Aufl. W Ernst & Sohn, Berlin (1967)Google Scholar
  53. 53.
    Syrett, B.C.: Erosion-corrosion of copper-nickel alloys in seawater and other aqueous environments—a literature review. Corros. NACE. 32(6), 242–252 (1976)CrossRefGoogle Scholar
  54. 54.
    Tanaka, H.: Vibration behavior and dynamic stress of runners of very high head reversible pump-turbines. In: IAHR Symposium Belgrade, Beitrag U2 (1990)Google Scholar
  55. 55.
    Taschenbuch der Chemie. 5. Aufl. Harri Deutsch, Zürich (1973)Google Scholar
  56. 56.
    Technik-Lexikon, Rowohlt Verlag, Bd 35, S. 94Google Scholar
  57. 57.
    Timcke, J.H.: Quellverhalten eines Schiffskreiselpumpen-Laufrads aus Gefüge-Verbundwerkstoff. Industriepumpen + Kompressoren 3, pp. 191–196 (1999)Google Scholar
  58. 58.
    Timcke, J.H.: Swelling behaviour of pump impellers made from a structural composite. World Pumps, Dec 28–31 (1999)Google Scholar
  59. 59.
    Tischner, H.: Hochlegierte Gußwerkstoffe zur Förderung korrosiver und abrasiver Fluide. Pumpentagung Karlsruhe C7 (1988)Google Scholar
  60. 60.
    Tischner, H.: Werkstoffwahl für Pumpen in Rauchgasentschwefelungsanlagen. KSB Techn Berichte 25 (1988)Google Scholar
  61. 61.
    Tuthill, A.H., Lamb, S.: Guidelines for the use of stainless steel in municipal wastewater treatment plants. NiDI Technical series No 10076, Nickel Development Institute www.nidi.org (1998)
  62. 62.
    Uetz, H.: Abrasion und Erosion. Hanser, München (1986)Google Scholar
  63. 63.
    Van den Berg, C.H.: Grain shape effects on wear. Ports Dredging 152, 11–15 (1999)Google Scholar
  64. 64.
    Vetter, G., Kießling, R.: Verschleißverhalten von Pumpenwerkstoffen bei hydroabrasiver Strahlbeanspruchung. Konstruktion 47, 186–190 (1995)Google Scholar
  65. 65.
    Vetter, G., Kießling, R.: Zur Auslegung von Spaltdichtungen in Pumpen gegen hydroabrasiven Verschleiß. Konstruktion 48, 167–173 (1996)Google Scholar
  66. 66.
    Vetter, G., Klotzbücher, G.: Einige tribologische Grundlagenuntersuchungen zum abrasiven Gleit- und Strahlverschleiß von Pumpenwerkstoffen. Konstruktion 45, 371–378 (1993)Google Scholar
  67. 67.
    Vetter, G., et al.: Multiphase pumping with twin-screw pumps. In: 17th International Pumps Users Symposium, pp. 153–169. Texas A & M (2000)Google Scholar
  68. 68.
    VGB-Richtlinien für Kesselspeisewasser: VGB Kraftwerkstechnik 60(10), 793–800 (1980)Google Scholar
  69. 69.
    Weber, J.: Korrosion und Ablagerungen in Kühlsystemen – Ursachen und Bekämpfung. Techn. Rundsch. Sulzer. 3, 219–232 (1972)Google Scholar
  70. 70.
    Weber, J.: Materials for Seawater Pumps and Related Systems. Pumps Offshore/Onshore, GOL, Norway (1984)Google Scholar
  71. 71.
    Weber, J., Bolliger, W.: Werkstoffe für die Förderung korrosiver Medien. Dechema, 10–12.6 (1987)Google Scholar
  72. 72.
    Wellinger, K., Uetz, H.: Gleitverschleiß, Spülverschleiß, Strahlverschleiß unter der Wirkung von körnigen Feststoffen. VDI-Forschungsheft 449, Ausg. B, Bd. 21 (1955)Google Scholar
  73. 73.
    Werkstoffe für Meerwasseranlagen. International Nickel, Druckschrift 54 (1968)Google Scholar
  74. 74.
    Wilson, K.C., Addie, G.R., Sellgren, A., Clift, R.: Slurry Transport Using Centrifugal Pumps, 2nd edn. Blackie Academic and Professional, London. ISBN 0 7514 0408 X (1997)Google Scholar
  75. 75.
    Riihimäki, A.: Corrosion-resistant cast steels for process industry pumps Vuoriteollisuus - Bergshanteringen 4/2002 (in Finnish)Google Scholar

Copyright information

© Springer Nature Switzerland AG 2020

Authors and Affiliations

  1. 1.VilleneuveSwitzerland

Personalised recommendations