Microstructural Characterization of Proton-Irradiated 316 Stainless Steels by Transmission Electron Microscopy and Atom Probe Tomography

  • Yun Soo LimEmail author
  • Dong Jin Kim
  • Seong Sik Hwang
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Proton irradiation is a well-known useful experimental technique to study neutron irradiation-induced phenomena in reactor core materials. Type 316 austenitic stainless steel was irradiated with 2 meV protons to doses up to 10 displacement per atom at 360 °C, and the various effects of the proton irradiation on the microstructural changes were characterized with transmission electron microscopy and atom probe tomography. Typical irradiation damage mainly consisted of small dislocation loops, cavities, tiny precipitates and network dislocations. Ni and Si were enriched, whereas Cr, Mn and Mo were depleted on the grain boundaries associated with irradiation-induced segregation. Ni–Si rich clusters were also found in the matrix. A new method to prepare TEM specimens of a proton-irradiated material is suggested, which was shown to be a relatively simple and effective method to chemically eliminate the inherent surface damage induced by a conventional high-energy focused ion beam and subsequent low-energy ion milling treatments.

Keywords

Stainless steel Proton irradiation TEM APT Defects Radiation induced segregation 

Notes

Acknowledgements

This work was financially supported by the Korean Nuclear R&D Program organized by the National Research Foundation (NRF) in support of the Ministry of Science, ICT and Future Planning (2017M2A8A4015155), and by the R&D Program of Korea Atomic Energy Research Institute.

