Distribution and Chemical Species of Chromium in the EAF Dust from Stainless Steel Plant

  • Zhi Li
  • Guojun MaEmail author
  • Xiang Zhang
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Electric Arc Furnace (EAF) dust generated in the production process of stainless steel is a hazard to the environment and human health due to its large amounts of toxic substances, such as Cr(VI). Cr in the EAF dust is mainly in the form of a residue according to sequential extraction procedure test, and only small amounts of Cr are mobility. Although the formation mechanism of the EAF dust has been gradually understood, the distribution and chemical species of Cr in EAF dust are rarely studied. In this paper, the distribution and chemical species of Cr in EAF dust were studied. The results show that Cr(III) and Cr(VI) are mainly present in the small particles. After sputtering about 140 s with Ar+ ion beam, the Cr(VI) on the surface of dust particles disappears, and the content of Cr(III) reaches 100%, indicating the Cr(VI) in the EAF dust comes from the oxidation of lower valent Cr-containing substances and enrich on the surface of the dust particles.

Keywords

EAF dust Cr(VI) formation Cr distribution Stainless steel 

References

  1. 1.
    Yan YF, Chen JX, Hu L (2007) Chromium metallurgy. Metallurgical Industry Press, BeijingGoogle Scholar
  2. 2.
    GB/T 12230, General purpose industrial valves-Specification of stainless steel castingsGoogle Scholar
  3. 3.
    ASTM A351, Standard specification for castings, austenitic, for pressure-containing partsGoogle Scholar
  4. 4.
    JIS G5121, Corrosion-resistant cast steels for general applicationGoogle Scholar
  5. 5.
    International Stainless Steel Forum (ISSF). Meltshop production statistics 2001 to 2006. http://www.worldstainless.org/crude_steel_production/meltshop_production_2001_2016
  6. 6.
    Vargas ASD, Ângela B, Masuero, Vilela ACF (2006) Investigations on the use of electric-arc furnace dust (EAFD) in Pozzolan-modified Portland cement I (MP) pastes. Cem Concr Res 36(10):1833–1841Google Scholar
  7. 7.
    Ma GJ (2005) Cr (VI)-containing electric furnace dust and filter cake: characteristics, formation, leachability and stabilization. University of Pretoria, Pretoria, South Africa, pp 25–98Google Scholar
  8. 8.
    Peng B, Peng J (2003) Stainless steel electric arc furnace dust physical and chemical properties and formation mechanism. North China Univ Technol 15(1):34–40Google Scholar
  9. 9.
    Davis A, Ruby MV, Bergstrom PD (1992) Bioavailability of arsenic and lead in soils from the Butte, Montana, mining district. Environ Sci Technol 26(3):461–468CrossRefGoogle Scholar
  10. 10.
    Ma GJ, Fan W, Xue ZL, Wang W, Tang H (2010) Leachability and fractionation of heavy metals in stainless steelmaking plant dusts. Acta Metallurgica Sinica (English Letters) 3(4):267–276Google Scholar
  11. 11.
    Laforest G, Duchesne J (2006) Characterization and leachability of electric arc furnace dust made from remelting of stainless steel. J Hazard Mater 135(1):156–164CrossRefGoogle Scholar
  12. 12.
    Sedumedi HN, Mandiwana KL, Ngobeni P, Panichev N (2009) Speciation of Cr(VI) in environmental samples in the vicinity of the ferrochrome smelter. J Hazard Mater 172(2):1686–1689CrossRefGoogle Scholar
  13. 13.
    Beukes JP, Dawson NF, Zyl PGV (2010) Theoretical and practical aspects of Cr(VI) in the South African ferrochrome industry. J S Afr Inst Min Metall 110(12):743–750Google Scholar
  14. 14.
    Fan W, Ma GJ, Xue ZL, Yang F, Fang Y (2012) Formation of Cr(VI)-bearing phases in the EAF dust from stainless steel plant. J Mater MetallGoogle Scholar
  15. 15.
    Cheng JF, Xu MH, Zeng HC, Feng R, Qiao Y (2002) The study of oxidation dynamic of Cr at high temperature. Chin J Electr Eng 22(8):135–138Google Scholar
  16. 16.
    Ma GJ, Su WH, Xue ZL, Xu ZH (2009) Microstructure and occurrence of chromium of the stainless steel plant dusts. China Iron and Steel Association, Beijing, China, 12 Nov 2009Google Scholar
  17. 17.
    Wu YJ, Jiang ZH, Liang LK, Jiang MF, Huang ZZ, Chen ZP (2003) Analysis of correlative thermodynamic problems in stainless steel smelting process(II)-dephosphorization of chromium- containing hot metal. J Iron Steel Res 15(4):12–17Google Scholar
  18. 18.
    Zhang JY, Xing XR, Song B (2004) Metallurgical physical chemistry. Metallurgical Industry Press, Beijing, pp 317–318Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Hubei Provincial Engineering Technology Research Center of Metallurgical Secondary ResourcesWuhan University of Science and TechnologyWuhanChina
  2. 2.Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of EducationWuhan University of Science and TechnologyWuhanChina
  3. 3.State Key Laboratory of Refractories and MetallurgyWuhan University of Science and TechnologyWuhanChina

Personalised recommendations