Effects of Temperature and Alkali Carbonates on Graphitization and Metallurgical Properties of Coke

  • Rongjin Zhu
  • Shengfu ZhangEmail author
  • Guangsheng Suo
  • Yue Wu
  • Xiaohu Zhou
  • Shuxing Qiu
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

In this paper, metallurgical cokes containing different proportion of alkali carbonate were subjected to treatment with annealing under N2 temperature from 1100 to 1600 °C to investigate graphitization and metallurgical properties of coke. The annealed coke powder was characterized using weight method, I-drum tumbling, X-ray diffraction and optical microscope. The results clearly showed that the weight loss increased with the increasing of temperature. The Na2CO3 (or K2CO3) also effectively accelerated the weight loss. Combined with the crystallite structure, it could be shown that the La and Lc of coke increased with the increasing of temperature, while the d002 revealed the opposite trend. It could also be shown that alkali carbonates destroyed crystallite structure. From optical micrographs, it could be seen that the porosity of coke increased with the increasing of temperature. The large pores decreased while the micropores increased gradually which revealed that alkali carbonates destroyed pore structure. The destruction of potassium carbonate was more obvious.

Keywords

Coke Alkali carbonate Crystalline structure Porosity 

Notes

Acknowledgements

This work was supported by the National Natural Science Foundation of China (Grant No. 51474042 & 51774061) and the Fundamental Research Funds for Central Universities (Grant No. 106112017CDJQJ138801). The authors also acknowledge the support provided by the Fund of Chongqing Science and Technology (Project No. cstc2018jscx-msyb0988).

References

  1. 1.
    Li K, Khanna R, Zhang J (2014) The evolution of structural order, microstructure and mineral matter of metallurgical coke in a blast furnace: a review. Fuel 133(5):194–215CrossRefGoogle Scholar
  2. 2.
    Hilding T, Gupta S, Sahajwalla V (2005) Degradation behaviour of a high CSR coke in an experimental blast furnace: effect of carbon structure and alkali reactions. ISIJ Int 45(7):1041–1050CrossRefGoogle Scholar
  3. 3.
    Watakabe S, Takeda K, Nishimura H (2006) Development of high ratio coke mixed charging technique to the blast furnace. ISIJ Int 46(4):513–522CrossRefGoogle Scholar
  4. 4.
    Peacey JG (1979) The iron blast furnace: theory and practice. Pergamon Press, New YorkGoogle Scholar
  5. 5.
    Wang W, Wang J, Xu R (2017) Influence mechanism of zinc on the solution loss reaction of coke used in blast furnace. Fuel Process Technol 159:118–127CrossRefGoogle Scholar
  6. 6.
    Nomura S, Terashima H, Sato E, Naito M (2007) Some fundamental aspects of highly reactive iron coke production. ISIJ Int 47(6):823–830CrossRefGoogle Scholar
  7. 7.
    Hilding T, Kazuberns K, Gupta S (2005) Effect of temperature on coke properties and CO2 reactivity under laboratory conditions and in an experimental blast furnace. In: Iron & steel technology conference, Vietnam, 9–12 May 2005Google Scholar
  8. 8.
    Xing X, Rogers H, Zhang G (2016) Coke degradation under simulated blast furnace conditions. ISIJ Int 56(5):786–793CrossRefGoogle Scholar
  9. 9.
    Kazuberns K, Gupta S, Grigore M (2008) Coke mineral transformations in the experimental blast furnace. Energy Fuels 22(5):514–522CrossRefGoogle Scholar
  10. 10.
    Li K, Zhang J, Barati M (2015) Influence of alkaline (Na, K) vapors on carbon and mineral behavior in blast furnace cokes. Fuel 145(37):202–213CrossRefGoogle Scholar
  11. 11.
    Kaczorowski J, Lindstad T (2007) The effect of potassium impregnation on the boundouard reactivity of selected single-source and commercial cokes. Ifapa 12(5):584–593Google Scholar
  12. 12.
    Mei Y, Wang Z, Fang H (2017) Na-containing mineral transformation behaviors during Na2CO3-catalyzed CO2 gasification of high-alumina coal. Energy Fuels 31(2):1235–1242CrossRefGoogle Scholar
  13. 13.
    Xing X, Rogers H, Zhang G (2016) Coke degradation under simulated blast furnace conditions. ISIJ Int 56(5):786–793CrossRefGoogle Scholar
  14. 14.
    Xing X, Ostrovski O (2013) Effect of annealing on properties of carbonaceous materials. Part II: porosity and pore geometry. Metall Mater Trans B Process Metall Mater Process Sci 44(4):862–869CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • Rongjin Zhu
    • 1
  • Shengfu Zhang
    • 1
    Email author
  • Guangsheng Suo
    • 1
  • Yue Wu
    • 1
  • Xiaohu Zhou
    • 1
  • Shuxing Qiu
    • 1
  1. 1.College of Materials Science and Engineering, Chongqing UniversityChongqingChina

Personalised recommendations