Update on Bifilms—The Fundamental Defect in Metals

  • John CampbellEmail author
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

The concept of the bifilm is now nearly 20 years old. It has been clearly shown to control structural defects in castings such as porosity and hot tearing, plus, in solid wrought products, mechanical properties such as ductility and fatigue. It appears to explain for the first time the structures of Al–Si alloys and cast irons. Furthermore, although there are a number of proposed mechanisms for crack initiation in metals, it seems most probable that these are invalid. It follows that there is probably no intrinsic crack failure mechanism for most engineering metals; metals should never crack. The only crack-initiating feature appears to be the bifilm, introduced accidentally during casting. By appropriate casting techniques, the introduction of bifilms can be avoided. For this reason, failure by fatigue and creep may be eliminated, together with invasive corrosion such as pitting, stress corrosion cracking and possibly other failure modes.

Keywords

Bifilm Creep Fatigue Corrosion Griffith crack Casting 

References

  1. 1.
    Campbell J (2015) Complete casting handbook, 2nd edn. Elsevier, OxfordGoogle Scholar
  2. 2.
    Campbell J (2011) The origin of Griffith cracks. Met Mat Trans B 42:1091–1097CrossRefGoogle Scholar
  3. 3.
    Wang J (2015) Atomistic simulations of dislocation pileup: grain boundary interaction. JOM 67(7):1515–1525CrossRefGoogle Scholar
  4. 4.
    Andrade EDC (1935) Plasticity of rock salt crystals. Nature 135: 310–310CrossRefGoogle Scholar
  5. 5.
    Gall K, Horstemeyer MF, Schilfgaarde MV, Baskes MI (2000) Atomistic simulations of the tensile debonding of an Al–Si interface. J Mech Phys Solids 48:2183–2212CrossRefGoogle Scholar
  6. 6.
    Charlotte M, Laverne J, Marigo J-J (2006) Initiation of cracks with cohesive force models. Eur J Mech A/Solids 25:649–669CrossRefGoogle Scholar
  7. 7.
    Wilshire B, Sharning PJ (2008) Int Mater Rev 14:91–104Google Scholar
  8. 8.
    Srinivasan A, Pillai UTS, Swaminathan J, Pai BC (2006) Enhanced creep properties of low pressure die cast AZ91 Mg alloy. Int J Cast Metals Res 19(5):265–268CrossRefGoogle Scholar
  9. 9.
    Tiryakioglu M, Eason PD, Campbell J (2013) Fatigue life of ablation-cast 6061-T6 components. Mater Sci Eng, A 559:447–452CrossRefGoogle Scholar
  10. 10.
    Tiryakioglu M (2014) The relationship between elongation and fatigue life in A206 aluminum castings. Mater Sci Eng, A 601:116–122CrossRefGoogle Scholar
  11. 11.
    Tiryakioğlu M (2011) Fracture surface facets and fatigue life potential of castings. Metall Mater Trans B 42(6) 1098–1103Google Scholar
  12. 12.
    Campbell J (2016) Consolidation and corrosion of metals: an overview of the role of bifilms in corrosion. Innov Corros Mater Sci 6:132–139. 000-000 1 2352-0949/16Google Scholar
  13. 13.
    Lin L, Liu Z, Li Y, Han X, Chen Xu (2012) Effects of severe cold rolling on exfoliation corrosion of Al–Zn–Mg–Cu–Cr alloy. J Mater Eng Perform 21(6):1070–1075CrossRefGoogle Scholar
  14. 14.
    Almaraz GM, Aburto AD, Gomez EC (2014) Ultrasonic fatigue endurance of Al alloy 6061-T6 on pre- and non-corroded specimens. Metall Mater Trans 45:280–286CrossRefGoogle Scholar
  15. 15.
    Yonezawa T, Watanate M, Hashimoto A (2015) Primary water SCC in 690 alloy. Metall Mater Trans 46:2768–2780CrossRefGoogle Scholar
  16. 16.
    Lu YH, Chen ZR, Zhu XF, Shoji T (2014) SCC behaviour of austenitic stainless 23CN20-09 M in high temperature water. Mater Sci Technol 30(15):1944–1950CrossRefGoogle Scholar
  17. 17.
    Harris ZD, Dolph JD, Pioszak GL, Rincon Troconis BC, Scully JR, Burns JT (2016) Hydrogen environment-assisted cracking of monel K-500. Metall Mater Trans 47:3488–3510CrossRefGoogle Scholar
  18. 18.
    Campbell J (2015) Quality castings: a personal account of the development of the cosworth casting process. Aspect Design 2013 and American Foundry Society 2015Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Emeritus Professor of Casting Technology, Department of Metallurgy and MaterialsUniversity of BirminghamBirminghamUK

Personalised recommendations