A Recent Look at CANDU Feeder Cracking: High Resolution Transmission Electron Microscopy and Electron Energy Loss Near Edge Structure (ELNES)

  • C. D. JudgeEmail author
  • S. Y. Persaud
  • A. Korinek
  • M. D. Wright
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

The primary heat transport system of modern CANDU® (CANDU is a registered trademark of Atomic Energy of Canada Limited) reactors uses A106B piping (i.e., feeder pipes). Feeder cracking has only affected tight-radius bends at outlet feeders (higher temperature), and cracking is limited to regions with high residual stress suffering from wall-thinning by flow accelerated corrosion. To date, the mechanism of feeder cracking has not been identified. This paper includes high-resolution transmission electron microscopy and electron energy loss near edge structure characterization of inside and outside surface intergranular cracks from ex-service CANDU feeders. Prior to this work, no high resolution characterization has been performed for CANDU feeder cracking. All intergranular cracks show evidence of cementite decomposition, leading to decoration of grain boundaries with amorphous carbon, and carbon diffusion along un-cracked boundaries ahead of crack tips. Sulfur has been found on the oxide-metal interface of all intergranular cracks, but is not observed ahead of the crack tips. Sulfur is believed to be from the breakdown of manganese sulfides during service. The cementite decomposition and breakdown of manganese sulfides are believed to be accelerated in the presence of hydrogen produced from the flow accelerated corrosion. Small (<15 nm) voids are also present ahead of some intergranular crack-tips along the ferrite-ferrite boundaries, indicating that hydrogen enhanced, low temperature creep-cracking, may also contribute to intergranular fracture.

Keywords

TEM Embrittlement ELNES Carbon steel 

Notes

Acknowledgements

The authors would like to acknowledge the CANDU Owners Group for funding support for this work. Koji Arioka and Roger Staehle, Grant Bickel and Jared Smith for helpful discussion.