References

  1. 1.
    J. McKinley, R. Lott, B. Hall, K. Kalchik, Examination of baffle-former bolts from D.C. cook unit 2, in Proceedings of the 16th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor, 2013Google Scholar
  2. 2.
    J. Pakarinen, U. Ehrnstén, H. Keinänen and W. Karlsen, Microstructural characterization of irradiated baffle bolts removed from a finnish VVER and a French PWR, in Proceedings of the 16th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor, 2013Google Scholar
  3. 3.
    J. Gan, G.S. Was, Microstructure evolution in austenitic Fe-Cr-Ni alloys irradiated with rotons: comparison with neutron-irradiated microstructures. J. Nucl. Mater. 297, 161–175 (2001)CrossRefGoogle Scholar
  4. 4.
    K.J. Stephenson, G.S. Was, Comparison of the microstructure, deformation and crack initiation behavior of austenitic stainless steel irradiated in-reactor or with protons. J. Nucl. Mater. 456, 85–98 (2015)CrossRefGoogle Scholar
  5. 5.
    J. Yu, J. Liu, J. Zhang, J. Wu, TEM investigation of FIB induced damages in preparation of metal material TEM specimens by FIB. Mater. Lett. 60, 206–209 (2006)CrossRefGoogle Scholar
  6. 6.
    A. Aitkaliyeva, J.W. Madden, B.D. Miller, J.I. Cole, J. Gan, Comparison of preparation techniques for nuclear materials for transmission eletron microscopy (TEM). J. Nucl. Mater. 459, 241–246 (2015)CrossRefGoogle Scholar
  7. 7.
    G.S. Was, J.T. Busby, T. Allen, E.A. Kenik, A. Jenssen, S.M. Bruemmer, J. Gan, A.D. Edwards, P.M. Scott, P.L. Andresen, Emulation of neutron irradiation effects with protons: validation of principle. J. Nucl. Mater. 300, 198–216 (2002)CrossRefGoogle Scholar
  8. 8.
    ASTM Standard E693-01, Standard practice for characterizing neutron exposure in iron and low alloy steels in terms of displacements per atom (dpa) (2001)Google Scholar
  9. 9.
    R.E. Stoller, M.B. Toloczko, G.S. Was, A.G. Certain, S. Dwaraknath, F.A. Garner, On the use of SRIM for computing radiation damage exposure. Nucl. Instrum. Methods Phys. Res. B 310, 75–80 (2013)CrossRefGoogle Scholar
  10. 10.
    ASTM G1-03, Standard practice for preparing, cleaning, and evaluating corrosion test specimens. ASTM, West Conshohocken, PA (2011)Google Scholar
  11. 11.
    R.E. Schramm, R.P. Reed, Stacking fault energies of seven commercial austenitic stainless steels. Metall. Trans. A 6A, 1345–1351 (1975)CrossRefGoogle Scholar
  12. 12.
    S.J. Zinkle, Radiation-Induced Effects on Microstructure. in Reference Module in Materials Science and Materials Engineering: Comprehensive Nuclear Materials (Elsevier, Amsterdam, 2012), pp. 65–98CrossRefGoogle Scholar
  13. 13.
    A.J. Ardell, P. Bellon, Radiation-induced solute segregation in metallic alloys. Curr. Opin. Solid State Mater. Sci. 20, 115–139 (2016)CrossRefGoogle Scholar
  14. 14.
    A.R. Laborne, P. Gavoille, J. Malaplate, C. Pokor, B. Tanguy, Correlation of radiation-induced changes in microstructure/microchemistry, density and thermo-electric power of type 304L and 316 stainless steels irradiated in the Phénix reactor. J. Nucl. Mater. 460, 72–81 (2015)CrossRefGoogle Scholar
  15. 15.
    Z. Jiao, Y. Chen, J. Hesterberg, E.A. Marquis and G. Was, Post-irradiation annealing in mitigation of IASCC in proton-irradiated stainless steel, in Proceedings of the 16th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor, 2013Google Scholar
  16. 16.
    W.V. Renterghem, M.J. Konstantinovic, M. Vankeerberghen, Evolution of the radiation-induced defect structure in 316 type stainless steel after post-irradiation annealing. J. Nucl. Mater. 452, 158–165 (2014)CrossRefGoogle Scholar
  17. 17.
    P.J. Maziasz, Overview of microstructural evolution in neutron-irradiated austenitic stainless steels. J. Nucl. Mater. 205, 118–145 (1993)CrossRefGoogle Scholar
  18. 18.
    C.M. Barr, G.A. Vetterick, K.A. Unocic, K. Hattar, X.-M. Bai, M.L. Taheri, Anisotropic radiation-induced segregation in 316L austenitic stainless steel with grain boundary character. Acta Mater. 67, 145–155 (2014)CrossRefGoogle Scholar
  19. 19.
    M. Tomozawa, Y. Miyahara, K. Kako, Solute segregation on Σ3 and random grain boundaries in type 316L stainless steel. Mater. Sci. Eng. A 578, 167–173 (2013)CrossRefGoogle Scholar
  20. 20.
    K. Fujii, K. Fukuya, Irradiation-induced microchemical changes in highly irradiated 316 stainless steel. J. Nucl. Mater. 469, 82–88 (2016)CrossRefGoogle Scholar
  21. 21.
    Y. Chen, P.H. Chou, E.A. Marquis, Quantitative atom probe tomography characterization of microstructures in a proton irradiated 304 stainless steel. J. Nucl. Mater. 451, 130–136 (2014)CrossRefGoogle Scholar
  22. 22.
    T. Toyama, Y. Nozawa, W. Van Renterghem, Y. Matsukawa, M. Hatakeyama, Y. Nagai, A. Al Mazouzi, S. Van Dyck, Irradiation-induced precipitates in a neutron irradiated 304 stainless steel studied by three-dimensional atom probe. J. Nucl. Mater. 418, 62–68 (2011)CrossRefGoogle Scholar
  23. 23.
    W. Van Renterghem, A. Al Mazouzi, S. Van Dyck, Influence of post irradiation annealing on the mechanical properties and defect structure of AISI 304 steel. J. Nucl. Mater. 413, 95–102 (2011)CrossRefGoogle Scholar
  24. 24.
    G.S. Was, S.M. Bruemmer, Effects of irradiation on intergranular stress corrosion cracking. J. Nucl. Mater. 216, 326–347 (1994)CrossRefGoogle Scholar
  25. 25.
    P.L. Andresen, G.S. Was, Irradiation assisted stress corrosion cracking, in Comprehensive Nuclear Materials, ed. by R.J.M. Konings, T.R. Allen, R.E. Stoller, S. Yamanaka (Elsevier Ltd., Amsterdam, 2012), pp. 177–295CrossRefGoogle Scholar
  26. 26.
    A.J. Jacobs, G.P. Wozadlo, G.M. Gordon, Low-temperature annealing: a process to mitigate irradiation-assisted stress corrosion racking. Corrosion 51, 731–737 (1995)CrossRefGoogle Scholar
  27. 27.
    S.M. Bruemmer, G.S. Was, Microstructural and microchemical mechanisms controlling intergranular stress corrosion cracking in light-water-reactor systems. J. Nucl. Mater. 216, 348–363 (1994)CrossRefGoogle Scholar
  28. 28.
    M.D. McMurtrey, B. Cui, I. Robertson, D. Farkas, G.S. Was, Mechanism of dislocation channel-induced irradiation assisted stress corrosion crack initiation in austenitic stainless steel. Curr. Opin. Solid State Mater. Sci. 19, 305–314 (2015)CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Nuclear Materials Research DivisionKorea Atomic Energy Research InstituteDaejeonSouth Korea

Personalised recommendations