Formation of He Bubbles by Repair-Welding in Neutron-Irradiated Stainless Steels Containing Surface Cold-Worked Layer

  • Masato Koshiishi
  • Naoto Shigenaka
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Stress corrosion cracking (SCC) has been found on surfaces of reactor internals which are heavily cold-worked by machining. When repair welding is applied to the cracked region, the cold-worked surface will be included in the welding region. Therefore, the effect of the cold-worked layer on the weldability of irradiated stainless steels (SSs) needs to be clarified. In this study, helium bubbles formed by welding on irradiated SSs were investigated by measurements and comparisons to published results. TIG welding was performed on an irradiated SS plate with a cold-worked layer generated by wire peening. Re-crystallization was confirmed in the weld after peening at the surface near the weld heat affected zone (HAZ). The helium bubble number density along the grain boundary in the re-crystallized region was the same as in the non-re-crystallized region, whereas the bubble diameter was smaller. Helium bubble growth was suppressed by the re-crystallization behavior.

Keywords

Austenitic stainless steel BWR Neutron irradiation Welding Helium bubble 

Notes

Acknowledgements

The authors wish to express their appreciation to Prof. Yutaka Watanabe of Tohoku University for his guidance and fruitful discussions. The authors also acknowledge Mr. Tsuneyuki Hashimoto of Nippon Nuclear Fuel Development Co., Ltd. for helpful discussions on this study.

References

  1. 1.
    W.R. Kanne Jr., Remote reactor repair: GTA weld cracking caused by entrapped helium. Weld. J. 67, 33–39 (1988)Google Scholar
  2. 2.
    C.A. Wang, M.L. Grossbeck, B.A. Chin, Threshold helium concentration required to initiate cracking during welding of irradiated stainless steel. J. Nucl. Mater. 225, 59–68 (1995)CrossRefGoogle Scholar
  3. 3.
    H.T. Lin, M.L. Grossbeck, B.A. Chin, Cavity microstructure and kinetics during GAS tungsten arc welding of helium-containing stainless steel. Metall. Trans. A 21A, 2585–2596 (1990)CrossRefGoogle Scholar
  4. 4.
    W.R. Kanne Jr., G.T. Chandler, D.Z. Nelson, E.A. Franko-Ferreira, Welding irradiated stainless steel. J. Nucl. Mater. 225, 69–75 (1995)CrossRefGoogle Scholar
  5. 5.
    K. Asano, S. Nishimura, Y. Saito, H. Sakamoto, Y. Yamada, T. Kato, T. Hashimoto, Weldability of neutron irradiated Austenitic stainless steel. J. Nucl. Mater. 264, 1–9 (1999)CrossRefGoogle Scholar
  6. 6.
    S. Suzuki, K. Takamori, K. Kumagai, T. Fukuda, Y. Yamashita, T. Futami, Evaluation of SCC morphology on L-Grade stainless steel in BWRs. J. High Press. Inst. Japan 42(4), 188–198 (2004)Google Scholar
  7. 7.
    M. Koshiishi, T. Nakamura, K. Asano, Influence of surface peening on the weldability of neutron-irradiated stainless steel, in 14th International Symposium on Environmental Degradation of Materials in Nuclear Power Systems–Water Reactors, ANS, pp.1392–1398 (2003)Google Scholar
  8. 8.
    JNES, Annual Report of Japan Nuclear Energy Safety Organization PMT Project of JFY 2003. (JNES Report, 2004)Google Scholar
  9. 9.
    JNES, Annual Report of Japan Nuclear Energy Safety Organization WIM Project of JFY 2004. (JNES Report, 2005)Google Scholar
  10. 10.
    JNES, Guideline of the Repair-welding on Neutron-irradiated Stainless Steels. (JNES SS report, JNES-SS-0502, 2005)Google Scholar
  11. 11.
    T. Hashimoto, M. Mochizuki, Modeling of helium bubble formation during welding of irradiated stainless steels, Effects of Radiation on Materials, ASTM STP 1366, ed. by M.L. Hamilton, A.S. Kumar, S.T. Rosinski, M.L. Grossbeck (ASTM, 2000), pp. 973–987Google Scholar
  12. 12.
    T. Hashimoto, N. Yanagida, M. Koshiishi, S. Kawano, H. Sakamoto, K. Nakata, M. Oishi, Numerical analysis on the weldability of neutron-irradiated stainless steels, Mathematical Modeling of Weld Phenomena 6, ed. by H. Cerjak, H.K.D.H Bhadeshia (Institute of Materials, 2002), pp. 443–466Google Scholar
  13. 13.
    M. Koshiishi, K. Kashiwakura, T. Hashimoto, H. Takahashi, weldability of neutron irradiated stainless steels studied by multi-pass TIG and YAG laser welding, in 11th International Conference on Environmental Degradation of Materials in Nuclear Power Systems–Water Reactors, ANS, pp. 951–959 (2003)Google Scholar
  14. 14.
    I. Ohnuma, H. Ohtani, K. Ishida, T. Nishizawa, Computer simulation of grain growth in particle dispersed structure. J. Japan Inst. Metals 58(10), 1133–1140 (1994)CrossRefGoogle Scholar
  15. 15.
    Z. Jiao, G. Was, T. Miura, K. Fukuya, Aspects of ion irradiations to study localized deformation in austenitic stainless steels. J. Nucl. Mater. 452, 328–334 (2014)CrossRefGoogle Scholar
  16. 16.
    T. Miura, K. Fujii, K. Fukuya, Z. Jiao, G. Was, A study for effects of grain size on occurrence of IASCC effects of grain size on localized deformation of irradiated stainless steel. J. Inst. Nucl. Saf. Syst. 18, 211–217 (2011)Google Scholar
  17. 17.
    K. Kako, Y. Miyahara, T. Arai, M. Mayuzumi, Effects of chemical compositions and grain size on stress corrosion cracking of Austenitic stainless steel in high temperature water, (CRIEPI Report, Q07020, 2008)Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Nippon Nuclear Fuel Development Co., LtdOarai-Machi, Higashi-Ibaraki-GunJapan
  2. 2.Hitachi-GE Nuclear Energy, LtdHitachi-Shi, Ibaraki-KenJapan

Personalised recommendations