In-Situ Proton Irradiation-Corrosion Study of ATF Candidate Alloys in Simulated PWR Primary Water

  • Peng WangEmail author
  • Gary S. Was
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Irradiation enhanced corrosion behavior of Accident Tolerant Fuel candidate alloys T91 and Fe15Cr4Al were evaluated using in-situ proton irradiation-corrosion experiments in hydrogenated pure water (at 320 °C, 3 wppm H2) with a 5.4 MeV proton beam. The thin sample acted as a “window” to allow protons to fully penetrate the sample while maintaining system pressure. The area of the samples exposed to the proton beam experienced effects from displacement damage and radiolysis products. The aim of the study was to characterize the effect of radiation on the kinetics and character of oxidation caused by accelerated waterside corrosion under irradiation. Samples irradiated with protons for total displacement damage of ~0.1 dpa (dose rate in water, 400 kGy/s) at an exposure time of 24 h were compared. Oxide morphology, phase structure, and composition of the oxide, metal and the metal/oxide interface were investigated using TEM and EDS and are related to the test conditions. The oxidation rate or resulting oxide thickness is dependent on the alloy Cr content; the oxidation rate increased as the Cr content decreased. The resulting oxide consists of an inner layer of Cr-rich spinel oxide and outer magnetite crystals in the unirradiated region; while the irradiated region consists of Cr-rich inner oxide spinel that was partially dissolved and coverage of outer non-faceted hematite precipitates.

Keywords

Accident tolerant fuel Irradiation Proton Corrosion 

Notes

Acknowledgements

This research was supported by Department of Energy (DOE), Nuclear Energy University Programs (NEUP), Grant No. DE-NE0008272. The authors also acknowledge the MIBL facilities and the MIBL staff who helped with the irradiations.

References

  1. 1.
    R.B. Rebak, Ferritic alloys as accident tolerant fuel cladding material for light water reactors, DE-NE0000568, Final Report Phase 1A FY2013-2014, General ElectricGoogle Scholar
  2. 2.
    K.A. Terrani et al., Uniform corrosion of FeCrAl alloys in LWR coolant environments. J. Nucl. Mat. 479, 36–47 (2016)CrossRefGoogle Scholar
  3. 3.
    K.A. Terrani, S.J. Zinkle, L.L. Snead, Advanced oxidation-resistant iron-based alloys for LWR fuel cladding. J. Nucl. Mat. 448, 420–435 (2014)CrossRefGoogle Scholar
  4. 4.
    S. Bragg-Sitton, Overview of international activities in accident tolerant fuel development for light water reactors. Presentation given at the IAEA technical working group on fuel performance and technology, Vienna, Austria, 24–25 April 2014Google Scholar
  5. 5.
    P. Ampornrat, G.S. Was, Oxidation of ferritic-martensitic alloys T91, HCM12A, and HT-9 in supercritical water. J. Nucl. Mat. 371, 1–17 (2007)CrossRefGoogle Scholar
  6. 6.
    R.L. Klueh, K. Ehrlich, F. Abe, Ferritic/martensitic steels: promises and problems. J. Nucl. Mate. 191–194, 116–124 (1992)Google Scholar
  7. 7.
    R.B. Rebak, in Advanced Steels for Accident Tolerant Fuel Cladding in Commercial Nuclear Reactors, ed by T. Ohji, J. Matyáš, N.J. Manjooran, G. Pickrell, A. Jitianu. Advances in Materials Science for Environmental and Energy Technologies III. The American Ceramic Society, published 2014 by WileyGoogle Scholar
  8. 8.
    S. Raiman, Irradiation accelerated corrosion of 316L stainless steel in simulated primary water, Ph.D. thesis, University of Michigan, 2016Google Scholar
  9. 9.
    J.F. Ziegler, The stopping and range of ions in matter (SRIM) 2013. Available from http://www.srim.org
  10. 10.
    ASTM E521. Standard practice for neutron radiation damage simulation by charged-particle irradiation (American Society for Testing and Materials, Philadelphia, 1996)Google Scholar
  11. 11.
    S. Raiman, A. Flick, O. Toader, P. Wang, N.A. Samad, Z. Jiao, G.S. Was, A facility for studying irradiation accelerated corrosion in high-temperature water. J. Nucl. Mater. 451(1–3), 40 (2014)CrossRefGoogle Scholar
  12. 12.
    S. Le Caër, Water radiolysis: influence of oxide surfaces on H22 production under ionizing radiation. Water 3, 235–253 (2011)CrossRefGoogle Scholar
  13. 13.
    R. Springell et al., Water corrosion of spent nuclear fuel: radiolysis driven dissolution at the UO2 water interface. Faraday Discuss. 180, 301–311 (2015)CrossRefGoogle Scholar
  14. 14.
    J. Töpfer, S. Aggarwal, R. Dieckmann, Point defects and cation tracer diffusion in (CrxFe1-x)3-δO4 spinels. Solid State Ionic 81, 251–266 (1995)CrossRefGoogle Scholar
  15. 15.
    L. Singheiser et al., High temperature corrosion issues for metallic materials in solid oxide fuel cells. Shreir’s Corrosion 1, 482–517 (2010). ElsevierCrossRefGoogle Scholar
  16. 16.
    B.J. Lewis, E.N. Onder, A.A. Prudil, Fundamentals of Nuclear Engineering (Wiley, Hoboken, 2017)Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Nuclear Engineering and Radiological ScienceUniversity of MichiganAnn ArborUSA

Personalised recommendations