Use of Municipal Solid Waste Incinerator (MSWI) Fly Ash in Alkali Activated Slag Cement

  • Kang HuangEmail author
  • Xiaohui Fan
  • Min Gan
  • Zhiyun Ji
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

This paper investigates the utilization of municipal solid waste incinerator fly ash (MFA) as a replacement of alkali-activated slag (AAS) cement. The mechanical performance of pastes with different dosages of MFA were studied and optimized. Compared with the AAS no MFA added, the compressive strength of the AAS pastes prepared at 3 d(days) with a 10% replacement of MFA fell sharply from 71.11 to 48.25 MPa, which remained stable with more MFA added. When the replacement proportion increased to 30%, the AAS pastes still reached a high compressive strength of 64.37 MPa at 28 d. XRD and SEM analysis were conducted to investigate the hydration products and micro structure of pastes. Main hydration products of the AAS paste with 30% MFA addition were calcium silicate hydrate (C-S-H) gel and C-A-S-H (C-CaO; A-Al2O3; S-SiO2; H-H2O) gel. Some unreacted MFA particles could be also observed from SEM analysis. This study provides a new resource utilization way of MFA.

Keywords

Ground granulated blast furnace slag MSWI fly ash Compressive strength Hydration product 

Notes

Acknowledgements

The research was financially supported by the National Natural Science Foundation of China (No. U1660206, U1760107), Hunan Provincial Co-Innovation Center for Clean and Efficient Utilization of Strategic Metal Mineral Resources and Innovation Driven Plan of Central South University (No. 2015CX005) and Hunan Key Research & Development Plan (2018SK2049).

References

  1. 1.
    Ferreira C, Ribeiro A, Ottosen L (2003) Possible applications for municipal solid waste fly ash. J Hazard Mater 96(2–3): 201–216CrossRefGoogle Scholar
  2. 2.
    Guo X, Shi H (2013) Self-solidification/stabilization of heavy metal wastes of class c fly ash-based geopolymers. J Mater Civ Eng 25(4):491–496CrossRefGoogle Scholar
  3. 3.
    Jin M, Zheng Z, Sun Y et al (2016) Resistance of metakaolin-MSWI fly ash based geopolymer to acid and alkaline environments. J Non Cryst Solids 450:116–122CrossRefGoogle Scholar
  4. 4.
    Minocha AK, Jain N, Verma CL (2003) Effect of inorganic materials on the solidification of heavy metal sludge. Cem Concr Res 33(10):1695–1701CrossRefGoogle Scholar
  5. 5.
    Lederer J, Trinkel V, Fellner J (2016) Wide-scale utilization of MSWI fly ashes in cement production and its impact on average heavy metal contents in cements: the case of Austria. Waste Manag 60:247–258CrossRefGoogle Scholar
  6. 6.
    Brown TJ, Idoine NE, Raycraft ER, Shaw RA, Deady EA, Hobbs SF, Bide T (2017) World mineral production 2011-2015. British Geological Survey, NottinghamGoogle Scholar
  7. 7.
    Shen JG, Guo CY, Chen M, Yu JK, Jian MF (2006) Utilization of metallurgical slag as resource materials in China. Dev Chem Eng Miner Process 14:487–493CrossRefGoogle Scholar
  8. 8.
    Lecomte I, Henrist C, Liégeois M et al (2006) (Micro)-structural comparison between geopolymers, alkali-activated slag cement and Portland cement. J Eur Ceram Soc 26(16):3789–3797CrossRefGoogle Scholar
  9. 9.
    Juenger MCG, Winnefeld F, Provis JL, Ideker JH (2011) Advances in alternative cementitious sbinders. Cem Concr Res 41:1232–1243CrossRefGoogle Scholar
  10. 10.
    Fernández-Jiménez A, Puertas F, Sobrados I, Sanz J (2003) Structure of calcium silicate hydrates formed in alkaline activated slag. Influence of the type of alkaline activator. J Am Ceram Soc 86(3):1389–1394CrossRefGoogle Scholar
  11. 11.
    Brough AR, Atkinson A (2002) Sodium silicate-based, alkali-activated slag mortars. Part I. Strength, hydration and microstructure. Cem Concr Res 32:865–879CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.School of Minerals Processing & BioengineeringCentral South UniversityChangshaPeople’s Republic of China

Personalised recommendations