Field-Assisted Sintering of Nickel-Based Superalloy Powder for High-Temperature Hybrid Turbine Disc Applications

  • Charis I. LinEmail author
  • Sebastian Niuman
  • Namiko Yamamoto
  • Anil Kulkarni
  • Jogender Singh
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Turbine discs are currently made of nickel-based superalloys, known for their high strength and creep resistance at high temperatures. Hybrid or dual-microstructure turbine discs allow for significant weight savings, but current methods of joining dissimilar nickel-based superalloys such as friction welding exhibit a heat-affected zone and localized melting at the interface, leading to weak bonding. Here, we show that field-assisted sintering technology may be used to sinter the nickel-based superalloy powder CM247LC to high relative density, and the effect of sintering temperature and time on porosity, grain size, and mechanical properties of CM247LC is investigated. We also show that the same technology may be used to form hybrid discs with a solid Inconel 718 core and a powder-sintered CM247LC rim without the formation of a heat-affected zone at the interface. Two different joining angles between the two materials in the hybrid discs are explored, and preliminary results suggest that the joining angle does not affect the tensile properties of the material interface.

Keywords

FAST Hybridization Ni-based superalloys Sintering Turbine disc 

References

  1. 1.
    Gabb TP, MacKay RA, Draper SL, Sudbrack CK, Nathal MV (2013) The mechanical properties of candidate superalloys for a hybrid turbine disk. NASA Technical Reports. https://ntrs.nasa.gov/archive/nasa/casi.ntrs.nasa.gov/20140000732.pdf. Accessed 16 July 2018
  2. 2.
    Mathey GF (1994) Method of making superalloy turbine disks having graded coarse and fine grains. US Patent 5,312,497. 17 May 1994Google Scholar
  3. 3.
    Gayda J, Gabb TP, Kantzos PT (2004) The effect of dual microstructure heat treatment on an advanced nickel-base disk alloy. Superalloys 2004:323–329CrossRefGoogle Scholar
  4. 4.
    Mourer DP, Williams JL (2004) Dual heat treat process development for advanced disk applications. Superalloys 2004:401–407CrossRefGoogle Scholar
  5. 5.
    Lemsky J, Gayda J (2005) Assessment of NASA dual microstructure heat treatment method utilizing Ladis SuperCooler(trademark) cooling technology. NASA Technical Reports. https://ntrs.nasa.gov/archive/nasa/casi.ntrs.nasa.gov/20050161950.pdf. Accessed 2 Sept 2018
  6. 6.
    Vairis A, Frost M (1998) High frequency linear friction welding of a titanium alloy. Wear 217(1):117–131CrossRefGoogle Scholar
  7. 7.
    Senkov ON, Mahaffey DW, Semiatin SL (2014) Inertia friction welding of the dissimilar superalloys Mar-M247 and LSHR. Metall Mater Trans A 45(12):5545–5561CrossRefGoogle Scholar
  8. 8.
    Mahaffey DW, Senkov ON, Shivpuri R, Semiatin SL (2016) Effect of process variables on the inertia friction welding of superalloys LSHR and Mar-M247. Metall Mater Trans A 47(8):3981–4000CrossRefGoogle Scholar
  9. 9.
    Guillon O, Gonzalez-Julian J, Dargatz B, Kessel T, Schierning G, Räthel J, Merrmann M (2014) Field-assisted sintering technology/spark plasma sintering: mechanisms, materials, and technology developments. Adv Eng Mater 16(7):830–849CrossRefGoogle Scholar
  10. 10.
    Belmonte M, González-Julián J, Miranzo P, Osendi MI (2010) Spark plasma sintering: a powerful tool to develop new silicon nitride-based materials. J Eur Ceram Soc 30:2937–2946CrossRefGoogle Scholar
  11. 11.
    Chanthapan S, Rape A, Gephart S, Kulkarni AK, Singh J (2011) Industrial scale field assisted sintering an emerging disruptive manufacturing technology: applications. Mater Sci Forum 169:25–28Google Scholar
  12. 12.
    Harris K, Erickson GL, Schwer RE (1984) MAR M 247 derivations—CM 247 LC DS alloy, CMSX® single crystal alloys, properties and performance. Superalloys 1984:221–230Google Scholar
  13. 13.
    Sundararaman M, Mukhopadhyay P, Banerjee S (1988) Precipitation of the δ-Ni 3 Nb phase in two nickel base superalloys. Metall Trans A 19(3):453–465CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • Charis I. Lin
    • 1
    Email author
  • Sebastian Niuman
    • 1
  • Namiko Yamamoto
    • 2
  • Anil Kulkarni
    • 3
  • Jogender Singh
    • 1
  1. 1.Penn State Applied Research LaboratoryState CollegeUSA
  2. 2.Department of Aerospace EngineeringThe Pennsylvania State UniversityUniversity ParkUSA
  3. 3.Department of Mechanical EngineeringThe Pennsylvania State UniversityUniversity ParkUSA

Personalised recommendations