References

  1. 1.
    J.P. Slade, T.S. Gendron, in Flow Accelerated Corrosion and Cracking of Carbon Steel Piping in Primary Water—Operating Experience at the Point Lepreau Generating Station. 12th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors (2005)Google Scholar
  2. 2.
    T.S. Gendron, J.P. Slade, G. White, Nucl. Eng. Int. 52, 630 (2007)Google Scholar
  3. 3.
    J.P. Slade, T.S. Gendron, in A Last look at PLGS Life-Limiting Feeder Degradation. 8th International Conference on CANDU Maintenance. Toronto, Canada (2008)Google Scholar
  4. 4.
    M.D. Wright, Role of Cold Work in Candu Feeder Cracking (Carbon Steel) (2008)Google Scholar
  5. 5.
    P. Shewmon, C. Richied, M. McKimpson, M. Ransick, Effect of hydrogen pressure on morphology of hydrogen attack. Scr. Metall. 14, 545–548 (1980)CrossRefGoogle Scholar
  6. 6.
    P. Shewmon, Y.H. Xue, Effect of high-pressure hydrogen on crack growth in carbon steel. Metall. Trans. A 22A, 2703–2707 (1991)CrossRefGoogle Scholar
  7. 7.
    P.G. Shewmon, Hydrogen attack of carbon steel. Metall. Trans. A 7A, 279–286 (1976)CrossRefGoogle Scholar
  8. 8.
    S.M. Schlogl, Y. van Leeuwen, E. van der Giessen, On methane generation and decarburization in low-alloy Cr-Mo steels during hydrogen attack. Metall. Mat. Trans. A 31A, 125–137 (2000)CrossRefGoogle Scholar
  9. 9.
    H.E. Hanninen, T.C. Lee, I.M. Robertson, H.K. Birkbaum, In situ observations on effects of hydrogen on deformation and fracture of A533B pressure vessel steel. J. Mat. Eng. Perform. 2:807–818 (1993)CrossRefGoogle Scholar
  10. 10.
    Y. Jagodzinski, H.E. Hanninen, O. Tarasenko, S. Smuk, Interaction of hydrogen with dislocation pile-ups and hydrogen induced softening of pure iron. Scripta Materialia 43, 245–251 (2000)CrossRefGoogle Scholar
  11. 11.
    M.W. Phaneuf, G.A. Botton, in Analysis of Degradation in Nickel-Based Alloys using Focused Ion Beam Imaging and Specimen Preparation Combined with Analytical Electron Microscopy. Fontevraud 5—Contribution of Materials Investigation to Problems Encountered in Pressurized Water Reactors (Societe Francaise d’Energie Nucleaire (SFEN), Paris, France, 2002), pp. 117–128Google Scholar
  12. 12.
    S.Y. Persaud, A.G. Carcea, J. Huang, A. Korinek, G.A. Botton, R.C. Newman, Analytical electron microscopy of a crack tip extracted from a stressed Alloy 800 sample exposed to an acid sulfate environment. Micron 61, 62–69 (2014)CrossRefGoogle Scholar
  13. 13.
    S. Lozano-Perez, A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis. Micron 39, 320–328CrossRefGoogle Scholar
  14. 14.
    K. Arioka, T. Miyamoto, T. Yamada, T. Terachi, Formation of cavities prior to crack initiation and growth on cold-worked carbon steel in high temperature water. Corrosion 66, 015008-1–14 (2010)CrossRefGoogle Scholar
  15. 15.
    K. Arioka, T. Miyamoto, T. Yamada, M. Aoki, Role of cavity formation in crack initiation of cold-worked carbon steel in high-temperature water. Corrosion 69:487–496 (2013)CrossRefGoogle Scholar
  16. 16.
    L.A.J. Garvie, A.J. Craven, R. Brydson, Use of electron energy loss near-edge fine structure in the study of minerals. Am. Mineral 79, 411–425 (1994)Google Scholar
  17. 17.
    Y. Li, P. Choi, C. Borchers, S. Westerkamp, S. Goto, D. Raabe, et al., Atomic-scale mechanisms of deformation-induced cementite decomposition in pearlite. Acta Materialia 59, 3965–3977 (2011)CrossRefGoogle Scholar
  18. 18.
    P. Choi, Y. Li, R. Kirchheim, D. Raabe, Deformation-induced cementite decomposition in pearlitic steel wires studied by Atom probe tomography. 18th international conference on composite materials Google Scholar
  19. 19.
    Y.I. Matrosov, V.N. Zikeev, Effect of impurities and alloying elements on the susceptibility of high-purity iron to brittle fracture. Metallovedenie Termicheskaya Obrabotka Metallov 11, 25–29 (1966)Google Scholar
  20. 20.
    R. Honda, H. Taga, Effect of carbon and oxygen on the fracture of iron. Metal Sci. J. 2, 172–176 (1968)CrossRefGoogle Scholar
  21. 21.
    J.R. Low Jr., R.G. Feustel, Inter-crystalline fracture and twinning of iron at low temperatures. Acta Metall. 1, 186–192 (1953)CrossRefGoogle Scholar
  22. 22.
    C.J. McMahon Jr., Brittle fracture of grain boundaries. Interface Sci. 12, 141–146 (2004)CrossRefGoogle Scholar
  23. 23.
    C.J. McMahon Jr., Intergranular brittleness in iron. Acta Metall. 14, 839–845 (1966)CrossRefGoogle Scholar
  24. 24.
    S. Lynch, Hydrogen embrittlement phenomena and mechanisms. Corros. Rev. 30, 105–122 (2012)Google Scholar
  25. 25.
    Z. Shirband, M.R. Shishesaz, A. Ashrafi, Hydrogen degradation of steels and its related parameters, a review. Phase Transitions 84, 924–943 (2011)CrossRefGoogle Scholar
  26. 26.
    N. Bandyopadhyay, C.J. McMahon Jr., The Micro-Mechanisms of Tempered Martensite Embrittlement in 4340-type Steels. Metall. Trans. A 14A, 1314–1325 (1983)Google Scholar
  27. 27.
    D. Bika, J.A. Pfaendtner, M. Menyhard, C.J. McMahon Jr., Sulfur-induced dynamic embrittlement in a low-alloy steel. Acta Metall. Mater. 43, 1895–1908 (1995)CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • C. D. Judge
    • 1
    Email author
  • S. Y. Persaud
    • 1
  • A. Korinek
    • 2
  • M. D. Wright
    • 1
  1. 1.Canadian Nuclear LaboratoryChalk RiverUSA
  2. 2.McMaster UniversityHamiltonCanada

Personalised recommendations