Oxidation Kinetics of Austenitic Stainless Steels as SCWR Fuel Cladding Candidate Materials in Supercritical Water

  • Hiroshi AbeEmail author
  • Ryuichi Suzuki
  • Yutaka Watanabe
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

The oxidation kinetics of supercritical-water-cooled reactor (SCWR) fuel cladding candidate materials, e.g. 15Cr-20Ni stainless steel (1520 SS) in supercritical water at 650 and 700 °C under 24 MPa has been investigated. Characteristics of oxide layers and its relation to oxidation behaviors are also studied. The applicability of the candidate materials for the fuel cladding of SCWR from oxidation kinetics, spalling susceptibility of oxide layer, and breakdown of Cr2O3 layer points of view has been discussed. The results indicate that the threshold condition for spalling of oxide layer is different at 650 and 700 °C. The decrease in oxidation kinetics of 1520 SS with time correspond to the change in rate-limiting process of oxidation from mass transfer through an Fe oxides to mass transfer through a Cr rich oxide layer with time. Based on the oxidation kinetics obtained in this study, 1520 SS is considered suitable for a fuel cladding of SCWR in combination with appropriate CW process. However, detailed evaluation and countermeasures for the degradation due to nodular oxidation are needed before application of tube-shaped 1520 SS in supercritical water at 700 °C. On the other hand, it is estimated that the use of that at 650 °C is acceptable because the weight gain after long-term exposure was considered to be much less than the threshold condition of the spalling.

Keywords

Oxidation kinetics Austenitic stainless steel Cold working Fuel cladding material Super critical water reactor 

Notes

Acknowledgements

Present study includes the result of “Research and Development of the Super Fast Reactor” entrusted to The University of Waseda by the Ministry of Education, Culture, Sports, Science and Technology of Japan (MEXT).

References

  1. 1.
    U.S. DOE, A Technology Roadmap for Generation IV Nuclear Energy Systems, December, (2002)Google Scholar
  2. 2.
    U.S. DOE, System Research Plan for the Supercritical Water-Cooled Reactor, August (2004)Google Scholar
  3. 3.
    Y. Oka, S. Koshizuka, in Proceedings of 1st International Symposium on Supercritical Water-Cooled Reactors, Design and Technology, Tokyo, Paper No. 101 (2000)Google Scholar
  4. 4.
    Y. Oka, et al., Research and Development of Super Light Water Reactors and Super Fast Reactors in Japan, The 5th International Symposium on Supercritical Water-Cooled Reactors (ISSCWR-5), (2011)Google Scholar
  5. 5.
    G.S. Was et al., J. Nucl. Mater. 371, 176–201 (2007)CrossRefGoogle Scholar
  6. 6.
    C. Sun et al., Corros. Sci. 51, 2508–2523 (2009)CrossRefGoogle Scholar
  7. 7.
    T.R. Allen et al., Nucl. Technol. 162, 342–357 (2008)CrossRefGoogle Scholar
  8. 8.
    X. Ru, R.W. Staehle, Corrosion 69(3), 211–229 (2013)CrossRefGoogle Scholar
  9. 9.
    L. Zhang et al., Nucl. Eng. Des. 249, 180–187 (2012)CrossRefGoogle Scholar
  10. 10.
    X. Ren, Corrosion 63(7), 603–612 (2007)CrossRefGoogle Scholar
  11. 11.
    J. Li et al., J. Nucl. Eng. 454, 7–11 (2014)Google Scholar
  12. 12.
    S. Sakurai, et al., The 5th International Symposium SCWR (ISSCWR-5), P-041, Vancouver, British Columbia, Canada, 13–16 Mar 2011 (2011)Google Scholar
  13. 13.
    D. Guzonas, R. Novotny, Prog. Nucl. Energy 77, 361–372 (2014)CrossRefGoogle Scholar
  14. 14.
    Y. Nakazono et al., J. Phys: Conf. Ser. 215, 012094 (2010)Google Scholar
  15. 15.
    Y. Oka, et al., The 6th International Symposium on Supercritical Water-Cooled Reactors (ISSCWR-6), No. 13035, 03–07 Mar 2013, Shenzhen, Guangdong, China (2013)Google Scholar
  16. 16.
    H. Abe et al., Nucl. Eng. Des. 280, 652–660 (2014)CrossRefGoogle Scholar
  17. 17.
    H. Abe, et al., 16th International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors (2013)Google Scholar
  18. 18.
    S. Penttilä et al., J. Supercrit. Fluids 81, 157–163 (2013)CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Graduate School of EngineeringTohoku UniversityAoba-ku, SendaiJapan

Personalised recommendations