Shape Casting pp 187-199 | Cite as

Campbellology for Runner System Design

  • Fu-Yuan HsuEmail author
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

The runner systems based on the Campbellology, the 10 casting rules of Professor John Campbell, were designed to achieve the bifilm-defect free casts during the filling process in gravity casting. In this study, three main methods were utilized to control the bottom-gating velocity under the critical velocity (the rule no. 2). In these methods, the kinetic energy form of liquid metal (with high velocity) was transformed to the static pressure form (under the critical velocity) in the bottom of the gating systems. The total head height with low energy loss was maintained in these runner designs. A continuous and positive static pressure of liquid metal against to the wall of mold cavity from the bottom to the top of cast was accomplished throughout the filling. Many design schemes to avoid the filling defects, such as oxide entrapment, confluence weld, bubble entrainment, and sand core blow defects, were also suggested in these casting processes.

Keywords

Runner system design Critical ingate velocity Bifilm defect Gravity casting 

References

  1. 1.
    Campbell J (2011) Complete casting handbook, metal casting process, metallurgy, techniques and design, 1st edn. p 614 [1a], pp 24–42 [1b], p 327 [1c], pp 67–72 [1d]Google Scholar
  2. 2.
    Hsu F-Y (2016) Bifilm defect formation in hydraulic jump of liquid aluminum. Metall Mater Trans B 47(3):1634–1648CrossRefGoogle Scholar
  3. 3.
    Smithells CJ, Brandes EA (1976) Metal reference book, 5th edn. ButterworthsGoogle Scholar
  4. 4.
    Green NR, Campbell J (1993) Statistical distributions of fracture strengths of cast Al–7Si–Mg. Mater Sci Eng, A 173:261–266CrossRefGoogle Scholar
  5. 5.
    Green NR, Campbell J (1993) Statistical distributions of fracture strengths of cast Al–7Si–Mg. Mater Sci Eng, A 173:261–266CrossRefGoogle Scholar
  6. 6.
    Green NR, Campbell J (1994), Influence of oxide film filling defects on the strength of Al–7Si–Mg alloy castings. Trans AFS, pp 341–347Google Scholar
  7. 7.
    Tiryakioglu M, Campbell J (2010) Weibull analysis of mechanical data for castings: a guide to the interpretation of probability plots. Metall Mater Trans A 41A:3121–3129CrossRefGoogle Scholar
  8. 8.
    Tiryakioglu M, Campbell J, Alexopoulos ND (2009) Quality indices for aluminum castings: a critical review. Metall Mater Trans B 40:802–811CrossRefGoogle Scholar
  9. 9.
    Hsu F-Y, Yang Y-M (2012) Confluence weld in an aluminum gravity casting. J Mater Process Technol 212:825–840CrossRefGoogle Scholar
  10. 10.
    Hsu F-Y, Jolly MR, Campbell J (2007) The design of L-shaped runners for gravity casting. In: Shape casting 2nd international symposium, Proceedings of 2007 TMS (The minerals, metals & materials society) annual meeting. Orlando, FL, USA, pp 101–108Google Scholar
  11. 11.
    Hsu F-Y, Jolly MR, Campbell J (2009) A multiple-gate runner system for gravity casting. J Mater Process Technol 209:5736–5750CrossRefGoogle Scholar
  12. 12.
    Hsu F-Y, Lin H-J (2009) A diffusing runner for gravity casting. Metall Mater Trans B 40(6):833–842CrossRefGoogle Scholar
  13. 13.
    Hsu F-Y, Lin H-J (2011) Foam filters used in gravity casting, Metall Mater Trans B 40(6):1110–1117CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Department of Materials Science and EngineeringNational United UniversityTaiwanRepublic of China

Personalised recommendations